Polymer rubber composite material

A foamed rubber and composite material technology, applied in the field of composite materials, can solve the problems of poor anti-skid performance, poor softness and elasticity, poor flexibility and resilience performance, etc., to improve strength and wear resistance, Improve compatibility and bonding, improve resilience

Inactive Publication Date: 2013-03-13
JINJIANG CHENGCHANG SHOES
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) is light in weight and easy to shape, but the softness and elasticity of the material are not good, and even if the softness partially meets the requirements, its

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Specific embodiment one of the present invention is as follows:

[0027] The foamed rubber composite material is composed of a mixture of rubber particles, fillers, coupling agents, metal oxides, lubricants, foaming agents, and bridging agents. The ratio of each component is:

[0028] Rubber pellet raw materials: 100kg, the proportion of which is: 35kg EVA (ethylene vinyl acetate), 25kg POE (polyolefin elastomer), 20kg EPDM rubber; 20kg chlorinated polyethylene rubber;

[0029] Filling agent: 20kg of talcum powder;

[0030] Coupling agent: 0.1kg of silane coupling agent is used;

[0031] Metal oxide: 0.6kg of ZnO is used as foaming aid and active agent;

[0032] Lubricant: 0.2kg of stearic acid and 0.3kg of zinc stearate;

[0033] Foaming agent: 4kg AC azo foaming agent is used;

[0034] Cross-linking agent: 1kg dicumyl peroxide;

[0035] The production process is as follows:

[0036] 1) Mix 100kg of raw materials of rubber particles with 20kg of talc powder, 0.6kg of ZnO, 0.2kg of s...

Example Embodiment

[0040] The second embodiment of the present invention is as follows:

[0041] The foamed rubber composite material is composed of a mixture of rubber particles, fillers, coupling agents, metal oxides, lubricants, foaming agents, and bridging agents. The ratio of each component is:

[0042] Rubber pellet raw material: 100kg, the proportion of which is: 40kg EVA (ethylene vinyl acetate), 20kg POE (polyolefin elastomer), 20kg EPDM rubber; 20kg chlorinated polyethylene rubber;

[0043] Filler: 2kg calcium carbonate is used;

[0044] Coupling agent: 15kg of titanate coupling agent;

[0045] Metal oxide: 2kg of ZnO is used as foaming aid and active agent;

[0046] Lubricant: 1kg of stearic acid and 1kg of zinc stearate;

[0047] Foaming agent: 0.5kg AC azo foaming agent;

[0048] Crosslinking agent: 0.4kg dicumyl peroxide is used;

[0049] The production process is as follows:

[0050] 1) Mix 100kg of raw materials of colloidal particles with 2kg of calcium carbonate, 2kg of ZnO, 1kg of stearic ac...

Example Embodiment

[0054] The third embodiment of the present invention is as follows:

[0055] The foamed rubber composite material is composed of a mixture of rubber particles, fillers, coupling agents, metal oxides, lubricants, foaming agents, and bridging agents. The ratio of each component is:

[0056] Rubber pellet raw materials: 100kg, the proportion of which is: 30kg EVA (ethylene vinyl acetate), 30kg POE (polyolefin elastomer), 20kg EPDM rubber; 20kg chlorinated polyethylene rubber;

[0057] Filler: use 15kg of talc or calcium carbonate;

[0058] Coupling agent: 10kg of silane coupling agent or titanate coupling agent;

[0059] Metal oxide: 1kg of ZnO is used as foaming aid and active agent;

[0060] Lubricant: use 0.7kg of stearic acid and 0.8kg of zinc stearate;

[0061] Foaming agent: 2kg AC azo foaming agent is used;

[0062] Cross-linking agent: 0.6kg dicumyl peroxide;

[0063] The production process is as follows:

[0064] 1) Combine 100kg of raw materials of colloidal particles with 15kg of tal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite material, in particular to a polymer rubber composite material specially applied to assemblies such as shoe materials, sports goods and leather. The polymer rubber composite material is mainly prepared from a colloidal particle raw material, a filling agent, a coupling agent, a metal oxide, a lubricating agent, a foaming agent and a bridging agent which are mixed according to a certain proportion, wherein the colloidal particle raw material is prepared from mixing EVA (ethylene vinyl acetate) and POE (polyolefin elastomer) with modified ethylene propylene diene monomer and chlorinated polyethylene rubber. The modified ethylene propylene diene monomer and the chlorinated polyethylene rubber are introduced in a formula, meanwhile, the coupling agent is introduced in the formula for improving compatibility and bonding property of all component materials and improving strength and anti-abrasion property of the composite material, and therefore the resilience, the flexibility and the abrasive resistance of the polymer rubber composite material are greatly improved, and the texture and the anti-slip property of the polymer rubber composite material can reach the grade of a rubber material.

Description

technical field [0001] The invention relates to a composite material, especially a foam rubber composite material specially used for shoe materials, sporting goods, leather and other components. Background technique [0002] Most of the existing EVA adopts the production method of POE modified materials. The modified materials are suitable for injection molding and compression molding. They can be widely used in shoe outsoles, sporting goods and other light industrial products. The ingredients are composed of 50-95% EVA, 5 -40% POE (polyolefin elastomer), 5-20% talcum powder or CaCO3, metal oxide 1-2%, lubricant 0.1-1%, peroxide (bridging agent) 0.4-1%, even Nitrogen foaming agent 1-4% and appropriate amount of pigment are mixed by internal mixer, auxiliary mixing by open mixer, pelletizing, injection molding or compression molding. The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) is light in weight and easy to shape, but the softness and el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L23/00C08L23/16C08L23/28C08K13/02C08K3/34C08K3/26C08K5/098C08K3/22C08J9/10
Inventor 李灿升
Owner JINJIANG CHENGCHANG SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap