Acrylic ester electrostatic flocking binding agent and preparation method thereof

An electrostatic flocking and acrylate technology, applied in the direction of ester copolymer adhesives, adhesive types, non-polymer adhesive additives, etc., can solve the problems that cannot meet the requirements of electrostatic flocking fabrics at the same time, and achieve excellent anti-corrosion Stain resistance, excellent water resistance, excellent high temperature resistance effect

Active Publication Date: 2013-07-24
LIAONING FIXED STAR FINE CHEM
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The modified acrylate electrostatic flocking adhesive often cannot meet the needs of electrostatic flock

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic ester electrostatic flocking binding agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Raw material ratio:

[0032] Lauryl alcohol polyoxyethylene (50) ether 1.2 grams, sodium lauryl sulfate 1.2 grams, itaconic acid 0.5 grams, N-methylol acrylamide 2.5 grams, acrylic acid 2 grams, butyl acrylate 75 grams, 21 grams of isooctyl acrylate, 10 grams of styrene, 2.39 grams of γ-methacryloxypropyl trimethoxysilane, 5 grams of epoxy resin E-44, 3.92 grams of adipate dihydrazide, 0.07 grams of sodium acetate gram, 0.4 gram of ammonium persulfate, 145 grams of deionized water;

[0033] Preparation:

[0034] 1) Take 50 grams of deionized water and all the emulsifiers, i.e. lauryl alcohol polyoxyethylene (50) ether, sodium lauryl sulfate, add them to the pre-milk kettle, fully dissolve, and then add the monomer i.e. itacan Acid, N-methylolacrylamide, acrylic acid, butyl acrylate, isooctyl acrylate, styrene and epoxy resin, fully stirred and emulsified to form a pre-emulsion;

[0035] 2) Mix 1% by weight of the pre-emulsion with γ-methacryloxypropyltrimethoxysilane...

Embodiment 2

[0042] Raw material ratio: 1.3 grams of lauryl alcohol polyoxyethylene (50) ether, 1.3 grams of sodium lauryl sulfate, 0.6 grams of itaconic acid, 2.6 grams of N-methylol acrylamide, 2.2 grams of acrylic acid, butyl acrylate 78 grams of ester, 23 grams of isooctyl acrylate, 11 grams of styrene, 2.54 grams of γ-methacryloxypropyl trimethoxysilane, 5.5 grams of epoxy resin E-44, 4.31 grams of adipate dihydrazide , 0.072 grams of sodium acetate, 0.43 grams of ammonium persulfate, 155 grams of deionized water, wherein the pre-milk still uses 60 grams of deionized water; the production process is the same as in Example 1.

Embodiment 3

[0044] Raw material ratio: 1.4 grams of lauryl alcohol polyoxyethylene (50) ether, 1.4 grams of sodium lauryl sulfate, 0.8 grams of itaconic acid, 2.8 grams of N-methylol acrylamide, 2.4 grams of acrylic acid, butyl acrylate 82 grams of ester, 25 grams of isooctyl acrylate, 11.5 grams of styrene, 2.7 grams of γ-methacryloxypropyl trimethoxysilane, 6 grams of epoxy resin E-44, 4.70 grams of adipate dihydrazide , 0.075 grams of sodium acetate, 0.45 grams of ammonium persulfate, 165 grams of deionized water, wherein the pre-milk kettle uses 70 grams of deionized water; the production process is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an acrylic ester electrostatic flocking binding agent and a preparation method thereof. The acrylic ester electrostatic flocking binding agent is a polymer emulsion which is prepared from the raw materials: polyoxyethylene dodecyl alcohol (50), sodium dodecyl sulfate, itaconic acid, N-hydroxymethyl acrylamide, acyclic acid, butyl acrylate, 2-ethylhexyl acrylate, styrene, gamma-methacryloxy propyl trimethoxyl silan, epoxy resin E-44, adipic acid dihydrazide, sodium acetate, ammonium persulfate and deionized water through seeded emulsion polymerization. The acrylic ester electrostatic flocking binding agent is an epoxy resin and organic silicon resin jointly-modified acrylic ester electrostatic flocking binding agent. The product has the advantages of flexibility, cold endurance, weather resistance and thermosetting stability and particularly has prominent water resistance and adhesive force.

Description

technical field [0001] The invention relates to an electrostatic flocking adhesive and its preparation method, which is an acrylate polymer emulsion co-modified by an epoxy resin and a silicone resin, and is especially suitable for the high fastness requirements of electrostatic flocking fabrics . Background technique [0002] Electrostatic flocking products have been widely used in textiles, automotive interiors, toys and other industries due to their practical functions such as wear resistance, sealing, sound insulation, heat insulation, anti-scalding, and anti-fouling. Electrostatic flocking adhesive is one of the key materials that affect the quality of electrostatic flocking products. Electrostatic flocking adhesives can generally be divided into two types: emulsion type and solvent type. The advantage of solvent type is that the curing temperature is lower, but there are disadvantages such as serious pollution and easy fire during drying. Emulsion adhesive is the mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J11/06C08F220/18C08F222/02C08F220/58C08F220/06C08F212/08C08F230/08C08F2/30C08F2/26
Inventor 李秀颖孙继昌郑文慧陈红梅王冠中杨菁
Owner LIAONING FIXED STAR FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap