Flexible heat-preserving tapestry brick and preparation method thereof

A facing brick and flexible technology, applied in the field of building thermal insulation and decoration materials, can solve the problems that inorganic materials are difficult to disperse evenly, affect the mechanical properties of products, lack thermal insulation fillers, etc., achieve safety integration, improve mechanical properties, and high utilization rate of raw materials Effect

Active Publication Date: 2013-05-22
南通南京大学材料工程技术研究院
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing flexible facing bricks lack thermal insulation fillers in composition, and in the production method, polymer emulsion and mud powder are directly mixed at high speed, which can easily cause emulsion breakage and seriously affect the mechanical properties of the final product.
If the resin and mud powder are directly blended, it is difficult for the inorganic material to disperse evenly in the high-viscosity resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Attapulgite 30%, fly ash floating beads 25%, butyl acrylate 15%, methyl methacrylate 10%, acrylic acid 3%, ethyl acetate 5%, ammonium polyphosphate 10%, azobisisobutyronitrile 0.5 %, 1.5% of glass fibers with a diameter of 2 μm and a length of 3 mm are mixed in a high-speed disperser to form a slurry and poured into a mold, placed in an oven at 80 ° C for 30 minutes, removed from the mold, and then placed at 80 ° C Insulate in the oven for 1 hour, take out the trimmed edges, and obtain gray flexible thermal insulation facing bricks.

Embodiment 2

[0032] Silicone oil modified kaolin 40%, fly ash floating beads 30%, ethyl acrylate 10%, methyl methacrylate 5%, acrylic acid 2%, ethyl acetate 3%, ammonium polyphosphate 7%, benzoyl peroxide 1%, 2% of glass fiber with a diameter of 4 μm and a length of 6 mm are mixed according to mass parts and ball milled in a ball mill to obtain pre-aggregated powder, then filled into a mold for compaction, placed in an oven at 110 ° C for 40 minutes, ejected, and then placed in Insulate in an oven at 110°C for 3 hours, take out the trimmed edges, and obtain a light red flexible thermal insulation facing brick.

Embodiment 3

[0034] Silicone oil modified bentonite 20%, fly ash floating beads 40%, butyl acrylate 15%, methyl methacrylate 10%, hydroxyethyl acrylate 5%, ammonium polyphosphate 6%, azobisisobutyronitrile 1% , 3% glass fiber with a diameter of 4 μm and a length of 3 mm is mixed according to mass parts, mixed into a slurry in a high-speed disperser and poured into a mold, placed in a 90°C oven for 30 minutes, ejected from the mold, and continued to be placed in a 90°C oven Keep warm for 1 hour, take out the cut edge, and get gray flexible heat preservation facing brick.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flexible heat-preserving tapestry brick and a preparation method of the flexible heat-preserving tapestry brick. The raw material of the brick is sizing agent or dry power formed by evenly mixing mud powder, a hollow filler, crylic acid monomers, a cross-linking agent, reinforced fibers, a solvent, an initiator and a fire retardant according to a certain proportion. The preparation method comprises the following steps of: forming in a mould in a heating way, drawing, drying, trimming and the like to obtain the flexible tapestry brick with the functions of heat preservation and flame retardance. The flexible heat-preserving tapestry brick has the characteristics of being flexible, heat-preserving, water-resistant, fire-resistant, anti-stain, anti-aging, scrubbing-resistant, low in specific gravity, simple in production process, low in cost and the like, thereby being widely applicable to the decoration indoors and outdoors.

Description

technical field [0001] The invention relates to the field of building thermal insulation and decoration materials, in particular to a flame-retardant flexible decorative brick for external thermal insulation of building exterior walls and a preparation method thereof. Background technique [0002] In recent years, severe fires caused by building insulation materials have occurred frequently, causing heavy casualties and property losses. In order to learn lessons from the “11.15” fires in the Jiaozhou Road teachers’ apartments in Shanghai and the “2.3” fires in Shenyang Wangchao Wanxin Building, on March 14, 2011, the Fire Department of the Ministry of Public Security issued a public document (2011) No. 65 "About Further Clarify the Relevant Requirements for Fire Supervision and Management of External Thermal Insulation Materials for Civil Buildings ", put forward emergency requirements for the use and management of thermal insulation materials for external walls of buildings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/20C04B18/08C04B14/22C04B14/18
CPCY02W30/91
Inventor 陆洪彬唐伟高扬之闻军
Owner 南通南京大学材料工程技术研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap