Resin composition for anti-counterfeit matrix material protective layer and anti-counterfeit matrix material

A technology of resin composition and protective layer, which is applied in the field of resin composition for protective layer of anti-counterfeit type material and anti-counterfeit type material, and can solve the problems of high cost and low work efficiency

Active Publication Date: 2014-04-09
SHENZHEN SECUTEK ANTICOUNTERFEIT MATERIALS
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The protective layer needs to have high hardness and chemical resistance. In order to meet the above requirements, many companies have developed a variety of protective layer compositions: one is the reaction between the resin composition and the curing agent. This protective layer composition can not only be used in It can react quickly at a lower temperature, and it can also react automatically at room temperature. When coating the protective layer, it can be rolled up after passing through the drying tunnel and only when the surface is dry, and then it can be cured at room temperature. effect, but the raw material resin composition of this method is mostly imported raw materials, and the cost is high; the other is the composition in the main resin according to the ratio of the amino resin, because the crosslinking of the amino group can only react quickly at high temperature, and the work Low efficiency and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition for anti-counterfeit matrix material protective layer and anti-counterfeit matrix material
  • Resin composition for anti-counterfeit matrix material protective layer and anti-counterfeit matrix material
  • Resin composition for anti-counterfeit matrix material protective layer and anti-counterfeit matrix material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0061] The present invention also provides a method for preparing the resin composition for the protective layer of the anti-counterfeit type material, comprising the following steps: mixing 50-80 parts by weight of acrylic resin, 0.5-3 parts by weight of the first auxiliary agent and 20-50 parts by weight of 1 part of the first organic solvent is mixed and stirred evenly to obtain the main agent; the first auxiliary agent is one or more of wetting agent, leveling agent, coupling agent and drier; 50-80 parts by weight The first cellulose ester type resin is mixed with 30 to 50 parts by weight of the second organic solvent, and stirred evenly to obtain an additive accelerator; the main agent is mixed with the additive accelerator to obtain a resin combination for the protective layer of anti-counterfeit font materials things.

[0062] Wherein, the acrylic resin, the first additive, the first organic solvent, the first cellulose ester resin and the second organic solvent are all...

Embodiment 1

[0098] 1.1 Use polyethylene terephthalate (PET) with a thickness of 25 μm as the surface material; mix 10 parts by weight of cellulose acetate with 70 parts by weight of toluene, stir at a speed of 500 rpm for 50 minutes until completely dissolved, and filter to obtain The paint is coated on the PET surface material, and the pattern layer is obtained after drying.

[0099] 1.2 Add 16.5 parts by weight of butyl acetate and 23 parts by weight of toluene to the reaction kettle, stir, then add 60.5 parts by weight of acrylic resin, continue stirring until uniform, then add 0.1 parts by weight of 1051 coupling agent, 0.1 parts by weight of DBTDL catalyst Stir the dry agent and 0.3 parts by weight of BYK-065 defoamer evenly to obtain the main material of the coating; add 25 parts by weight of butyl acetate and 25 parts by weight of toluene to the reaction kettle, stir, and then add 50 parts by weight of fiber Plain nitroresin, continue to stir until uniform, filter and obtain coatin...

Embodiment 2

[0107] 2.1 Use polyethylene terephthalate (PET) with a thickness of 25 μm as the surface material; mix 10 parts by weight of cellulose acetate with 70 parts by weight of toluene, stir at a speed of 500 rpm for 50 minutes until completely dissolved, and filter to obtain The paint is coated on the PET surface material, and the pattern layer is obtained after drying.

[0108] 2.2 Add 23 parts by weight of butyl acetate and 13 parts by weight of toluene into the reaction kettle, stir, then add 63.5 parts by weight of acrylic resin, continue to stir until uniform, then add 0.1 parts by weight of 1051 coupling agent, 0.1 parts by weight of DBTDL catalyst Stir the dry agent and 0.3 parts by weight of BYK-065 defoamer evenly to obtain the main material of the coating; add 27.8 parts by weight of butyl acetate and 17.8 parts by weight of toluene to the reaction kettle, stir, and then add 54.40 parts by weight of fiber Plain nitroresin, continue to stir until uniform, filter and obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a resin composition for an anti-counterfeit matrix material protective layer and an anti-counterfeit matrix material. The anti-counterfeit matrix material comprises a surface material, a pattern layer, a protective layer, an ink layer, a dielectric layer, an adhesive layer and release paper in sequence, wherein the protective layer is formed by curing the resin composition with an isocyanate curing agent. Compared with the prior art, the resin composition and the anti-counterfeit matrix material have the beneficial effects that the protective layer takes acrylic resin as the main film forming material and the acrylic resin has better physical and mechanical properties, excellent weather resistance, chemical resistance and water resistance and high light and colour retention and has better protective effects on the pattern layer; meanwhile, the cellulose ester resin is added as an additive accelerator; the hydroxyl of the cellulse ester resin and the isocyanate curing undergo an addition polymerization reaction and then a film is formed by curing, so that the resin composition can form the film quickly; and besides, the cellulose ester resin has better hydrophilicity and lipophilicity and can endow the protective layer with better printing adaptability.

Description

technical field [0001] The invention belongs to the technical field of anti-counterfeit materials, and in particular relates to a resin composition for a protective layer of anti-counterfeit type material and an anti-counterfeit type material. Background technique [0002] Counterfeiting has existed since ancient times, so anti-counterfeiting is an ancient topic, as old as human civilization. With the increasing prosperity of the commodity economy and the continuous development of science and technology, anti-counterfeiting has become a new and constantly changing field. [0003] Anti-counterfeiting technology refers to the measures taken to achieve the purpose of anti-counterfeiting. It can accurately identify the authenticity within a certain range and is not easy to be imitated and copied. Simply put, it is a technology to prevent counterfeiting and counterfeiting. It is a preventive technical measure adopted in order to protect the corporate brand, protect the market, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D101/12C09D175/04C09D133/00C08G18/79C08G18/62C08G18/64B32B27/06B32B27/36G09F3/02G09F3/10
Inventor 刘斌钟稳根谭铭
Owner SHENZHEN SECUTEK ANTICOUNTERFEIT MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com