Artificial texture stone and production method thereof

An artificial and textured technology, applied in the field of artificial stone, can solve problems such as poor decorative effect, and achieve the effect of good decorative effect, unique craftsmanship and scientific composition ratio.

Active Publication Date: 2012-12-12
SHANGHAI APE STONE
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problem of poor decorative effect of the existing artificial stone, the invention provides an artificial texture stone and a production method of the artificial texture stone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Step 1. Use natural or pre-processed stone models to remake molds according to market and customer needs. Prepare the main color paste and auxiliary color paste, the main color paste components include:

[0064] Portland cement 40kg;

[0065] Slag 5 kg;

[0066] 51 kg of 50~100 mesh quartz sand;

[0067] Pigment 3 kg;

[0068] High-performance polycarboxylate superplasticizer 0.5 kg;

[0069] Organic bentonite 0.5 kg;

[0070] Citric acid 0.1 kg;

[0071] Defoamer 0.2 kg;

[0072] Correspondingly, the weight ratio of each component of the auxiliary color slurry is:

[0073] High alumina cement 50 kg;

[0074] Silica fume 5kg;

[0075] Colored sand 37kg;

[0076] Pigment 5kg;

[0077] High-performance polycarboxylate superplasticizer 0.5kg;

[0078] Cellulose ether 0.2kg;

[0079] Organic bentonite 0.5kg;

[0080] Polyacrylamide 0.1kg;

[0081] Homemade coagulant 1kg;

[0082] Composite water repellent 1kg;

[0083] Defoamer 0.2kg;

[0084] Pre-mix the ...

Embodiment 2

[0089] Process 1. Use natural or pre-processed stone models to remake molds according to market and customer needs. Prepare main color paste and auxiliary color paste, wherein the main color paste components include:

[0090] White Portland cement 50kg;

[0091] Slag 8kg;

[0092] Rock chip 5kg;

[0093] Beige colored sand 15kg;

[0094] Color sand blue ash 18kg;

[0095] Pigment iron oxide yellow 3kg;

[0096] High-performance polycarboxylate superplasticizer 0.5kg;

[0097] Starch ether 0.05kg;

[0098] Tartaric acid 0.02kg;

[0099] Defoamer 0.1kg;

[0100] Auxiliary color paste components include:

[0101] White high alumina cement 45kg;

[0102] Silica fume 14kg;

[0103] Rock chip 5kg;

[0104] Beige colored sand 15kg;

[0105] Color sand blue ash 18kg;

[0106] Pigment orange 5kg;

[0107] High-performance polycarboxylate superplasticizer 0.5kg;

[0108] Xanthan gum 0.4kg;

[0109] Attapulgite clay 5kg;

[0110] Polyethylene oxide 0.2kg;

[0111] Home...

Embodiment 3

[0119] Use natural or pre-processed stone models to reproduce molds according to market and customer needs. Prepare main color paste and auxiliary color paste, wherein the main color paste components include:

[0120] White Portland cement 50kg;

[0121] Fly ash 10kg;

[0122] Colored sand violet 5kg;

[0123] Beige colored sand 15kg;

[0124] Red top red colored sand 15kg;

[0125] Pigment iron oxide yellow 3kg;

[0126] High-performance polycarboxylate superplasticizer 0.5kg;

[0127] Starch ether 0.05kg;

[0128] Tartaric acid 0.02kg;

[0129] Defoamer 0.1kg;

[0130] Auxiliary color paste components include:

[0131] Sulphoaluminate cement 50kg;

[0132] Slag 13kg;

[0133] Colored sand violet 4kg;

[0134] Beige colored sand 15kg;

[0135] Red top red colored sand 15kg;

[0136] Pigment brown red 5kg;

[0137] High-performance polycarboxylate superplasticizer 0.5kg;

[0138] Xanthan gum 0.4kg;

[0139] Attapulgite clay 5kg;

[0140] Polyethylene oxide 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an artificial texture stone and a production method of the artificial texture stone. The method comprises the following steps of: preparing main color slurry and auxiliary color slurry; pouring the main color slurry and the auxiliary color slurry onto a material guide rail, and forming a pre-mixed colorful slurry body with different colors and different textures through helical push; making the pre-mixed colorful slurry body naturally flow into a die to form naturally flowing color textures; and forming. According to a formula and the production method for the artificial texture stone which is scientific in component proportion and rational in process, the process is unique, and the cost is low; the produced product is outstanding in surface texture, and the textures are vivid; and the decoration effect of the product is enhanced.

Description

technical field [0001] The invention relates to an artificial stone, in particular to an artificial stone with natural lines and clear boundary color texture throughout the body, and a production method of the artificial stone. Background technique [0002] In recent years, with the rapid development of the real estate industry, natural stone has attracted widespread attention for its beautiful decorative effects and simple craftsmanship, and has developed rapidly. But today's natural stone is a non-renewable resource after all, and the processing procedures are relatively cumbersome, the density is high, the transportation is inconvenient, and the price is relatively high. [0003] Artificial stone has also been promoted and applied to a certain extent because of its simple and beautiful decorative effect and low price imitating natural stone. For example, the artificial stone disclosed in patent CN100348540C is made of inorganic substances such as silica, alumina, sodium ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B28/04C04B111/54C04B111/82
Inventor 陈国迈陈迈华夏艺由继业曾亮孙祥山周伟龙
Owner SHANGHAI APE STONE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap