Preparation process of silicate reverse osmosis scale inhibitor

A preparation process and reverse osmosis technology, which is applied in the new process field of water medium scale inhibitor, can solve the problems of dangerous operation, high toxicity of hydrofluoric acid, high cost of replacing membrane parts, and achieves low temperature rise, easy control and high tolerance. Effect

Active Publication Date: 2013-11-27
SHANGHAI FUYIN ENVIRONMENTAL PROTECTION TECH CO LTD +1
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of these two treatment methods are that the toxicity of hydrofluoric acid is too high, the operation is dangerous, and the cost of replacing the membrane is too high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of silicate reverse osmosis scale inhibitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation process of a silicate reverse osmosis scale inhibitor, the specific steps are: dissolving 98 kilograms of maleic anhydride in 40 kilograms of water, adding 80 kilograms of 50% sodium hydroxide solution dropwise under stirring, and controlling the reaction temperature to 20 ~50°C to convert maleic anhydride into maleic acid sodium salt; after reacting for 0.5h, heat the reaction system to 50~60°C in a water bath of 60~65°C, and add 127 kg of 30% hydrogen peroxide in five times , every interval of 20 minutes; add 12.19 kg of catalyst vanadium pentoxide, carry out the epoxidation reaction of maleate to generate sodium epoxy succinate, control the reaction temperature at 65-70°C, pH value of 5-7, heat preservation reaction After 1.5 hours, 16 kg of diethylenetriamine was added to carry out the polymerization reaction. The reaction temperature was controlled at 85-90°C and the reaction time was 4 hours to obtain a brownish-red viscous liquid with a solid content...

Embodiment 2

[0022] A kind of preparation technology of silicate reverse osmosis antiscaling agent, concrete steps are: dissolve 196 kilograms of maleic anhydride in 100 kilograms of water, slowly add 165 kilograms of 50% sodium hydroxide solution under the condition of stirring, control reaction temperature 40 ~50°C to convert maleic anhydride into maleic acid sodium salt; after reacting for 0.5h, heat the reaction system to 50~60°C in a water bath of 60~65°C, add 200 kg of 30% hydrogen peroxide in six times , every interval of 20 minutes; add 15.19 kg of catalyst vanadium pentoxide, carry out epoxidation reaction of maleate to generate sodium epoxy succinate, control the reaction temperature at 65-70 ° C, pH value of 5.5-6.0, heat preservation reaction After 1 hour, 19 kg of diethylenetriamine was added to carry out the polymerization reaction, the reaction temperature was controlled at 90-100°C, and the reaction time was 3.5 hours to obtain a brown-red viscous liquid with a solid content...

Embodiment 3

[0024] A kind of preparation technology of silicate reverse osmosis antiscalant, concrete steps are: dissolve 294 kilograms of maleic anhydride in 110 kilograms of water, slowly add 300 kilograms of 40% sodium hydroxide solution under the condition of stirring, control reaction temperature 20 ~30 ℃, maleic anhydride is converted into maleic acid sodium salt; after reacting for 0.5 hours, the reaction system is heated to 55~60 ℃ in a water bath of 60~65 ℃, and 320 kg of 30% hydrogen peroxide is added in seven times, Each interval is 20 minutes; add 18.9 kg of catalyst vanadium pentoxide to carry out epoxidation reaction of maleate to generate sodium epoxy succinate, control the reaction temperature at 65-70°C, pH value at 5.5-6.0, and keep warm for 1 hour Finally, add 12 kg of diethylenetriamine to carry out the polymerization reaction, control the reaction temperature to 90-95°C, and the reaction time is 3 hours to obtain a brownish-red viscous liquid with a solid content of no...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation process of a silicate reverse osmosis scale inhibitor, which is characterized by comprising the following steps: maleic anhydride is dissolved into water, under a stirring condition, caustic soda solution is added, and the reaction temperature is controlled to be 20 to 50 DEG C; a reaction system is heated to be 50 to 60 DEG C, oxydol and vanadic oxide are added, the reaction temperature is controlled to be 60 to 70DEG C, and the pH value is 5 to 7; diethylene triamine is added, polymerization reaction is performed, the reaction temperature is controlled to be 80 to 100 DEG C, the reaction time is 3 to 5 h, and maroon grume with solid content which is not lower than 30 percent can be obtained, namely amino disodium polyepoxysuccinicate solution is obtained and can be used as the silicate reverse osmosis scale inhibitor. According to the invention, diethylene triamine is taken as a polymerization initiator for disodium polyepoxysuccinicate, troubles caused by aftertreatment when calcium hydroxide is used as an initiator are avoided, diethylenetriamine is also inserted into the molecular structure of the polyepoxysuccinic acid sodium, and the scale inhibitor is endowed with a novel function of resisting silicate scale.

Description

technical field [0001] The invention relates to a preparation process of a reverse osmosis membrane scale inhibitor with scale inhibition ability for silicate, which is applied to reverse osmosis (RO) systems, nanofiltration (NF) and nanofiltration (NF) of deionized water, pure water and ultrafiltration water. In the ultrafiltration (UF) system, it can prevent silicate scaling on the membrane surface and have good scale inhibition effect on carbonate, sulfate, iron oxide and aluminum salt, which belongs to the new technology field of water medium scale inhibitor. Background technique [0002] There are many types of reverse osmosis membrane antiscalants in the market. At present, foreign brands are still the main ones in China, and most of the domestically developed reverse osmosis agents are imitations, lacking independent research and development capabilities. The ingredients of the agents are mainly concentrated in organic phosphines and polycarboxylic acids. . Compared ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C02F5/12
Inventor 刘坤张入心夷坤许桓
Owner SHANGHAI FUYIN ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com