Method for nickeling carbon fiber/cyanate ester resin composite material

A cyanate resin and composite material technology, which is applied in metal material coating process, liquid chemical plating, superimposed layer plating, etc. The effect of low production cost

Inactive Publication Date: 2014-03-26
XIAN UNIV OF TECH
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this invention is to provide a kind of method of nickel plating of carbon fiber / cyanate resin composite material, which solves the problems of missing plating and too thin coating when the surface of carbon fiber / cyanate resin composite material is nickel-plated in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for nickeling carbon fiber/cyanate ester resin composite material
  • Method for nickeling carbon fiber/cyanate ester resin composite material
  • Method for nickeling carbon fiber/cyanate ester resin composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Using 25mm×25mm×5mm carbon fiber / cyanate resin composite plate; the plating area is 0.175dm 2 , the loading of the plating solution refers to the ratio of the plating area of ​​the workpiece to the volume of the plating solution, and the loading of the plating solution is 0.5dm 2 / L to calculate the required volume of electroless plating solution and electroplating solution are 350mL.

[0043] Step 1, pre-processing,

[0044] a. Degreasing: Soak the carbon fiber / cyanate resin composite material in 350mL acetone, take it out after ultrasonication for 20min, wash it with distilled water, and dry it;

[0045] b. Coarsening: Soak the material obtained in step a in 350mL of 35% nitric acid, heat it in a water bath to 40°C, keep it warm for 20min, wash it with distilled water, and dry it;

[0046] c. Sensitization: Dissolve 5.25g of stannous chloride in 14mL of concentrated hydrochloric acid, add 7g of tin particles, dilute to 350mL with distilled water to obtain a sensitiz...

Embodiment 2

[0057] Carbon fiber / cyanate resin composite plate with diameter d=130mm and thickness t=5mm is used; the plating area is 2.86dm 2 , the loading of the plating solution refers to the ratio of the plating area of ​​the workpiece to the volume of the plating solution, according to the loading of the plating solution is 1.43dm 2 / L calculates that the volumes of both the electroless plating solution and the electroplating solution are 2L.

[0058] Step 1, pre-processing,

[0059] a. Degreasing: Soak the carbon fiber / cyanate resin composite material in 2L of acetone, take it out after ultrasonication for 15min, wash it with distilled water, and dry it;

[0060] b. Coarsening: Soak the material obtained in step a in 2L of 35% nitric acid, heat it in a water bath to 40°C, keep it warm for 15 minutes, wash it with distilled water, and dry it;

[0061] c. Sensitization: Dissolve 30g of stannous chloride in 80mL of concentrated hydrochloric acid, add 30g of tin particles, dilute to 2L...

Embodiment 3

[0071] Use 20mm×20mm×5mm carbon fiber / cyanate resin composite plate; the plating area is 0.12dm 2 , the loading of the plating solution refers to the ratio of the plating area of ​​the workpiece to the volume of the plating solution, according to the loading of the plating solution is 1.2dm 2 / L to calculate the required volume of electroplating solution and electroplating solution are 100mL.

[0072] Step 1, pre-processing,

[0073] a. Degreasing: Soak the carbon fiber / cyanate resin composite material in 100mL of acetone, take it out after ultrasonication for 10min, wash it with distilled water, and dry it;

[0074] b. Coarsening: Soak the material obtained in step a in 100mL of 35% nitric acid, heat it in a water bath to 40°C, keep it warm for 18min, wash it with distilled water, and dry it;

[0075] c. Sensitization: Dissolve 1.5g of stannous chloride in 4mL of concentrated hydrochloric acid, add 1.8g of tin particles, dilute to 100mL with distilled water to obtain a sens...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for nickeling a carbon fiber/cyanate ester resin composite material. The method comprises the following steps: pre-nickeling the surface of a pretreated carbon fiber/cyanate ester resin composite material through a chemical plating method, and then, nickeling by using an electroplating method. According to the method, chemical plating is combined with electroplating, the pre-nickeling procedure is carried out by the chemical plating method firstly to form a uniform conductive layer on the material surface, and then, the nickel layer is thickened by the electroplating method to both ensure the uniformity of the nickeling layer and ensure enough thickness for the nickeling layer, the problems of plating leakage and too thin plating layer when nickeling the surface of the carbon fiber/cyanate ester resin composite material in the prior art are solved, uniform and thick enough plating layer is obtained, the plating layer is uniform, integral, free of plating leakage phenomenon, good in binding force with a base material, free of gap and capable of meeting the application conditions of a space optical mirror, and the electroplating and chemical plating production costs are low, so that volume production can be realized.

Description

technical field [0001] The invention belongs to the technical field of surface treatment of non-metallic materials, and in particular relates to a nickel-plating method for a carbon fiber / cyanate resin composite material. Background technique [0002] Remote sensing is the main means to realize the detection of military targets, and the level of remote sensing cameras determines the modernization level of a country's national defense. Since the 1980s, remote sensing cameras have been competing to develop among countries all over the world. The most representative ones are the US SPOT5 (2001, 2.5-meter resolution), IKNOS (1999, 1-meter resolution), KH-12 ( In 2007, 0.1-meter resolution) and other cameras can detect the number of pedestrians and vehicles on the ground and sensitive areas, greatly improving the level of detail of military intelligence, so large-caliber high-resolution remote sensing cameras are the needs of future military struggles. However, the improvement o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C28/02C23C18/36C23C18/28C23C18/30C25D3/16C25D5/56
Inventor 张云鹏李晓娜林雪张甜甜
Owner XIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap