Microwave dielectric ceramic BaCu2V2O8 with low temperature sintering function and preparation method thereof
A technology of microwave dielectric ceramics and low-temperature sintering, applied in the field of dielectric ceramic materials, can solve the problems of restricting low-temperature co-firing technology and the development and limitation of microwave multilayer devices, and achieve the effect of large application value and small temperature coefficient of resonance frequency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment
[0019] Table 1 shows four specific examples of different sintering temperatures constituting the present invention and their microwave dielectric properties. The preparation method is as above, and the microwave dielectric properties are evaluated by the cylindrical dielectric resonator method; the powder is mixed with Ag powder accounting for 20% of the powder mass, pressed and molded, and sintered at 670 ° C for 4 hours; X-ray diffraction Both phase analysis and SEM observation showed that BaCu 2 V 2 o 8 There is no chemical reaction with Ag, that is, BaCu 2 V 2 o 8 It can be co-fired with Ag electrodes at low temperature.
PUM
Property | Measurement | Unit |
---|---|---|
quality factor | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com