A technology for epoxy resin paint and wind power blades, applied in the field of paint, can solve the problems of blade life influence, coating corrosion, affecting blade surface quality, etc., and achieves good salt spray corrosion resistance, high adhesion, and good compatibility. Effect

Active Publication Date: 2015-12-09
南通市通州区五接农业机电管理站有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the sea is different from the land, there are more salt spray in the air, which will seriously affect the quality of the blade surface, first of all, the coating will be corroded, and the life of the blade will be affected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of special epoxy resin paint for wind power blades resistant to salt spray

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The first step, take epoxy resin 30Kg, acrylic resin 5Kg, amino resin 5Kg, rosin modified maleic acid resin 2Kg, polystyrene emulsion 2Kg, dimethylol propionic acid 1Kg, methyl methacrylate 2Kg, tert-butyl Base perbenzoate 1Kg, polyethylene wax 4Kg, alcohol-containing nitrocellulose 4Kg, butyl acetate 50Kg, ethylene glycol butyl ether 4Kg, mix homogeneously in mixer, and stirring speed is 800 rev / mins;

[0022] Step 2, add 3Kg of thickener and 4Kg of dispersant, mix evenly in the mixer, and the stirring speed is 1000 rpm;

[0023] Step 3: Add 2Kg of nonionic surfactant, 10Kg of pigment, and 15Kg of filler, mix evenly in a mixer at a stirring speed of 1000 rpm, grind to a fineness of less than 20 μm, and pack.

[0024] Described epoxy resin refers to epoxy resin E-44, and described amino resin refers to amino resin DM-225, and described thickener is polyurethane thickener, and described dispersant is lauryl Trimethyl ammonium chloride, described nonionic surfactant is T...

Embodiment 2

[0026] Step 1, take 50Kg of epoxy resin, 10Kg of acrylic resin, 10Kg of amino resin, 4Kg of rosin modified maleic acid resin, 4Kg of polystyrene emulsion, 3Kg of dimethylol propionic acid, 4Kg of methyl methacrylate, tert-butyl Base perbenzoate 3Kg, polyethylene wax 6Kg, alcohol-containing nitrocellulose 7Kg, butyl acetate 70Kg, ethylene glycol butyl ether 6Kg, mix homogeneously in mixer, and stirring speed is 1000 rev / mins;

[0027] Step 2, add 6Kg of thickener and 7Kg of dispersant, mix evenly in the mixer, and the stirring speed is 1200 rpm;

[0028] Step 3: Add 5Kg of nonionic surfactant, 20Kg of pigment, and 30Kg of filler, mix evenly in a mixer at a stirring speed of 1200 rpm, grind to a fineness of less than 20 μm, and pack.

[0029] Described epoxy resin refers to epoxy resin E-44, and described amino resin refers to amino resin DM-225, and described thickener is polyurethane thickener, and described dispersant is lauryl Sodium sulfate, described nonionic surfactant i...

Embodiment 3

[0031] Step 1, take 40Kg of epoxy resin, 6Kg of acrylic resin, 7Kg of amino resin, 3Kg of rosin modified maleic acid resin, 3Kg of polystyrene emulsion, 2Kg of dimethylol propionic acid, 3Kg of methyl methacrylate, tert-butyl Base perbenzoate 2Kg, polyethylene wax 5Kg, alcohol-containing nitrocellulose 6Kg, butyl acetate 60Kg, ethylene glycol butyl ether 5Kg, mix homogeneously in mixer, and stirring speed is 900 rev / mins;

[0032] Step 2, add 5Kg of thickener and 6Kg of dispersant, mix evenly in the mixer, and the stirring speed is 1100 rpm;

[0033] Step 3: Add 4Kg of nonionic surfactant, 15Kg of pigment, and 20Kg of filler, mix evenly in a mixer at a stirring speed of 1100 rpm, grind to a fineness of less than 20 μm, and pack.

[0034] Described epoxy resin refers to epoxy resin E-44, and described amino resin refers to amino resin DM-225, and described thickener is polyurethane thickener, and described dispersant is lauryl Sodium sulfate, described nonionic surfactant is T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a special salt spray resistance epoxy resin paint for a wind power blade and belongs to the technical field of coatings. The preparation method comprises the following steps: taking epoxy resin, acrylic resin, amino resin, rosin modified maleic acid resin, polystyrene latex, dimethylolpropionic acid, methyl methacrylate, tert-butyl perbenzoate, polyethylene wax, alcohol nitrocotton, butyl acetate and ethylene glycol butyl ether for uniformly mixing in a mixer; then adding a thickener and a dispersant and uniformly mixing in the mixer;adding a nonionic surfactant, a pigment and packing, uniformly mixing in the mixer, grinding to the fineness of below 20mum and packaging. The epoxy resin paint provided by the invention has good compatibility to the wind power blade made of an epoxy resin material, has a high adhesive force which can reach 1 grade, has good salt spray corrosion resistance and is suitable for coating the marine wind power blade.

Description

technical field [0001] The invention relates to a preparation method of epoxy resin paint, in particular to an epoxy resin paint with salt spray resistance for wind power blades, which belongs to the technical field of coatings. Background technique [0002] As we all know, due to the pressure of environmental protection and the impact of global climate change, countries around the world are vigorously developing renewable energy. Wind power has developed rapidly in recent years. According to the statistics of installed capacity of wind power in the world by Danish BTM Consulting Company: 28GW (28.19 million kW) was newly added in 2008, accumulatively exceeding 122GW (about 120 million kW). In 2009, 38GW (38.1 million kW) was newly added, and the cumulative total exceeded 160GW (about 160 million kW). Due to the limited land in Europe and the United Kingdom, it is difficult to develop large-scale wind power on land. They chose to develop offshore and carried out technical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/08C09D7/12
Inventor 袁宏亮
Owner 南通市通州区五接农业机电管理站有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap