Roller-coating type high-durability multifunctional flight deck skid-resistant coating

A technology for flight decks and anti-skid coatings, applied in coatings and other directions, can solve problems such as poor weather resistance, harsh construction environment requirements, and long cycle times, and achieve excellent resistance to various chemical solvents and oils, low construction environment requirements, and high durability. Good high and low temperature effect

Active Publication Date: 2015-06-17
江阴市大阪涂料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the overall performance of the coating is average, especially the data such as pedaling comfort and friction coefficient are still far from the actual requirements.
Moreover, the current deck paint has the disadvantages of cumbersome construction, long cycle, harsh requirements on the construction environment, low bonding strength of anti-skid materials and coating systems, and poor weather resistance.
[0004] During the technical investigation, it was found that the deck coating of the traditional sand-spraying process currently used is very serious to the wear and tear of the cables and soldiers' shoes on the ship, causing certain safety hazards
At the same time, it is difficult to clean during the daily maintenance process. During the repair, the construction period is prolonged due to the construction of multiple layers of coatings, which causes a lot of inconvenience.
The anti-skid sand in the coating is easy to fall off from the paint film, which poses a potential hidden danger to the safety of precision electronic instruments and personnel on board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roller-coating type high-durability multifunctional flight deck skid-resistant coating
  • Roller-coating type high-durability multifunctional flight deck skid-resistant coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Proportionally mix 15kg of epoxy-modified silicone resin, 10kg of toughened elastic resin, and 8kg of solvent for 10min, then add 2kg of dispersant, 10kg of heat-reflecting pigment, 3kg of metal oxide, and 2kg of thixotropic agent and stir at high speed for 40min, then add 10kg of curing agent, 15kg of silicon carbide and 25kg of metal aluminum particles were stirred for 5 minutes to obtain a roller-coated high-durability multifunctional anti-skid coating for flight decks;

[0024] Metal oxides are composed of CaO, MgO and ZrO 2 Composition of the mixture, the mass percentage of each component in the mixture is: 30%CaO, 30%MgO and 40%ZrO 2 .

[0025] Silicon carbide is formed by mixing silicon carbide particles with a particle size of 15-20 mesh and 30-40 mesh respectively, and the mass percentage of silicon carbide particles with a particle size of 15-20 mesh in the silicon carbide anti-skid particles is 50%;

[0026] The particle size of metal aluminum particles is ...

Embodiment 2

[0030] Proportionally mix 25kg of epoxy-modified silicone resin, 5kg of toughened elastic resin, and 3kg of solvent for 10 minutes, then add 1kg of dispersant, 5kg of heat-reflecting pigment, 1kg of metal oxide, and 5kg of thixotropic agent and stir at high speed for 40 minutes, then add 10kg of curing agent, 30kg of silicon carbide and 15kg of metal aluminum particles were stirred for 5 minutes to obtain a roller-coated high-durability multi-functional anti-skid coating for flight decks;

[0031] The composition of the thixotropic agent is: 50% polyamide wax, 50% fumed silica;

[0032] The mass percent of polyamide curing agent in curing agent is 55%;

[0033] All the other components are composed the same as in Example 1.

Embodiment 3

[0035] Proportionally mix 20kg of epoxy-modified silicone resin, 7kg of toughened elastic resin, and 4kg of solvent for 10 minutes, then add 2kg of dispersant, 12kg of heat-reflecting pigment, 2kg of metal oxide, and 1kg of thixotropic agent and stir at high speed for 40 minutes, then add 15kg of curing agent, 22kg of silicon carbide and 15kg of metal aluminum particles, stirred for 5 minutes to obtain a roller-coated high-durability multi-functional anti-skid coating for flight decks;

[0036] The composition of the thixotropic agent is: 50% polyamide wax, 50% fumed silica;

[0037] The mass percentage of polyamide curing agent in curing agent is 50%;

[0038] All the other components are composed the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a roller-coating type high-durability multifunctional flight deck skid-resistant coating. The roller-coating type high-durability multifunctional flight deck skid-resistant coating comprises epoxy modified organic silicon resin, toughened elastic resin, heat reflection pigment, metal oxide, silicon carbide, metal aluminum particle, a curing agent and a solvent. The coating can be applied to more base materials, has excellent adhesion to various base materials, and is particularly suitable for iron, aluminum alloy, thermal spraying metal and ceramic surface; moreover, the coating has excellent flexibility, skid-resistant abrasive resistance, salt spray resistance, ultraviolet ray resistance, fire prevention, high-temperature resistance, and resistance to various chemical solvents and oils; meanwhile, the coating has important performances of cooling by heat reflection, absorbing radar waves, reducing the heavy wear of the cable, and the like. The coating can be directly rolled, and can be used for simply and conveniently carrying out single-pass coating construction and repair; besides, the high and low temperature resistance is good, the construction is convenient and the requirements on the construction environment are low.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a roller-coated high-durability multifunctional anti-slip coating for flight decks. Background technique [0002] The most successful application of anti-slip coatings is on the decks of aircraft carriers and ships. The coatings increase the friction coefficient of the decks, and the coatings can prevent aircraft and vehicles from sliding on the decks when the aircraft carrier is sailing. It is precisely because of the above-mentioned special purposes that the research direction of anti-skid coating technology is becoming more and more refined. From general civilian use to anti-skid research specifically for aircraft carriers, a special anti-skid coating production and research center has been established. There are many kinds of anti-slip coatings and a wide range of uses, and special and general anti-slip coatings have emerged as the times require. For example, the EPOXO300C ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/06C09D7/12C09D5/00
Inventor 李一新陈雷江林峰
Owner 江阴市大阪涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com