Bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet material and preparation method thereof

A basalt fiber and reinforced thermoplastic technology is applied in the field of bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet and its preparation. performance effect

Active Publication Date: 2013-04-24
LIAONING LIAOJIE SCI & TECH
View PDF2 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In the prior art, basalt fiber and thermosetting resin are used to composite. Although this composite material has high strength and high impact resistance, the disadvantage is that the therm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet material and preparation method thereof
  • Bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]A mixture of 40 parts by weight of polypropylene resin and 0.5 parts by weight of isopropyl triisostearate titanate titanate coupling agent is fully mixed in a high-speed mixer, melted and mixed with parts by weight It is composited with 60 parts of continuous basalt fiber, and made into continuous basalt fiber reinforced polypropylene (PP / BF) unidirectional prepreg tape after flattening, and the continuous basalt fiber reinforced polypropylene unidirectional prepreg tape (prepreg tape specification: thickness 0.2mm, width 650mm, length ≥ 1m) cut into a prepreg tape with a width of 200mm and a length of 1m, and then lay it criss-cross to 15 layers, put it into the mold, and send it into the mold when the temperature reaches 185°C In the hot press, the pressure is 1 MPa, and the holding time is 30 minutes. After the heat preservation is over, it is sent to a cold press with a pressure of 2 MPa and a pressure hold of 30 minutes. The mold is released to obtain a two-way co...

Embodiment 2

[0041] A mixture of 50 parts by weight of polyvinyl chloride resin and 0.2 parts by weight of bis(dioctyloxypyrophosphate) ethylene titanate and triethanolamine chelate titanate coupling agent , after fully mixing uniformly in a high-speed mixer, melt and compound with continuous basalt fiber of 50 parts by weight, and flatten to make continuous basalt fiber reinforced polyvinyl chloride (PVC / BF) unidirectional prepreg tape, the continuous basalt Fiber-reinforced polyvinyl chloride unidirectional prepreg tape (prepreg tape specifications: thickness 0.27mm, width 10mm, length ≥ 5m) is cut into a prepreg tape with a width of 10mm and a length of 5m, and then criss-cross Lay up to 100 layers, put it into the mold, and when the temperature reaches 170°C, send it into a hot press with a pressure of 1.5 MPa and a holding time of 40 minutes. After the heat preservation is over, it is sent to a cold press with a pressure of 2.5 MPa and a pressure hold of 60 minutes. Extruded from the...

Embodiment 3

[0045] The polybutylene terephthalate resin of 50 parts by weight and the mixture of two (dioctyl phosphite base) isopropyl titanate titanate coupling agents of 0.4 parts by weight are mixed at high speed After fully mixing in the machine, it is melted and compounded with continuous basalt fiber of 50 parts by weight, and flattened to make PBT / BF unidirectional prepreg tape, and the continuous basalt fiber reinforced PBT unidirectional prepreg tape (prepreg tape specification : The thickness is 0.3mm, the width is 650mm, and the length is ≥1m) cut into a prepreg tape with a width of 650mm and a length of 1m, and then lay it in a criss-cross pattern to 200 layers, put it into the mold, and wait until the temperature reaches 218°C , into the hot press, pressure 1MPa, holding time 30min. After the heat preservation is over, it is sent to a cold press with a pressure of 3 MPa and a pressure hold of 70 minutes. The mold is released to obtain a two-way continuous basalt fiber reinf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Melt indexaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of high polymer material, and discloses a bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet material and a preparation method thereof. The composite sheet material is prepared from the following components by weight: 40-60 parts of a thermoplastic resin, 40-60 parts of a continuous basalt fiber and 0.2-0.5 part of a titanate coupling agent. The invention also discloses a preparation method of the bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet material. The bidirectional continuous basalt fiber reinforced thermoplastic resin composite sheet material provided by the invention has good flame resistance, high temperature resistance, comprehensive performance and a low price.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a bidirectional continuous basalt fiber reinforced thermoplastic resin composite plate and a preparation method thereof. Background technique [0002] Continuous fiber reinforced thermoplastic resin is composed of fiber and resin. Most thermoplastic resins have low tensile strength, but have high toughness and plasticity; fibers have high tensile strength, but are easily damaged and Not easy to form and process. The combination of fiber and resin complements the defects of the two, so that the comprehensive performance of continuous fiber reinforced thermoplastic resin composites is greatly improved. Compared with traditional steel and aluminum, its density is about 1 / 5 of steel and about 1 / 2 of aluminum; its specific strength and specific modulus are much higher than those of steel and aluminum alloys, so in terms of stiffness and strength Under the same conditions, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L27/06C08L67/02C08L77/02C08L69/00C08K7/10C08K3/34C08J5/06
Inventor 邢明祥
Owner LIAONING LIAOJIE SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap