Single-component room-temperature-vulcanized fluorosilicone rubber and preparation method thereof

A room temperature vulcanization, fluorosilicone rubber technology, applied in the field of one-component room temperature vulcanized fluorosilicone rubber and its preparation, can solve the problems of poor compatibility between fluororubber and silicone rubber, reduced tear strength, and poor cold resistance of fluororubber , to achieve the effect of good sealing and bonding performance, good performance and excellent oil resistance

Active Publication Date: 2013-01-02
安徽斯迈特新材料股份有限公司
View PDF6 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, fluorine rubber and silicone rubber have poor compatibility, even if they are mixed, the mechanical strength, tensile strength, tear strength and other properties of the mixed rubber will be significantly reduced, and will delaminate during use
In addition, after mixed use, the cold resistance of fluorine rubber deteriorates
At present, there is no domestic patent report on the preparation of one-component room temperature vulcanized fluorosilicone rubber. US5342879 and US6369155 are organopolysiloxanes with trifluoropropyl groups added with fillers and vulcanizing agents to prepare oil-resistant fluorine-containing high-temperature vulcanized silicon rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Under the protection of dry nitrogen, 1500 grams of hydroxyl-terminated fluoropolysiloxane (25 ° C, 50000 mpa s), 300 grams of heavy calcium, 150 grams of LM-150 (gas-phase silica, produced by Cabot Corporation), Add 150 grams of methyl tributyl ketoxime silane, 30 grams of vinyl tributyl ketoxime silane, 30 grams of KH550, 15 grams of KH560, 3 grams of dibutyltin dilaurate and 20 grams of methyl fluorine-containing silicone oil into the high-speed dispersion After dispersing evenly in the kettle at high speed, use polyethylene plastic bottles for airtight packaging. The performance test of the obtained one-component room temperature vulcanized fluorosilicone rubber is shown in Table 1.

[0024]

Embodiment 2

[0026] Under the protection of dry nitrogen, 1,500 grams of hydroxyl-terminated fluoropolysiloxane (25 ° C, 50,000 mpa s), 300 grams of titanium dioxide, 150 grams of LM-150 (gas-phase silica, produced by Cabot Corporation), Add 120 grams of methyltriacetoxysilane, 40 grams of KH560, 3 grams of tin acetate and 20 grams of methyl fluorine-containing silicone oil into the high-speed dispersion kettle in sequence. After uniform dispersion at high speed, use polyethylene plastic bottles for airtight packaging. The performance test of the obtained one-component room temperature vulcanized fluorosilicone rubber is shown in Table 1.

[0027]

Embodiment 3

[0029] Under the protection of dry nitrogen, 1000 grams of hydroxyl-terminated fluoropolysiloxane with a viscosity of 80000mpa·s, 500 grams of hydroxyl-terminated fluoropolysiloxane with a viscosity of 20000mpa·s, and 300 grams of nano-calcium (modified light calcium carbonate), 150 grams of LM-150 (fumed white carbon black, produced by Cabot), 150 grams of methyltrimethoxysilane, 30 grams of isopropyl titanate, 30 grams of KH550, 15 grams of KH560, 3 grams Add dibutyltin dilaurate and 20 grams of methyl fluorine-containing silicone oil into the high-speed dispersion kettle in sequence, and after high-speed dispersion is uniform, use polyethylene plastic bottles for airtight packaging. The performance test of the obtained one-component room temperature vulcanized fluorosilicone rubber is shown in Table 1.

[0030]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a single-component room-temperature-vulcanized fluorosilicone rubber which is prepared from the following raw materials in parts by weight: 100 parts of hydroxyl-terminated fluorine-containing polysiloxane, 1-30 parts of inorganic filler, 3-15 parts of crosslinking agent, 2-5 parts of silane coupling agent, 0-3 parts of titanate coupling agent, 0.1-0.5 part of catalyst and 0-2 parts of methyl fluorosilicon oil. The preparation method comprises the following steps: evenly dispersing the raw materials in a closed high-speed dispersion machine at room temperature in a dry nitrogen protective atmosphere, and packaging in a closed environment. The single-component room-temperature-vulcanized fluorosilicone rubber has the advantages of excellent oil resistance, favorable sealing and bonding properties and favorable performance, can be used for fuel-resistant sealing (such as aircraft and automobile fuel tanks, and oil tank and tank truck pipelines), can be cured into an elastomer at room temperature, and is convenient for processing and application, thereby being an indispensable oil-resistant sealing material for aviation industry and automobile industry in China as well as a necessary fuel-resistant sealing material for sealing of overall aircraft fuselage, fuel tanks and engine platforms.

Description

technical field [0001] The invention relates to a one-component room temperature vulcanized fluorosilicone rubber and a preparation method thereof. Background technique [0002] Room temperature vulcanized silicone rubber (RTV) is a silicone rubber product that came out in the 1960s. This rubber has good heat resistance, cold resistance and excellent electrical insulation properties of silicone rubber. More importantly, it is easy to use and can be used at room temperature. It can be vulcanized without heat or pressure. One-component room temperature vulcanized silicone rubber is made by mixing all its components evenly and packing them in a sealed container. When used, it is extruded from the sealed container and cross-linked into a silicone elastomer after contacting water in the air. Because fluororubber has excellent heat resistance, oil resistance, fuel resistance, compression recovery and other properties, fluororubber is widely used as some parts of automobiles, air...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/08C08K13/02C08K5/54
Inventor 田建国侯智杰
Owner 安徽斯迈特新材料股份有限公司