Method for preparing large number of carbon quantum dot biology imaging agents

A technology for carbon quantum dots and biological imaging, applied in the field of preparation methods and imaging agents prepared by this method, can solve the problems of difficulty in functionalization, low quantum yield of carbon dots, limited application prospects, etc. Low cytotoxicity, high yield effect

Inactive Publication Date: 2014-01-01
LANZHOU UNIVERSITY
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after investigating various methods, we found a commonality. After these carbon dots are prepared, a surface passivation process is required. The quantum yield of carbon dots without this step of passivation is very low (1 %about)
However, the reagents used for passivation of carbon dots are often polymer-based, and it is more difficult for the carbon dots passivated by polymers to be modified in the next step to make them functional.
This will limit its broad application prospects
And partly limit the mass production of carbon quantum dots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing large number of carbon quantum dot biology imaging agents
  • Method for preparing large number of carbon quantum dot biology imaging agents
  • Method for preparing large number of carbon quantum dot biology imaging agents

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] a Mix 4 mL (about 21% of the total volume) 3-aminotriethoxysilane with 15 mL glycerol;

[0030] b Put the precursor into a polytetrafluoroethylene reactor, purge with argon for 10 min, and seal it under the protection of argon;

[0031] c Heating the precursor to 200°C, reacting under the protection of an inert atmosphere for 30 min, and then cooling to room temperature to obtain a transparent, yellow liquid carbon quantum dot bioimaging agent.

[0032] reaction products see figure 1 , under the excitation of a 365 nm LED light source, the carbon quantum dot bioimaging agent of the present invention can emit strong blue fluorescence, and its absolute quantum yield is measured to be 35.4%. Therefore, its excellent fluorescence properties can be used for bioimaging agents.

Embodiment 2

[0034] a Mix 0.15 mL (about 1% of the total volume) 3-aminotriethoxysilane with 15 mL glycerol;

[0035] b Put the precursor into a polytetrafluoroethylene reactor, purge with argon for 10 min, and seal it under the protection of argon;

[0036] c. Heating the precursor to 200°C, reacting for 30 min and then cooling to room temperature, the obtained transparent and yellow liquid is a carbon quantum dot bioimaging agent.

Embodiment 3

[0038] a Mix 15 mL (about 99% of the total volume) 3-aminotriethoxysilane with 0.15 mL glycerol;

[0039] b Put the precursor into a polytetrafluoroethylene reactor, purge with argon for 10 min, and seal it under the protection of argon;

[0040] c Heating the precursor to 200°C, reacting for 30 min and then cooling to room temperature, the obtained transparent and yellow liquid is a carbon quantum dot bioimaging agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a large number of carbon quantum dot biology imaging agents and carbon quantum dot biology imaging agents. The method provided by the invention comprises the followings: glycerol with the mass ratio of 1 to 99 percent and a silane coupling agent with the mass ratio of 99 percent to 1 percent are mixed for serving as a presoma, and under inert gas protection, full reaction is performed at the temperature of 160 DEG C to 270 DEG C so as to obtain the carbon quantum dot biology imaging agent. The method provided by the invention has the advantages that the yield of the carbon quantum dot biology imaging agent prepared is high, and under different excitation wavelengths, different colors of fluorescent light can be stimulated; during the preparing process, processes of product surface passivation, surface decoration and the like can be accomplished in one step; a thin-film device can be prepared; the carbon quantum dot biology imaging agent is low in cytotoxicity, can be dissolved in water or an organic solvent easily, and can be used in the fields of cell imaging, or living imaging and the like; the imaging agent has the advantages of photobleaching resistance and the like.

Description

technical field [0001] The invention relates to a preparation method of a biological imaging agent and the imaging agent prepared by the method, in particular to a preparation method of a carbon quantum dot biological imaging agent and the carbon quantum dot biological imaging agent. Background technique [0002] Fluorescent materials are widely used in biological imaging and other fields. Such materials generally include: fluorescent dyes, quantum dots, and noble metal nanoclusters. However, the current fluorescent materials still have various limitations in the application of biological imaging. For example, fluorescent dyes were first used in imaging and other fields, but they faced problems such as photobleaching and photodegradation. The birth of various quantum dots seems to have solved this problem. However, many quantum dots are difficult to be widely used in the field of biological imaging due to the complicated synthesis steps and the preparation products are hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/02B82Y30/00C08L29/04C08K3/04C08J5/18G01N21/64A61K49/00C01B32/15
Inventor 王强黄一凡周鑫
Owner LANZHOU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com