A kind of preparation method of oil-water separation material

A technology of oil-water separation and hydrazine hydrate steam, applied in the field of nanomaterials, can solve problems such as poor mechanical strength and high energy consumption

Active Publication Date: 2016-06-08
UNIV OF SCI & TECH OF CHINA
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

German "Advanced Functional Materials" (Advanced Functional Materials, 2012, Issue 22, page 4421) reported a three-dimensional sponge-like graphite material prepared by reducing graphene oxide. First, graphene oxide was prepared by Hummers method, and then reduced to reduced Graphene oxide, and then freeze-dried to obtain spongy graphene. The graphene nanosheets are relatively large, but their mechanical strength is poor. When recycling, heat treatment is required to remove the adsorbed oil, which consumes a lot of energy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of oil-water separation material
  • A kind of preparation method of oil-water separation material
  • A kind of preparation method of oil-water separation material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The embodiment of the present invention discloses a preparation method of an oil-water separation material, comprising the following steps:

[0029] Soaking the sponge material in the graphene oxide solution, taking out the obtained sponge material and centrifuging to obtain the graphene oxide-coated sponge material;

[0030] The graphene oxide-coated sponge material is subjected to a reduction reaction under the action of a reducing agent to obtain an oil-water separation material.

[0031] The invention obtains the graphene oxide-coated sponge material by soaking, dipping, and centrifuging; then, under the action of a reducing agent, the graphene oxide-coated sponge material is reduced to obtain an oil-water separation material, that is, a reduced graphene oxide-coated sponge material. Cover with sponge.

[0032] According to the present invention, the graphene oxide is preferably prepared according to the following method:

[0033] Mix graphite flakes, sodium nitra...

Embodiment 1

[0045] Weigh 5.00g of graphite flakes and 3.75g of NaNO 3 In a 1L beaker, slowly add 150mL of concentrated sulfuric acid, and mechanically stir for 0.5h. Slowly add 20gKMnO in 0.5h 4 , After continuing to stir for 20h, stop stirring. A purplish red solution with a small amount of flakes was obtained. The solution was allowed to stand for 5 days with occasional manual stirring. Slowly add 500mL deionized water, then slowly add 30mLH 2 o 2 , to obtain a reaction solution containing graphene oxide.

[0046] The reaction solution was centrifuged at 10,000 rpm for 10 min, the supernatant was poured off, washed and centrifuged with deionized water repeatedly for 4 times, and a graphene oxide solid product was obtained.

[0047] Disperse the graphene oxide solid in deionized water, centrifuge at 6000rpm for 10min, collect the supernatant, add water to disperse the lower precipitate and centrifuge again (centrifuge at 6000rpm for 10min), and collect the supernatant again. Repea...

Embodiment 2

[0051] Cut the polymer sponge into cube samples of 2cm*2cm*2cm size, wash and dry, soak in 10mL0.2mg / mL graphene oxide solution, take it out and centrifuge at 1000rpm for 5 minutes to obtain the oxidized Graphene coated sponge;

[0052] The graphene oxide-coated sponge sample block was soaked in 50 mL of hydriodic acid aqueous solution with a mass concentration of 30%, and heated to 85° C. for reduction to obtain a reduced graphene oxide-coated sponge;

[0053] The reduced graphene oxide-coated sponge is cleaned and dried to obtain a redox graphene-based sponge.

[0054] Field emission scanning electron microscope observation is carried out to described polymer sponge and reduced graphene oxide coated sponge, the results can be found in figure 2 and image 3 , figure 2 and image 3 The scanning electron micrographs of the polymer sponge and the reduced graphene oxide coated sponge provided by Example 2 of the present invention are obtained by figure 2 and image 3 It ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of an oil-water separation material, comprising the following steps: soaking a sponge material in a graphene oxide solution, taking out the obtained sponge material and centrifuging to obtain a graphene oxide-coated sponge material; The graphene-coated sponge material undergoes a reduction reaction under the action of a reducing agent to obtain an oil-water separation material. The oil-water separation material prepared by the present invention is the reduced graphene oxide coated sponge, the graphene layer is evenly coated, tightly coated, has good resilience and mechanical stability, and the reduced graphene oxide layer provides good hydrophobicity and lipophilicity , can be used in oil-water separation technology.

Description

technical field [0001] The invention relates to the technical field of nanomaterials, in particular to a preparation method of an oil-water separation material. Background technique [0002] The oil-water separation material is a material that uses the selective separation of materials to realize the separation, purification and concentration of organic and inorganic components of the feed liquid. It has the advantages of high efficiency, energy saving, environmental protection, simple separation process, and recyclable utilization. It is widely used In food, medicine, environmental protection, chemical industry, metallurgy, energy, petroleum and water treatment and other fields. [0003] The separation effect of the oil-water separation material depends on the properties of the material itself. Among them, superhydrophobic three-dimensional porous nanomaterials have a good oil-water separation effect due to their light weight, porosity, and large specific surface area, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B31/04B01D17/022C01B32/184
Inventor 俞书宏叶荫东
Owner UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com