Preparation method of transparent film-grade thermoplastic polyurethane elastomer

A thermoplastic polyurethane and transparent film technology, applied in the field of thermoplastic polyurethane elastomers, to achieve good high and low temperature resistance, high tensile strength and elongation at break, and good aging resistance

Active Publication Date: 2012-07-11
SHANGHAI LIANJING MATERIAL ASSETAB
View PDF4 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] The purpose of the present invention is to solve the defect that crystal points can be produced in the process of preparing TPU in the prior art, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of transparent film-grade thermoplastic polyurethane elastomer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Premix: 0.5% antioxidant, and 0.15% hindered amine light stabilizer, and 0.25% benzotriazole UV absorber, and 0.5% montan wax and / or erucamide wax Add slip agent and 0.01% environmental catalyst to 70% polybutylene adipate polyol (PBA, hydroxyl value 56±3mgKOH / g, acid value≤0.5mgKOH / g) with molecular weight 2000 Mix to obtain polymer polyol mixed solution,

[0064] Mixing: pouring the polymer polyol mixing solution and 22% diisocyanate into a single-screw mixing device through a mass flow meter for mixing to obtain a preliminary reaction mixture,

[0065] Reaction: pour the preliminary reaction mixture with 4.5% 1,4-butanediol into a co-rotating twin-screw continuous reaction extruder for reaction, the reaction temperature is 150-250°C, the pressure is 4-8MPa, the screw The rotation speed is between 250-350rpm, the kneading frequency is between 7-15 times / s, the length-to-diameter ratio of the screw is 48, the length of the reaction section is 1561mm, the length of the...

Embodiment 2

[0069] Premix: 0.5% antioxidant, and 0.15% hindered amine light stabilizer, and 0.25% benzotriazole UV absorber, and 0.5% montan wax and / or erucamide wax Add slip agent and 0.01% environmental protection catalyst to 67% polybutylene adipate polyol (PBA, hydroxyl value 56 ± 3mgKOH / g, acid value ≤ 0.5mgKOH / g) with a molecular weight of 2000 Mix to obtain polymer polyol mixed solution,

[0070] Mixing: pouring the polymer polyol mixed solution and 24% diisocyanate into a single-screw mixing device through a mass flow meter for mixing to obtain a preliminary reaction mixture,

[0071] Reaction: pour the preliminary reaction mixture with 5.5% 1,4-butanediol into a co-rotating twin-screw continuous reaction extruder for reaction, the reaction temperature is 150-250°C, the pressure is 4-8MPa, the screw The rotation speed is between 250-350rpm, the kneading frequency is between 7-15 times / s, the length-to-diameter ratio of the screw is 48, the length of the reaction section is 1561mm...

Embodiment 3

[0075] Premix: 0.5% antioxidant, and 0.15% hindered amine light stabilizer, and 0.25% benzotriazole UV absorber, and 0.4% montan wax and / or erucamide wax Slip agent, and 0.01% environmental protection catalyst are added to 68% polyethylene adipate butylene glycol ester polyol (PEBA, hydroxyl value 37 ± 2mgKOH / g, acid value ≤ 0.5mgKOH / g) of molecular weight 3000 ) are mixed to obtain a polymer polyol mixed solution,

[0076] Mixing: pouring the polymer polyol mixed solution and 23% diisocyanate into a single-screw mixing device through a mass flow meter for mixing to obtain a preliminary reaction mixture,

[0077] Reaction: pour the preliminary reaction mixture with 5.8% 1,4-butanediol into a co-rotating twin-screw continuous reaction extruder for reaction, the reaction temperature is 150-250°C, the pressure is 4-8MPa, the screw The rotation speed is between 250-350rpm, the kneading frequency is between 7-15 times / s, the length-to-diameter ratio of the screw is 48, the length ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Acid valueaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of thermoplastic polyurethane elastomer (TPU), and specifically relates to a formula and a production technology of transparent film-grade TPU. According to the invention, 20-40% of diisocyanate, 45-75% of polymer polyhydric alcohol with a molecular weight of 1000-4000, 4-10% of 1,4-butylene glycol, 0.2-1% of an anti-oxidant, 0.2-1.5% of a lubricant, 0.001-0.02% of an environment-friendly catalyst, 0.2-1.0% of an ultraviolet ray absorbing agent, 0-0.8% of a hydrolysis-resisting agent, 0.1-1% of a light stabilizing agent, and 0-2% of other auxiliary agents are processed through steps such as premixing, reacting, dicing and dehydrating, and drying and curing, such that the transparent film-grade TPU is obtained. According to the invention, with the innovations on formula, equipment and technology, a defect of fisheye generation in TPU preparation processes in prior arts is solved. Factors such as a filling manner, an auxiliary agent adding manner, distributive mixing and dispersive mixing effects of an extruder, extruder retention time, and drying and curing are comprehensively considered, such that a stable product with high quality is produced.

Description

[technical field] [0001] The invention relates to the technical field of thermoplastic polyurethane elastomer (TPU), in particular to a formula and production process of a transparent film grade thermoplastic polyurethane elastomer. [Background technique] [0002] The English name of thermoplastic polyurethane elastomer is Thermoplastic Polyurethane, or TPU for short. It is the three major types of polyurethane elastomers together with cast polyurethane elastomer (CPU) and mixing polyurethane elastomer (MPU). TPU is a kind of polyurethane elastomer that can be plasticized after heating and can be dissolved by solvent. Compared with cast polyurethane elastomer (CPU) and mixing polyurethane elastomer (MPU), TPU has no or little chemical structure. Chemically crosslinked, the molecular chains are essentially linear, but there is a certain amount of physical crosslinking. [0003] The earliest company to study TPU was Bayer in Germany. However, the products that were formally c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08L75/06C08L75/08C08K5/134C08K5/526C08K5/3475C08K5/3435C08K5/20C08G18/66C08G18/42C08G18/48B29C47/92B29C71/00B29C71/02B29C48/92
CPCB29C48/92
Inventor 范年春蔡建国龙双林许海亮吴超学
Owner SHANGHAI LIANJING MATERIAL ASSETAB
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka