Polyvinyl chloride (PVC) cable material for automobile data transmission wire

A technology for data transmission and automotive wiring, applied in plastic/resin/wax insulators, organic insulators, etc., can solve the problems of complex process and high cost, and achieve the effect of simple process, low cost and elimination of odor

Active Publication Date: 2013-03-13
JIANGSU HENGTONG ELECTRONICS CABLE TECH CO LTD
View PDF9 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wear resistance of the cable material in the above-mentioned patents needs to be further improved.
In recent years, with the development of irradiation technology, the development of cross-linked cable materials has been promoted. Irradiation cross-linked PVC insulation materials can significantly improve the wear resistance of materials, but the process is complicated and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl chloride (PVC) cable material for automobile data transmission wire
  • Polyvinyl chloride (PVC) cable material for automobile data transmission wire
  • Polyvinyl chloride (PVC) cable material for automobile data transmission wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] SG3 type PVC resin: 100 parts, trioctyl trimellitate: 25 parts, epoxy soybean oil: 2 parts, dioctyl terephthalate: 3 parts, nano calcium carbonate: 10 parts, commercially available calcium zinc Stabilizer: 8 parts, polyethylene wax: 0.8 parts, ACR impact modifier: 4 parts, bisphenol A: 0.2 parts, nano barium sulfate: 2 parts, silicone powder: 0.6 parts; the silicone powder The body is nanocrystalline silicon dioxide powder coated with silicone (the parts by weight of the silicone powder are 0.2 parts by weight, and the parts by weight of the silicon dioxide powder are 0.4 parts by weight).

Embodiment 2

[0023] SG3 type PVC resin: 100 parts, trioctyl trimellitate: 30 parts, dioctyl terephthalate: 3 parts, nano calcium carbonate: 12 parts, commercially available calcium zinc stabilizer: 12 parts, polyethylene Wax: 1.2 parts, ACR impact modifier: 3 parts, bisphenol A: 0.2 parts, nano barium sulfate: 2 parts, silicone powder: 0.6 parts; the silicone powder is coated with silicone Nanocrystalline silicon dioxide powder (the parts by weight of the silicone powder are 0.2 parts, and the parts by weight of the silicon dioxide powder are 0.4 parts).

Embodiment 3

[0025] SG3 type PVC resin: 100 parts, trioctyl trimellitate: 28 parts, epoxy soybean oil: 2 parts, dioctyl terephthalate: 2 parts, nano calcium carbonate: 10 parts, commercially available calcium zinc Stabilizer: 10 parts, polyethylene wax: 0.8 parts, ACR impact modifier: 2 parts, bisphenol A: 0.2 parts, nano barium sulfate: 2 parts, silicone powder: 0.6 parts; the silicone powder The body is nano-amorphous silicon dioxide powder coated with silicone (the parts by weight of the silicone powder are 0.2 parts by weight, and the parts by weight of the silicon dioxide powder are 0.4 parts by weight).

[0026] The commercially available calcium-zinc stabilizer described in Examples 1-3 is the 519A calcium-zinc stabilizer suitable for wires and cables produced by Jiangxi Hongyuan Chemical Co., Ltd.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polyvinyl chloride (PVC) cable material for an automobile data transmission wire. The PVC material comprises the components based on parts by weight: 100 parts of SG3 type PVC resin, 25-30 parts of plasticizer 1, 3-5 parts of plasticizer 2, 10-12 parts of calcium carbonate, 8-12 parts of stabilizer, 0.8-1.2 parts of polyethylene wax, 2-4 parts of ACR impact modifier, 0.1-0.5 part of antioxidant, 2-3 parts of nano barium sulfate and 0.3-0.8 part of silicone powder, wherein the plasticizer 1 comprises one or two selected from trioctyl trimellitate or purified terephthalic acid dioctyl ester; the plasticizer 2 comprises one or two selected from epoxidized soybean oil and terephthalic acid dioctyl ester; and the silicone powder is silica powder treated by silicone. The PVC cable material has the temperature classification of 105 DEG C, thus having good processability under the condition of high-speed processing; and the obtained cable has excellent abrasion resistance and mechanical property, and the odor can be eliminated.

Description

technical field [0001] The invention relates to the technical field of insulating cable materials, more specifically, the invention relates to a PVC cable material for data transmission automobile wires. Background technique [0002] Polyvinyl chloride material has good rigidity, high strength, flame retardancy, corrosion resistance, good electrical insulation, good processing performance and low price, so it is widely used in the cable material industry. Usually, automotive wires are usually made of polyvinyl chloride resin as the base material, adding plasticizers, stabilizers and processing aids, and processed by special mixing equipment. Automobile wires and cables are different from ordinary wires and cables, and are specially designed for the needs of automobiles. Since the interior of the car is a very complicated small environment, there are various complex conditions such as vibration, friction, oil pollution, high heat, cold and electromagnetic radiation, so the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/00C08K13/06C08K9/10C08K3/26C08K3/30C08K5/12C08K5/1515C08K3/36H01B3/44
Inventor 王惠兵吕秀云陈夏裕金春敏钱江华
Owner JIANGSU HENGTONG ELECTRONICS CABLE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products