High-temperature wire drawing lubricant and preparation method thereof

A lubricant and wire drawing technology, applied in the field of high temperature wire drawing lubricant and its preparation, can solve the problems of oil product evaporation and smoke, on-site environment deterioration, slow heat dissipation of lubricating oil, etc., to solve high temperature failure, protect the environment, promote cooling effect

Inactive Publication Date: 2014-03-05
全威(铜陵)铜业科技有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat dissipation of the lubricating oil is slow, which will damage the mold and affect the product quality. At the same time, th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] specific implementation plan

[0012] The present invention will be described in detail below through specific examples.

[0013] A high-temperature wire drawing lubricant and a preparation method thereof, which are made of the following raw materials in parts by weight (kg): sodium dodecylbenzenesulfonate 2, boric acid 1, triethanolamine borate 2, ricinoleic acid polyester 1, Castor oil 12, fatty alcohol polyoxyethylene ether 1, ethylene glycol 10, citric acid 1, oleic acid triethanolamine soap 1, antiwear agent 10, water 1000;

[0014] The anti-wear agent is made of the following raw materials in parts by weight (kg): diatomite 2.4, jade 1.2, urotropine 2.0, urea 0.4, silane coupling agent KH-550 1.0, dodecylbenzenesulfonic acid Sodium 0.1, ascorbic acid 1, sulfur powder 1, nano-aluminum nitride powder 1.2, water 60; the preparation method is to put jade and diatomaceous earth into a calcination furnace at 540-570 ℃, calcinate for 2-3 hours, cool, pulverize and put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-temperature wire drawing lubricant and a preparation method thereof. The lubricant and the preparation method are characterized in that: the lubricant is prepared from following raw materials by weight: 2-3 parts of sodium dodecyl benzene sulfonate, 1-2 parts of boric acid, 2-3 parts of triethanolamine borate, 1-2 parts of ricinoleic acid polyester, 12-15 parts of ricinus oil, 1-2 parts of a polyoxyethylene alkyl ether, 10-12 parts of glycol, 1-2 parts of citric acid, 1-2 parts of triethanolamine oleate soap, 10-14 parts of an antiwear agent and 1000 parts of water; nano aluminium nitride powder is added into the antiwear agent, thus promoting heat dissipation so that cooling effects are good, enhancing the film-forming property and prolonging the service lifetime of a wire drawing die; the lubricant can resolve issues of extreme-pressure wear resistance, resistance to high-temperature oxidation, surface rust protection, and the like of metal wires at high-temperature environments; the method is simple and the cost is reduced; problems of failure at high temperature, etc. of conventional lubricants are solved; and the lubricant is suitable for wire drawing processes of various metals and alloys.

Description

technical field [0001] The invention relates to the field of metal processing, in particular to a high-temperature wire drawing lubricant and a preparation method thereof. Background technique [0002] Metal wire drawing is a manufacturing process in which the aluminum plate is repeatedly scraped out with sandpaper. The main process of the process is divided into three parts: deesterification, sand mill, and water washing. In the wire drawing process, the special film technology after anodizing can make the metal surface generate a film layer containing the metal component, clearly showing every tiny silk trace, so that fine hair strands appear in the metal matte luster. In recent years, more and more metal shells of products have used metal wire drawing process to play the role of beauty and corrosion resistance. Make the product have both fashion and technology elements. This is one of the reasons why the craft is so popular. [0003] In metal pressure processing. Unde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/00C10M125/20C10N30/06C10N40/24C10N30/12C10N30/08
Inventor 王文金
Owner 全威(铜陵)铜业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap