Antistatic, moisture-regaining and dyeable core pattern complex fiber and fabric made by same

A composite fiber, skin-core technology, applied in fiber processing, plant fiber, cellulose/protein conjugated man-made filament, etc., can solve the problems of reduced antistatic effect, poor washing resistance of fabrics, and high relative cost. Self-cleaning and anti-fouling function, dry and soft feel, long-lasting and safe effect

Inactive Publication Date: 2013-08-07
世纪宝姿(厦门)实业有限公司
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it has poor hand feel, poor dyeability, and high cost
[0005] In the Chinese patent application CN1099823A, complexes of inorganic substances are used, such as sodium bisulfite, sodium thiosulfate, ammonium vanadate, copper sulfate, etc., and non-polymer organic compounds, such as alkyl quaternary ammonium chlorides, alkylamide halogenated Tre

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Synthesize the sheath-core composite fiber with the following ratio: the mass ratio of dyeable polyester / cotton fiber is 70 / 30.

[0031] Two screws are used to control their respective temperatures to melt the high-temperature and high-pressure cationic dyeable polyester (CDP) (A) and cotton fiber that form the sheath-core respectively, and transport them to the spinning box through their respective melt pipelines. Then the melt is sent to the sheath-core composite spinning assembly quantitatively by the metering pump, extruded, cooled, oiled, and wound to obtain the raw silk of the skin-core composite fiber, and the raw silk is stretched After shaping, the finished sheath-core fiber can be obtained. The spinning temperature is 255°C, the winding speed can be adjusted within the range of 2000m / min, the stretching temperature is 90°C, the setting temperature is 160°C, and the stretching ratio is 2.0 times.

[0032] The equilibrium moisture regain of this fiber is 2.1%, an...

Embodiment 2

[0039] Synthesize the sheath-core composite fiber with the following ratio: the mass ratio of polyethylene terephthalate / cotton fiber is 30 / 70.

[0040] Use two screws to control their respective temperatures to melt the high-temperature and high-pressure cationic polyethylene terephthalate and cotton fiber that form the sheath-core respectively, and transport them to the spinning box through their respective melt pipelines. , and then the melt is sent quantitatively to the sheath-core composite spinning assembly by the metering pump, extruded, cooled, oiled, and wound to obtain the raw silk of the skin-core composite fiber, and the raw silk is stretched and shaped The finished sheath-core fiber can be obtained. The spinning temperature is 270°C, the winding speed can be adjusted within the range of 1900m / min, the stretching temperature is 95°C, the setting temperature is 170°C, and the stretching ratio is 2.0 times.

[0041] The equilibrium moisture regain of this fiber is 3...

Embodiment 3

[0048] Synthesize sheath-core composite fibers with the following ratio: the mass ratio of atmospheric pressure boiling cationic dyeable polyester / bamboo fiber is 65 / 35.

[0049] Two screws are used to control their respective temperatures to melt the high-temperature and high-pressure cationic normal pressure boiling dyeable cationic dyeable polyester and bamboo fiber materials that form the sheath-core respectively, and transport them to the spinning machine through their respective melt pipelines. box, and then the melt is sent quantitatively into the sheath-core composite spinning assembly by the metering pump according to the regulations, extruded, cooled, oiled, and wound to obtain the raw silk of the skin-core composite fiber, and the raw silk is then drawn The finished sheath-core fiber can be obtained by stretching and setting. The spinning temperature is 255°C, the winding speed can be adjusted within the range of 1800m / min, the stretching temperature is 90°C, the se...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an antistatic, moisture-regaining and dyeable core pattern complex fiber and fabric made by the same. The core pattern complex fiber comprises a leather layer and a core layer, wherein the mass ratio of the leather layer to the core layer is 90/10 to 10/90; the core layer is made of polyhydroxy fibre or muti-carboxylic fibre with good hygroscopicity, dyeability and anti-static function; the leather layer is melt-spinnable superpolymer; and the complex fiber has various functions of good mechanical strength, hygroscopicity, anti-static function, dyeability and the like. The fabric made by combining the core pattern complex fiber with photocatalyst coating has the advantages that the fabric is antimicrobial and is disinfected; organic pollutants such as formaldehyde can be effectively removed; and the sustainability and the safety are high.

Description

technical field [0001] The invention relates to a sheath-core composite fiber, in particular to an antistatic, moisture-absorbing and dyeable sheath-core composite fiber Background technique [0002] During the processing and use of chemical fiber textiles, polyamide fibers will generate electrification when they are in contact with each other or with other objects. If the charge continues to accumulate and cannot be eliminated, it will cause various static phenomena. Static electricity makes it difficult to process polyamide textiles. Dust is easily absorbed during product use, and electric sparks generated by static electricity can cause explosions and fires. Therefore, conductive and antistatic fibers, as a high-tech, high-value-added polymer fiber material, have very important and extensive demands in civil, industrial, decorative and military applications. [0003] Commonly used antistatic methods are: (1) pure conductive polymer fiber, which has good antistatic effect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01D5/34B32B27/02B32B9/04D01F8/14D01F8/06D01F8/12D01F8/02D06M11/46D06M101/06D06M101/32D06M101/20D06M101/34
Inventor 殷青林
Owner 世纪宝姿(厦门)实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap