Durable wood-bamboo cellulose composite material
A bamboo cellulose and composite material technology, which is applied to wood processing appliances, household components, flat products, etc., can solve the problems of wood bamboo fiber or plant fiber being easy to grow fungi and high price, and achieve long service life and shock resistance. Strong, low-emission effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1
[0024] The material is 9 mm thick low-density wood fiberboard (density 350kg / m 3 Around), using low molecular weight modified phenolic resin and additives treatment method. Phenolic resin has a molecular weight of 200, a viscosity of 100-250cps at 25°C, a solid resin content of 50%-60%, and is modified by diphenylmethane diisocyanate (MDI) (application amount 3%) to increase water resistance; the auxiliary is borax , Boric acid, potassium borate and sodium carbonate, the ratio (weight) can be 1: 1: 1: 2, and the amount can be up to 5% of the resin weight to reduce the osmotic pressure of the wood and increase the pH value of the product surface. The dipping method can be used to treat the wood fiber board in the modified phenolic resin glue for 5 minutes, or the modified phenolic resin glue can be directly applied to the wood fiber board to replace the traditional vacuum-pressurization treatment. After sizing, the average phenolic solid resin content of the wo...
Example Embodiment
[0025] Example 2
[0026] The difference from Example 1 is that the three-layer or five-layer wood fiber board assembly is heated and pressed by microwave (or radio frequency), the pressing pressure is 1.5-2.0 MPa, the pressing temperature is 90-105 degrees, and the pressing time is about 5-10 minutes, the pH value of the product surface is between 10 and 12. The product has good durability against corrosion, no anti-corrosion treatment is required, and it is sufficient for outdoor use.
Example Embodiment
[0027] Example 3
[0028] The material is a low-density plant fiber sheet made of 9mm thick diphenylmethane diisocyanate MDI (density 350 kg / m 3 Left and right), the others are the same as in Example 1. Treat the plant fiber board with modified phenolic resin for 5-30 minutes. You can also directly roll-coat the modified phenolic resin glue to replace the traditional vacuum-pressurization treatment. After sizing, the plant fiber board with a thickness of 9 mm can be averaged The phenolic solid resin content reaches 12%. After the above treatment, the three-layer or five-layer plant fiber board assembly blank is hot-pressed, the hot-pressing pressure is 1.5-3.0 MPa, the hot-pressing temperature is 145-155C°, the hot-pressing time is about 8-20 minutes, and the pH value of the product surface is 10 And 12. The product has good durability against corrosion, no anti-corrosion treatment is required, and it is sufficient for outdoor use.
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap