Method for direct modifying and yarn flattening of reclaimed material woven bag
A technology of woven bags and recycled materials, applied in stretch spinning, rayon manufacturing, conjugated rayon, etc., can solve the problems of flat yarn strength reduction, plastic molecular structure damage, and affecting the quality of plastic packaging products, etc., to achieve Improve the tensile strength, increase the tensile strength, save the effect of the process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1.
[0017] After sorting, cleaning, draining, and crushing waste plastics, 100kg of broken plastics are obtained, and then 9kg of new polyolefin materials, 4.5kg of mica powder, 3kg of epoxy resin, 1kg of titanium dioxide, 0.5kg of paraffin and 0.5kg of calcium stearate are combined with The crushed plastic is mixed and put into a high-speed mixer to stir and mix evenly; the mixture is directly fed into the screw wire drawing extruder for heating, and the temperature is increased to 200°C for melting and plasticization; then the molten plastic mixture is directly sent to the filter for filtering; Then extrude the filtered plastic mixture from the die to extrude the plastic into a melted and soft film and squeeze it out; then pass the film through the water tank and cool it with water, and set the water temperature to 50°C; The film is cut into raw filaments by a roller blade, and the raw filaments are heated by an oven while drawing with traction. The draw ratio i...
Example Embodiment
[0019] Example 2.
[0020] After sorting, cleaning, draining and crushing waste plastics, 100kg of broken plastics are obtained, and then 10kg of new polyolefin materials, 5kg of mica powder, 3.5kg of epoxy resin, 1.1kg of titanium dioxide, 0.55kg of paraffin and 0.55kg of calcium stearate Mix with the broken plastic and put it into a high-speed mixer to stir and mix evenly; send the mixture directly into the screw drawing extruder for heating, increase the temperature to 208℃ for melting and plasticization; then send the molten plastic mixture directly into the filter for filtering ; Then extrude the filtered plastic mixture from the die, squeeze the plastic into a thin film in a melted state and squeeze it out; then pass the film through the water tank for water cooling, and set the water temperature to 55°C; The film is cut into raw filaments by a roller blade, and the raw filaments are heated by an oven while drawing with traction. The draw ratio is set to 6 times, and finall...
Example Embodiment
[0022] Example 3.
[0023] After sorting, cleaning, draining, and crushing the waste plastics, 100kg of broken plastics are obtained, and then 9-11kg of new polyolefin materials, 5.5kg of mica powder, 4kg of epoxy resin, 1.2kg of titanium dioxide, 0.6kg of paraffin and 0.6kg of stearin Calcium acid and crushed plastic are mixed and put into a high-speed mixer to stir and mix evenly; the mixture is directly fed into the screw drawing extruder for heating, and the temperature is increased to 215°C for melting and plasticization; then the molten plastic mixture is directly sent to the filter Filter the filtered plastic mixture from the die head, extrude the plastic into a melted and soft film and squeeze it out; then let the film pass through the water tank and perform water cooling, and set the water temperature to 60 ℃; Next, the film is cut into filaments by a roller blade, and the filaments are heated through an oven while drawing with traction force. The draw ratio is set to 6....
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap