6000-mesh inorganic powder-filled modified pa (polyamide)6 master batch and preparation method thereof

An inorganic powder, PA610 technology, applied in the field of 6000 mesh inorganic powder filling modified PA6 masterbatch and its preparation, can solve the problem of poor compatibility, mechanical properties, dimensional stability can not meet the ideal requirements, the interface is difficult to form sticky. junction and other problems, to achieve the effects of good mechanical properties, lower production costs, and good compatibility

Inactive Publication Date: 2012-07-04
徐州腾飞工程塑料有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The carrier resin is PA6, and the filler often uses polar inorganic fillers such as calcium carbonate and kaolin, but the compatibility between the two is poor, and it is difficult to form a good bond at the interface
In order to improve the interfacial bonding between the resin and the inorganic filler, and form a good interfacial adhesion between the resin and the inorganic filler, the mechanical and dimensional stability of the whole system after the masterbatch is mixed with the matrix resin cannot meet the ideal requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 6000-mesh inorganic powder-filled modified pa (polyamide)6 master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] raw material:

[0026] PA6 (Nylon 6) 15kg

[0027] Stearic acid (HSt) 0.8kg

[0028] Polyethylene wax 3kg

[0029] Paraffin (WAX) 0.6kg

[0030] 6000 mesh heavy calcium carbonate 70kg.

[0031] Its preparation method is:

[0032] 1) Put 70kg of 6000-mesh heavy calcium carbonate into a high-speed mixer and mix at a high speed. When the temperature reaches 80°C, dehumidification begins. After the temperature reaches 110°C, add stearic acid and mix for 5 minutes;

[0033] 2) Put the mixture in the high mixer into the cold mixer for cooling, and when the cooling temperature drops to 30°C, the material is discharged to obtain modified 6000 mesh heavy calcium carbonate;

[0034] 3) Put PA6, polyethylene wax, and paraffin into the high mixer in sequence and mix for 1 minute, then add the modified 6000 mesh heavy calcium carbonate and continue mixing for 1 minute;

[0035] 4) Put the mixed material in the high mixer into the cold mixer for cooling, and when the cooling te...

Embodiment 2

[0042] raw material:

[0043] PA6 (Nylon 6) 15kg

[0044] Stearic acid / titanate 0.8kg

[0045] Polyethylene wax 5kg

[0046] Paraffin (WAX) 0.8kg

[0047] 80kg of 6000 mesh heavy calcium carbonate.

[0048] The steps of its manufacturing method are:

[0049] 1) Put 80kg of 6000 mesh heavy calcium carbonate into a high-speed mixer and mix at high speed. When the temperature reaches 85°C, dehumidification starts. After the temperature reaches 120°C, add stearic acid / titanate and mix for 5 minutes;

[0050] 2) Put the mixture in the high mixer into the cold mixer for cooling, and when the cooling temperature drops to 50°C, the material is discharged to obtain modified 6000 mesh heavy calcium carbonate;

[0051] 3) Put PA6, polyethylene wax, and paraffin into a high-mixer in turn and mix for 2 minutes, then add modified 6000-mesh heavy calcium carbonate and continue mixing for 3 minutes;

[0052] 4) Put the mixed material in the high mixer into the cold mixer for cooling, an...

Embodiment 3

[0055] raw material:

[0056] PA6 (Nylon 6) 15kg

[0057] Stearic acid / aluminate 0.8kg

[0058] Polyethylene wax 3kg

[0059] Paraffin (WAX) 0.6kg

[0060] 6000 mesh heavy calcium carbonate 70kg.

[0061] 6000 mesh inorganic powder filled modified PA6 masterbatch and its preparation method are as follows:

[0062] 1) Put 70kg of 6000-mesh heavy calcium carbonate into a high-speed mixer and mix at a high speed. When the temperature reaches 90°C, dehumidification begins. After the temperature reaches 120°C, add stearic acid / aluminate and mix for 5 minutes;

[0063] 2) Put the mixture in the high mixer into the cold mixer for cooling, and when the cooling temperature drops to 45°C, the material is discharged to obtain modified 6000 mesh heavy calcium carbonate;

[0064] 3) Put PA6, polyethylene wax, and paraffin wax into a high-mixer and mix for 3 minutes, then add modified 6000-mesh heavy calcium carbonate and continue mixing for 2 minutes;

[0065] 4) Put the mixed material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a 6000-mesh inorganic powder-filled modified PA (Polyamide)6 master batch and a preparation method thereof and belongs to the technical field of high-molecular materials. The PA6 master batch comprises the following main raw materials: PA6, a surface treating agent, polyethylene wax, paraffin wax and 6000-mesh inorganic powder, and the preparation method of the PA6 master batch comprises the following steps of: putting the 6000-mesh inorganic powder into a high-speed mixer for agitation and dehumidification, adding the surface treating agent for mixing and agitation and putting in a cold mixer for cooling, putting the PA6, the polyethylene wax and the paraffin wax into the high-speed mixer in sequence for mixing and agitation, adding the modified 6000-mesh inorganic powder for mixing and agitation, putting in the cold mixer for cooling and discharging and pelleting with an extruder to prepare the 6000-mesh inorganic powder-filled modified PA6 master batch. The 6000-mesh inorganic powder-filled modified PA6 master batch and the preparation method thereof have the beneficial effects that after the 6000-mesh inorganic powder-filled modified PA6 master batch is mixed with matrix resin, a whole system has good compatibility, dispersibility, flowability and processing performance, and a produced product has good mechanical property, dimension stability, toughness and impact resistance and the 6000-mesh inorganic powder-filled modified PA6 master batch is particularly suitable for manufacturing PA6 water supply pipes, PA6 double-walled corrugated tubes, plastic turnover boxes and automotive interior products.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a 6000-mesh inorganic powder filled modified PA6 masterbatch and a preparation method thereof. Background technique [0002] With the rapid development of the plastics industry and the wide application of plastic products, people pay more and more attention to the technology of filling and modifying plastics. Adding various inorganic fillers to the resin and then mixing and molding can not only greatly reduce the cost of the product, but also significantly reduce the cost of the product. Improve certain properties of plastics, such as mechanical energy, thermal properties, wear resistance and aging resistance, so as to endow materials with new characteristics to meet the needs of different uses. [0003] PA6 (Nylon 6) filler masterbatch includes three parts: carrier resin, filler and additives. The carrier resin is PA6, and the filler often uses polar inorganic fillers...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08K13/06C08K9/06C08K9/04C08K3/26C08K3/34C08K3/36C08K3/22B29B9/06
Inventor 李新忠高腾
Owner 徐州腾飞工程塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap