Low-density polyethylene-modified polyvinyl chloride (PVC) synthetic leather and manufacturing method thereof

A low-density polyethylene and polyvinyl chloride technology, used in chemical instruments and methods, synthetic resin layered products, dyed low-molecular-weight organic compounds, etc., can solve the problems of hydrolysis resistance, insufficient weather resistance, product quality problems, residual and other problems, to achieve the effects of good vapor permeability and moisture absorption conductivity, high adhesion fastness, and increased flexibility

Inactive Publication Date: 2013-03-27
HEFEI ANSHAN COATING FABRICS
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistan

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A low-density polyethylene modified polyvinyl chloride synthetic leather, including a surface layer, a foam layer and an adhesive layer, and a raised cloth,

[0027] The surface layer is made of the following raw materials in parts by weight to form a slurry:

[0028] SG-1 type PVC resin 30-40, SG-6 type PVC resin 70-80, propylene glycol sebacate polyester 45-50, n-butyl methacrylate 20-25, PVC color paste 5-6, bisthioglycolic acid Isooctyl di-n-octyl tin 1-2, zinc stearate 1-2, light calcium carbonate 5-10, 4,4'-oxobisbenzenesulfonyl hydrazide 2-3, nano barite powder 40-45, Modified bentonite 50-60, isopropyl dioleic acid acyloxy (dioctyl phosphate acyloxy) titanate 1-2, antioxidant 1035 1-2, 3-aminopropyltrimethoxysilane 3 -4;

[0029] The foamed layer is prepared from the following raw materials in parts by weight:

[0030] SG-1 type PVC resin 40-50, SG-4 type PVC resin 70-80, low density polyethylene 30-40, acetyl triethyl citrate 30-35, dibutyl maleate 40-45, A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses low-density polyethylene-modified polyvinyl chloride (PVC) synthetic leather. The low-density polyethylene-modified PVC synthetic leather comprises a surface layer, a foamed layer, a bonding layer and a brushing fabric, and is characterized in that the surface layer is prepared by mixing the following raw materials in parts by weight to form slurry: 30 to 40 parts of SG-1 type PVC resin, 70 to 80 parts of SG-6 type PVC resin, 45 to 50 parts of propanediol sebacate polyester, 20 to 25 parts of n-butyl methacrylate, 5 to 6 parts of PVC color paste, 1 to 2 parts of di-hydrosulfo isooctyl chloroacetate di-n-octyl tin, 1 to 2 parts of zinc stearate, 5 to 10 parts of light calcium carbonate, 2 to 3 parts of 4,4'-oxo bi-benzenesulfonyl hydrazide, 40 to 45 parts of nano- barite powder and 50 to 60 parts of modified bentonite. Through the improvements of the formula and the process, the flexibility of the synthetic leather is improved, and the synthetic leather has a natural comfortable hand feeling similar to that of natural leather and is difficult to damage or tear after being used for 3 to 5 years.

Description

technical field [0001] The invention belongs to the technical field of chemical synthetic leather fabric processing, in particular to low-density polyethylene modified polyvinyl chloride synthetic leather and a manufacturing method thereof. Background technique [0002] At present, polyvinyl chloride synthetic leather modified by polyurethane and low-density polyethylene is widely used in commercial furniture and household furniture and other furniture fields. Polyurethane synthetic leather has the advantages of high imitation and good hand feeling, and has been widely favored by the market. However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process, and there will be a large amount of residual DMF even after sufficient drying, which becomes a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other problems lim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/06B32B27/12B32B27/18B32B37/02B32B37/12C09D4/02C09D4/06C09D7/12C09D4/00C09C1/42C09C3/08C09C3/06
Inventor 藏德虎
Owner HEFEI ANSHAN COATING FABRICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap