Surface sizing agent emulsion and preparation method for same
A technology of surface sizing agent and emulsion, applied in the direction of adding water repellent, inorganic compound, non-polymer organic compound, etc., can solve the problem of large amount of sizing agent, and achieve the effect of improving hydrophobicity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1
[0037] Synthesis of cationic polymer:
[0038] a) Dissolve 0.3g potassium persulfate in 10g deionized water to form an aqueous initiator solution for use;
[0039] b) Add 100g of chitosan and 300g of deionized water into a 1000ml four-necked flask, dissolve, and raise the temperature to 60°C;
[0040] c) At 60°C, add 1g of hydrogen peroxide to a four-necked flask and keep it at 60°C for 1 hour; adjust the pH to 10.2 with 3g of sodium hydroxide.
[0041] d) Raise the temperature to 70°C again, quickly add 10g of 3-chloro-2-hydroxypropyltrimethylammonium chloride into a four-necked flask, keep at 70°C for 2 hours; neutralize with 1g of acetic acid to pH=3.05, then drop Add 0.5g of vinyl triisopropoxysilane and initiator solution, drip for 5 minutes, keep at 70℃ for 0.5 hour, add 0.5g of sodium methylene dinaphthalene sulfonate, keep at 70℃ for 0.5 hour, add 30.9g Deionized water was cooled to 25°C and filtered to obtain a cationic polymer: solid content by weight of 2...
Example Embodiment
[0046] Example 2
[0047] Synthesis of cationic polymer:
[0048] a) Dissolve 3 g of sodium persulfate in 10 g of deionized water to form an aqueous initiator solution. spare;
[0049] b) Add 100g of chitosan and 300g of deionized water into a 1000ml four-necked flask, dissolve, and raise the temperature to 70°C;
[0050] c) At 70°C, add 5g of hydrogen peroxide to a four-necked flask and keep it at 70°C for 3 hours; adjust the pH to 12.93 with 10g of sodium hydroxide.
[0051] d) Raise the temperature to 90℃ again, quickly add 30g of 2,3-epoxypropyltrimethylammonium chloride into a four-necked flask, keep at 90℃ for 5 hours; neutralize with 3g of acetic acid to pH=4.85, then add dropwise 5g γ-methacryloxypropyltrimethoxysilane and initiator solution, dripping time 15 minutes, keep at 90℃ for 1 hour, add 1g sodium methylene dimethanesulfonate, keep at 90℃ for 1 hour, Add 278g of deionized water, cool to 25°C and filter to obtain a cationic polymer: solid content by weight of 20.4wt%, ...
Example Embodiment
[0056] Example 3
[0057] Synthesis of cationic polymer:
[0058] a) Dissolve 2 g of ammonium persulfate in 10 g of deionized water to form an aqueous initiator solution. spare;
[0059] b) Add 100g of chitosan and 300g of deionized water into a 1000ml four-necked flask, dissolve, and raise the temperature to 65°C;
[0060] c) At 65°C, add 3g of hydrogen peroxide to a four-necked flask and keep it at 65°C for 2 hours; adjust pH=11.60 with 6g of sodium hydroxide.
[0061] d) Raise the temperature to 80℃ again, quickly add 20g 3-chloro-2-hydroxypropyltrimethylammonium chloride into a four-necked flask, keep at 80℃ for 3 hours; neutralize with 2g acetic acid to pH=4.08, and then drop Add 3g of vinyltriethoxysilane and initiator solution, drip for 10 minutes, keep at 80℃ for 0.8 hours, add 0.7g of sodium methylene dimethynaphthalene sulfonate, keep at 80℃ for 0.8 hours, add 138.5g to The ionized water was cooled to 25°C and filtered to obtain a cationic polymer: the weight solid content ...
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Weight average molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap