Process for coating isocyanate composition to interior of woven bag

A technology for coating isocyanates, woven bags, applied in textile and papermaking, one-component polyolefin rayon, spray/jet textile material processing, etc.

Inactive Publication Date: 2013-04-03
尚欣
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the deficiencies of the existing woven bag surface coating methods and provide a wear-resistant, corrosion-resistant, high-strength, long-life , while the production process is simple, high efficiency, non-polluting woven bag coating method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] According to the polypropylene resin that is 100 parts by weight, add the antioxidant 1010 that is 0.4 part by weight, the ultraviolet absorber UV-327 that is 0.5 part by weight, the auxiliary antioxidant DLTP that is 0.6 part by weight; The mixture obtained is passed The extruder and wire drawing machine are stretched and wound to make polypropylene filament. On a circular loom, polypropylene yarn is used as warp and weft to weave a cylindrical fiber braided layer, and then the paint is sprayed on the inner side of the braided layer to form an inner lining. The paint includes the following components (parts by mass) and content:

[0017] Ethylene-vinyl acetate copolymer 16

[0018] Polyvinyl alcohol 56

[0019] Isocyanate 16

[0020] Polyether diol 35

[0021] Diethyltoluenediamine 10.

[0022] After the above-mentioned coating components are fully mixed on-site, under the conditions of temperature 45°C and pressure 10MPa, use a spray gun to spray on the inner side...

Embodiment 2

[0024] Repeat embodiment 1, the coating process of woven bag is roughly the same as embodiment 1, and difference is that coating comprises following component (mass part) and content:

[0025] Ethylene-vinyl acetate copolymer 20

[0026] Polyvinyl alcohol 65

[0027] Isocyanate 25

[0028] Polyether diol 26

[0029] Diethyltoluenediamine 20

[0030] The spraying temperature is 60°C, the spraying pressure is 15MPa, and the spraying thickness is 0.6mm.

Embodiment 3

[0032] Repeat embodiment 1, the coating process of woven bag is roughly the same as embodiment 1, and difference is that coating comprises following component (mass part) and content:

[0033] Ethylene-vinyl acetate copolymer 18

[0034] Polyvinyl alcohol 60

[0035] Isocyanate 20

[0036] Polyether diol 30

[0037] Diethyltoluenediamine 15

[0038] The spraying temperature is 53°C, the spraying pressure is 13MPa, and the spraying thickness is 0.3mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

A process for coating isocyanate composition to the interior of a woven bag comprises the following steps: weaving warps and wefts, which are made from fiber material, into a cylindrical fiber braid layer on a circular weaving machine; coating material prepared on site is sprayed to the inner side of the braid layer to form an inner lining, wherein the coating material comprises the following components in part by mass: 16-20 parts of ethylene-vinyl acetate copolymer, 56-65 parts of polyvinyl alcohol, 16-25 parts of isocyanate, 26-35 parts of polyether glycol and 10-20 parts of diethyl methyl benzene diamine; and drying to obtain the woven bag product with the inner coating.

Description

technical field [0001] The invention relates to a coating method, in particular to the process of coating an isocyanate composition inside a woven bag. Background technique [0002] Woven bags are widely used in industry, agriculture, construction and other industries to transport powder products. Woven bags are usually woven from cross-woven wires, and there are tiny gaps at the intersections of the woven wires. In order to make up for this defect, people have used polyethylene resin for the surface coating of woven bags. This coating is easy to age and fall off, is not wear-resistant, and has a short service life. The manufacturing method of this kind of surface coated woven bag is: weave the fiber tube on the circular loom first, then add the coating resin into the extruder, extrude the hot melt film through the extruder, and coat it on the braided tube The outer surface of the object becomes a product. This production method requires more production equipment, consum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/568D06M15/333D06B1/02D01F6/46D06M101/20
Inventor 尚欣
Owner 尚欣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap