Inorganic functional coating for degrading formaldehyde by negative ions and preparation method of coating

A technology of inorganic functional coatings and negative ions, which is applied in the field of materials, can solve the problems that the combination of inorganic coatings cannot achieve the best effect, the number of released negative ions is limited, and the effect of negative ion release is affected. It achieves high thermal hardness, enhanced crosslinking density, and increased effect of density

Active Publication Date: 2013-09-11
华夏贝能(北京)生态科技有限公司
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There have been researches on inorganic coatings capable of releasing negative ions in the prior art, but the negative ion components added in most inorganic coatings are limited in the number of releasing negative ions, and the cost is high. The selection of raw materials for inorganic coatings and the relationship between raw materials The combination cannot achieve the best effect, which will affect the release effect of negative ions and the performance of the coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] An inorganic functional coating for degrading formaldehyde by negative ions, the coating is composed of component A and component B, wherein the raw materials and weight ratio of component A are as follows,

[0066] Yttria stabilized zirconia powder 2%;

[0067] Aluminum oxide powder 2%;

[0068] Silicon fume 2%;

[0069] Silicon carbide powder 2%;

[0070] Shell powder 5%;

[0071] Ground calcium carbonate powder 10%;

[0072] Coral Pink 1%;

[0073] Pearl powder 1%;

[0074] Kaolin 1%;

[0075] Bentonite 1%;

[0076] Carbon fiber 0.5%;

[0077] Hydroxyethylcellulose 0.8%;

[0078] Sodium hexametaphosphate 0.2%;

[0079] Zinc powder 5%;

[0080] Light calcium carbonate powder 10%;

[0081] Rutile titanium dioxide 1%;

[0082] Negative ion powder 2%

[0083] Talc powder 5%;

[0084] Diatomaceous earth 5%;

[0085] Retarder 0.3%;

[0086] Defoamer 0.2%; deionized water balance;

[0087] The sum of the distribution ratios of the groups in A above is 100%; ...

Embodiment 2

[0108] An inorganic functional coating for degrading formaldehyde by negative ions, the coating is composed of component A and component B, wherein the raw materials and weight ratio of component A are as follows,

[0109] Yttria stabilized zirconia powder 3%;

[0110] Aluminum oxide powder 3%;

[0111] Silicon fume 3%;

[0112] Silicon carbide powder 3%;

[0113] Shell powder 10%;

[0114] Ground calcium carbonate powder 15%;

[0115] Coral Pink 2%;

[0116] Pearl powder 2%;

[0117] Kaolin 5%;

[0118] Bentonite 5%;

[0119] Carbon fiber 0.8%;

[0120] Hydroxyethylcellulose 0.8%;

[0121] Sodium hexametaphosphate 0.5%;

[0122] Zinc powder 10%;

[0123] Light calcium carbonate powder 15%;

[0124] Rutile titanium dioxide 3%;

[0125] Negative ion powder 6%

[0126] Talc powder 5%;

[0127] Diatomaceous earth 5%;

[0128] Defoamer 0.2%; deionized water balance;

[0129] The sum of the distribution ratios of the groups in A above is 100%;

[0130] The raw mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The invention relates to an inorganic functional coating for degrading formaldehyde by negative ions and a preparation method of the coating. The coating comprises a component A and a component B, wherein the component A contains negative ion powder. The coating is high in abrasion resistance, hardness and high-temperature hot hardness, adhesive force and peeling strength and can be abraded for 9 hours, cross-linking density is greatly enhanced and compactness of the coating is increased as the coating is compounded with inorganic materials with different particle sizes, gaps among large-particle-size raw materials are filled up as the raw materials with different particle sizes are mixed, thermal stress dispersion among the large-particle-size raw materials is absorbed and buffered by small-particle-size raw materials, thermal stress concentration of the small-particle-size raw materials is resisted and isolated by the large-particle-size raw materials, the coating is environment-friendly and green, VOC (volatile organic compound) is avoided, a large number of negative ions can be generated, and the coating is superior to other products in the field.

Description

technical field [0001] The invention belongs to the field of materials, and in particular relates to an inorganic functional coating for anion-degrading formaldehyde and a preparation method thereof. Background technique [0002] As early as the 1970s, European scientists conducted a comprehensive and systematic study on the impact of indoor air and pointed out that among more than 500 organic substances detected from indoor air, there were more than 20 carcinogens. According to statistics in the World Health Organization's "World Health Report", nearly half of the world's people are exposed to indoor pollution. Patients suffering from respiratory diseases due to indoor environmental pollution account for 36% of the world's population, and chronic disease patients account for 23%. and lung cancer patients accounted for seventeen per thousand. The Indoor Pollution Detection and Observation Center of the China Interior Decoration Association has learned that among the many de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/04C09D7/12
Inventor 朱胜美张晟玮
Owner 华夏贝能(北京)生态科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com