Rubber material for prestressing jack sealing ring and preparation method for rubber material

A technology of rubber compound and jack, which is applied in the field of rubber compound processing, can solve the problems of high cost, high price of hydrogenated nitrile rubber and chlorohydrin rubber, etc., and achieve suitable elasticity, good wear resistance and low material cost Effect

Inactive Publication Date: 2012-07-18
HEFEI SHICHUAN ENG MACHINERY
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The usual 41# nitrile rubber formula is inferior to hydrogenated nitrile rubber and chlorohydrin rubber in terms of oil resistance, heat resistance and air tightness, but hydrogenated nitrile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber material for prestressing jack sealing ring and preparation method for rubber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. Raw material preparation:

[0032] Preparation of raw materials for rubber compound:

[0033] Weigh polyurethane rubber 100, silicone rubber 8, fluorine rubber 5, ethylene propylene rubber 3.5, natural rubber 0.8, sulfur 0.4, zinc oxide 0.5, stearic acid 0.4, antioxidant RD 0.3, antioxidant 4010NA1, paraffin wax 3, high wear resistance Carbon black N33063, dioctyl phthalate DBP 20, aluminum hydroxide 30, accelerator PZ1-2,

[0034] Preparation of raw materials for B rubber compound:

[0035] Weigh one-component homopolychlorohydrin rubber 85, copolychlorohydrin rubber 15, zinc stearate 1, anti-aging agent RD 2, gelatin T-780.5, rhine wax 1, carbon black 48, barium sulfate 12, phthalate two Dioctyl formate 7, lead trioxide 4, sulfur 0.4, accelerator Na-222.

[0036] 2. The method for preparing the rubber compound of the prestressed jack sealing ring comprises the following steps:

[0037] The first step: Prepare A rubber material and B rubber material respectively...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber material for a prestressing jack sealing ring. The rubber material is formed by mixing a rubber material A and a rubber material B in an equal ratio, wherein the rubber material A consists of the following raw materials in part by weight: 95 to 105 parts of polyurethane rubber, 7 to 9 parts of silicone rubber, 4 to 6 parts of fluororubber, 3 to 4 parts of ethylenepropylene rubber, 0.7 to 0.9 part of natural rubber, 0.3 to 0.5 part of sulfur, 0.4 to 0.6 part of zinc oxide, 0.3 to 0.5 part of stearic acid, 1 to 2 parts of antioxidant 4010NA, 3 to 4 parts of paraffin, 62 to 65 parts of highly wear-resistant carbon black N330, 18 to 22 parts of dioctyl phthalate (DOP), 25 to 35 parts of aluminum hydroxide and 1 to 2 parts of accelerator PZ; and the rubber material B consists of the following raw materials in part by weight: 82 to 87 parts of unary homopolymer of chlorohydrin rubber, 12 to 18 parts of copolymer of chlorohydrin rubber, 1 to 2 parts of zinc stearate, 1 to 3 parts of antioxidant RD, 0.4 to 0.6 part of gum-easy T-78, 1 to 2 parts of rhein wax, 45 to 55 parts of carbon black, 10 to 14 parts of barium sulfate, 5 to 8 parts of DOP, 4 to 6 parts of lead trioxide, 0.4 to 0.6 part of sulfur and 1 to 2 parts of accelerator Na-22. The sealing ring prepared from the rubber material has high oil resistance, heat resistance, air tightness, flame retardance and tear resistance and is low in material cost.

Description

technical field [0001] The invention relates to the field of rubber compound processing, in particular to a prestressed jack sealing ring rubber compound and a preparation method thereof. Background technique [0002] The sealing ring is a vulnerable part of the prestressed jack, and the sealing ring is made of rubber. Therefore, there are special requirements for the formula of the rubber material, and the products are required to have high oil resistance and heat resistance, and at the same time have high air tightness. The usual 41# nitrile rubber formula is inferior to hydrogenated nitrile rubber and chlorohydrin rubber in terms of oil resistance, heat resistance and air tightness, but hydrogenated nitrile rubber and chlorohydrin rubber are expensive and costly; The research and practice of improving heat and airtight performance and saving material cost are of great practical significance. Contents of the invention [0003] The invention provides a prestressed jack ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08L83/04C08L27/12C08L23/16C08L7/00C08L71/00C08K13/02C08K3/04C08K3/06C08K3/22C08K5/12C08K5/098C08K3/30
Inventor 丁煜倩王正宇朱焕章张凯东朱友武王从永王从凯王从华
Owner HEFEI SHICHUAN ENG MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap