Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A calcium carbide slag and cement technology, applied in the cement field, can solve the problems of low cement antifreeze, waste of resources, high energy consumption, etc., and achieve the effects of overcoming frost, saving mineral resources, and high antifreeze
Inactive Publication Date: 2015-12-02
安徽济峰节能材料有限公司
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, there are mainly the following problems in cement production: (1) Limestone is mainly used as the main raw material, which is costly and will cause waste of resources and environmental pollution. Although some enterprises use industrial waste such as calcium carbide slag to produce cement clinker, the mixing is low. , high energy consumption; (2) The degree of antifreeze of cement is low, which can only meet the winter construction needs in some areas
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] After crushing and drying the cement ingredients, batching, grinding, and calcining, antifreeze is added to the cement clinker, and the parts by weight of each component are: 30 parts of limestone, 40 parts of carbide slag, and 0.5 part of iron raw material , 5 parts of clay, 5 parts of fly ash, 0.5 parts of cement reinforcing agent, 0.3 parts of antifreeze, 5 parts of gypsum, 1 part of short-wave fiber, 1 part of modifier, and 2 parts of corrosion-resistant components.
Embodiment 2
[0015] After crushing and drying the cement ingredients, batching, grinding, and calcining, antifreeze is added to the cement clinker, and the parts by weight of each component are: 31 parts of limestone, 45 parts of carbide slag, and 0.6 part of iron raw material , 6 parts of clay, 6 parts of fly ash, 0.6 parts of cement reinforcing agent, 0.4 parts of antifreeze, 6 parts of gypsum, 2 parts of short-wave fiber, 1 part of modifier, and 2 parts of corrosion-resistant components.
Embodiment 3
[0017] After crushing and drying the cement ingredients, batching, grinding, and calcining, antifreeze is added to the cement clinker. The parts by weight of each component are: 32 parts of limestone, 48 parts of carbide slag, and 1 part of iron raw material , 7 parts of clay, 7 parts of fly ash, 0.7 parts of cement reinforcing agent, 0.5 parts of antifreeze, 6 parts of gypsum, 3 parts of short-wave fiber, 1 part of modifier, and 2 parts of corrosion-resistant components.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
compressive strength
aaaaa
aaaaa
flexural strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses calcium carbide slag cement. The cement is composed of following raw materials in parts by weight: 30 to 35 parts of limestone, 40 to 65 parts of calcium carbide slag, 0.5 to 5.5 parts of ferruginous raw material, 5 to 10 parts of clay, 5 to 25 parts of fly ash, 0.5 to 1.5 parts of cement reinforcing agent, 0.3 to 0.9 part of anti-freezing agent, 5 to 8 parts of gypsum, 1 to 5 parts of short glass fiber and 1 to 2 parts of modifier. The blending amount of calcium carbide slag is largely increased during the cement preparation process, the mineral resource is saved, the cement production cost is reduced and the discharge of pollutant is reduced. The cement reinforcing agent is added, so the compressive strength of the cement is improved, and the mixed materials are fully utilized. The anti-freezing agent is added, so the anti-freezing performance of the cement is improved, and the cement can satisfy the needs of construction in most areas in winter.
Description
technical field [0001] The invention relates to carbide slag cement, which belongs to the field of cement. Background technique [0002] Cement is one of the important building materials today. It is made of silicate clinker made by mixing limestone, coal, iron powder and clay and other mineral raw materials, and then adding gypsum to the clinker and grinding it. . With the rapid development of my country's economy, the demand for cement has doubled. According to incomplete statistics, the national cement output reached 2.18 billion tons in 2012. At the same time, the research on special cement is also increasing. Chinese patent 200710137472.1 discloses a cement enhancer, which makes full use of industrial waste gas mixture materials, reduces cement costs, saves mineral energy, and improves the ecological environment. Chinese patent 200710055161.0 discloses an antifreeze cement, by adding cement antifreeze components, the cement antifreeze effect is uniform and the antif...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more