Noise-reducing polyethylene composite material for drainage pipeline of building and preparation method thereof
A technology for building drainage and composite materials, which is applied in the field of polyethylene sound-absorbing composite materials for building drainage pipes and its preparation, can solve the problems of failing to meet environmental protection requirements, and achieve high oxidation induction time, unchanged hydrostatic performance, and mechanical properties Improved effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1:
[0031] (1) Formula: 40 parts by weight of high-density polyethylene, 0.015 parts by weight of dicumyl peroxide, 0.8 parts by weight of vinyl trimethoxysilane, 50 parts by weight of activated nano-scale barium sulfate, activation Treated 1200 mesh barium sulfate 10 parts by weight, polyethylene wax 2 parts by weight, titanium dioxide 4 parts by weight, antioxidant 1010 0.3 parts by weight, antioxidant 168 0.3 parts by weight, and carbon black 2 parts by weight number.
[0032] (2) Preparation process: weigh the above formula and add it to a high-speed mixer, stir at 25°C for 5 minutes, and then discharge the material for later use. Add the mixed material into the extruder for granulation. The process conditions of the extruder:
[0033] The length-to-diameter ratio of the extruder is L / D=44:1, the number of heating sections of the extruder is 12, and the vacuum extraction port is opened in the 9th heating section, and the processing temperature gradually i...
Example Embodiment
[0036] Example 2:
[0037] (1) Formula: 30 parts by weight of high-density polyethylene, weight ratio of 1:1 mixture of di-tert-butane and 1,3-di-tert-butyl dicumyl peroxide, 0.02 parts by weight, dimethyl 0.8 parts by weight of vinyl ethoxysilane, 50 parts by weight of activated nano-scale barium sulfate, 20 parts by weight of activated 1200 mesh barium sulfate, 2 parts by weight of polyethylene wax, 4 parts by weight of titanium dioxide Number, antioxidant 1010 0.3 parts by weight, antioxidant 168 0.3 parts by weight, and carbon black 2 parts by weight.
[0038] (2) Preparation process: weigh the above formula and add it to a high-speed mixer, stir at 25°C for 5 minutes, and then discharge the material for later use. Add the mixed material into the extruder for granulation. The process conditions of the extruder:
[0039] The length-to-diameter ratio of the extruder is L / D=44:1, the number of heating sections of the extruder is 12, and the vacuum extraction port is opened in ...
Example Embodiment
[0040] Example 3:
[0041] (1) Formula: 30 parts by weight of high-density polyethylene, 0.01 parts by weight of 2,5-dimethyl-2,5 bis(tert-butylperoxy)hexyne, methyl vinyl diethoxy silane 0.5 parts by weight, 40 parts by weight of activated nano-barium sulfate, 20 parts by weight of activated 1200 mesh barium sulfate, 2 parts by weight of polyethylene wax, 4 parts by weight of titanium dioxide, 168 parts by weight of antioxidant 0.3 parts by weight, 2 parts by weight of carbon black.
[0042] (2) Preparation process: weigh the above formula and add it to a high-speed mixer, stir at 25°C for 5 minutes, and then discharge the material for later use. Add the mixed material into the extruder for granulation. The process conditions of the extruder:
[0043] The length-to-diameter ratio of the extruder is L / D=44:1, the number of heating sections of the extruder is 12, and the vacuum extraction port is opened in the 9th heating section, and the processing temperature gradually incr...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap