Styrene-ethylene-butadiene-styrene (SEBS) thermoplastic elastomer bra lining material as well as preparation method and application thereof

A thermoplastic elastomer and cushion material technology, applied in bras, applications, clothing, etc., can solve the problems of anti-oxidation, poor anti-allergic, easy to cause allergic reactions, easy to age, etc., and achieve economic and social benefits that are not easily soaked in water Significant, easy-to-operate effects

Inactive Publication Date: 2014-01-22
WUHAN INSTITUTE OF TECHNOLOGY
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, most of the pads are some plastic foam materials, which have the disadvantages of being difficult to wash, easy to age, and difficult to dry after washing; Adding chemical foaming agents and foaming aids, some people are prone to allergic reactions when exposed to such substances
In r

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Styrene-ethylene-butadiene-styrene (SEBS) thermoplastic elastomer bra lining material as well as preparation method and application thereof
  • Styrene-ethylene-butadiene-styrene (SEBS) thermoplastic elastomer bra lining material as well as preparation method and application thereof
  • Styrene-ethylene-butadiene-styrene (SEBS) thermoplastic elastomer bra lining material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1) Mixing material: According to the ratio of parts by mass, add 100 parts of powdery high molecular weight (about 220,000) SEBS elastomer into a high-speed mixer and stir for 5 minutes, then add 400 parts of naphthenic rubber oil, and stir for another 20 minutes , to obtain oil-extended SEBS elastomer. Add 0.5 parts of alkyl polyphenol antioxidant 1010, 0.5 part of phosphite antioxidant 168, 1 part of polyethylene wax, and 50 parts of talc powder (1250 mesh) to the oil-extended SEBS elastomer, at high speed Blend for 15 minutes;

[0022] 2) Pelletizing: Put the uniformly mixed material into a twin-screw extruder to extrude and granulate. The process conditions for granulation are 150-155°C in the feeding section, 165-170°C in the melting and compression section, and 165-170°C in the homogenizing section. 170-175°C, the die temperature is 170°C, the screw speed is 250-350 rpm;

[0023] 3) Injection: Add the prepared pellets to the injection machine for injection moldi...

Embodiment 2

[0027] 1) Mixing material: Add 100 parts of powdered low molecular weight (about 70,000) SEBS elastomer into a high-speed mixer and stir for 5 minutes, then add 100 parts of naphthenic rubber oil and 100 parts of paraffin base rubber oil, and then stirred for 20 minutes to obtain an oil-extended SEBS elastomer. 15 parts of EVA resin, 0.5 part of maleic anhydride grafted SEBS, 0.5 part of alkyl polyphenol antioxidant 1010, 0.5 part of alkyl polyphenol antioxidant DLTP, 1 part of zinc stearate, 35 parts of talcum powder (1250 mesh) added to the oil-extended SEBS elastomer, and stirred for 15 minutes in a high-speed mixer;

[0028] 2) Pelletizing: Put the uniformly mixed material into a twin-screw extruder to extrude and granulate. The process conditions for granulation are 150-155°C in the feeding section, 170-175°C in the melting and compression section, and 170-175°C in the homogenizing section. 175-180°C, the die temperature is 175°C, the screw speed is 250-350 rpm;

[0029...

Embodiment 3

[0031] 1) Mixing material: Add 50 parts of powdery high molecular weight (about 220,000) SEBS elastomer and 50 parts of low molecular weight (about 70,000) SEBS elastomer into a high-speed mixer and stir for 5 minutes before adding 250 parts of paraffin-based rubber oil were stirred for another 20 minutes to obtain an oil-extended SEBS elastomer. Add 0.5 part of alkyl polyphenol antioxidant 1010, 0.5 part of antioxidant phosphite 168, 0.5 part of colorant, 1 part of calcium stearate, 30 parts of light calcium carbonate (800 mesh) to the oil-extended Type SEBS elastomer, stir for 15 minutes in a high-speed mixer;

[0032] 2) Pelletizing: Put the uniformly mixed material into a twin-screw extruder to extrude and granulate. The process conditions for granulation are 150-155°C in the feeding section, 165-170°C in the melting and compression section, and 165-170°C in the homogenizing section. 170-175°C, the die temperature is 170°C, the screw speed is 250-350 rpm;

[0033] 3) Inj...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a bra backing material and a preparation method of the bra lining material. The preparation method comprises the steps of: 1) adding a powder-shaped styrene-ethylene-butadiene-styrene (SEBS) thermoplastic elastomer into a high-speed mixing machine, stirring, adding mineral oil with regulated parts and stirring again to obtain an oil-charging type SEBS elastomer; 2) adding antioxygen, lubricating agents, coloring agents and filling agents into the oil-charging type SEBS elastomer obtained in the step 1), uniformly stirring the mixture in the high-speed mixing machine and adding an ethylene-vinyl acetate copolymer and a compatilizer to be mixed; 3) extruding and pelletizing the mixture obtained in the step 2) in a double-screw extruder. The bra lining material has the beneficial effects that the lining material has the characteristics of anti-aging, low cost, low hardness, high elasticity, high flexibility and comfortable handfeel, and is difficult to soak and convenient to clean; through an injection process, the bra liner is conveniently and directly molded; moreover, pouring materials can be recycled, so that the liner is simple in process, low in energy consumption, high in efficiency, high in repeatability and easy to operate.

Description

technical field [0001] The invention belongs to the field of macromolecular materials, and in particular relates to a bra pad material and a preparation method thereof, in particular to a SEBS thermoplastic elastomer bra pad material, a preparation method and use thereof. Background technique [0002] Bras can modify and protect women's breast deformities, and can make women's breast lines more beautiful. Bras generally require padding to be added to the cups during use. In the prior art, most of the pads are some plastic foam materials, which have the disadvantages of being difficult to wash, easy to age, and difficult to dry after washing; Adding chemical foaming agents and foaming aids, some people are prone to allergic reactions when exposed to such substances. In recent years, there has also been a type of silicone rubber bra pad made of silicone rubber, but because this type of silicone rubber bra pad is a product that has not been hydrogenated and saturated during t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/02C08L23/08C08L91/00A41C3/14
Inventor 刘仿军李亮陈金芳彭林峰
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap