Nano silver decoration laminated board

A technology of nano-silver and decorative stickers, applied in the field of nano-materials, can solve the problems of failing to give full play to the anti-mildew and antibacterial effects of nano-silver, and achieve the effects of convenient storage and transportation, high reactivity, good stability and dispersibility

Active Publication Date: 2014-06-04
DEHUA TB NEW DECORATION MATERIAL CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN200958280Y (2007-10-10) discloses a decorative veneer panel containing nano-silver, but this uses nano-silver sol, which fails to give full play to the anti-mildew and antibacterial effect of nano-silver

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano silver decoration laminated board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Preparation of nano silver:

[0039] The sodium dodecylsulfonate solution is added to the silver nitrate aqueous solution to obtain a mixed solution, and the molar ratio of sodium dodecylsulfonate to silver nitrate is 2:1;

[0040] Heat the mixture to 45°C, add dicyclohexane-18-crown-6 and sodium borohydride to the mixture while stirring, heat to 70°C, and keep stirring for 5 minutes; dicyclohexane-18-crown The molar ratio of -6 to silver nitrate is 1:1; the molar ratio of sodium borohydride to silver nitrate is 0.5:1, and the pH value is controlled to be 8 to obtain nano silver.

[0041] Preparation of nano-silver aqueous solution:

[0042] Dissolve in deionized water with deionized water as solvent, nano silver as solute, acrylic resin as complexing agent and stabilizer in deionized water, then add dispersant and first reducing agent to form a solution;

[0043] The dispersant is triethanolamine, and the mass content in the solution is 1%; the first reducing agent i...

Embodiment 2

[0055] Preparation of nano silver:

[0056] The sodium dodecylsulfonate solution is added to the silver nitrate aqueous solution to obtain a mixed solution, and the molar ratio of sodium dodecylsulfonate to silver nitrate is 3:1;

[0057] Heat the mixture to 55°C, add dicyclohexane-18-crown-6 and potassium borohydride to the mixture while stirring, heat to 85°C, and keep stirring for 8 minutes; dicyclohexane-18-crown The molar ratio of -6 to silver nitrate is 1-2:1; the molar ratio of potassium borohydride to silver nitrate is 0.5-1:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0058] Preparation of nano silver aqueous solution:

[0059] Using deionized water as solvent, nano silver as solute dissolved in deionized water, acrylic resin as complexing agent and stabilizer dissolved in deionized water, then adding dispersant and reducing agent to form a solution;

[0060] The dispersant is triethanolamine, the mass content in the solution is 1-3%; the fir...

Embodiment 3

[0071] Preparation of nano silver:

[0072] The sodium dodecylsulfonate solution is added to the silver nitrate aqueous solution to obtain a mixed solution, and the molar ratio of sodium dodecylsulfonate to silver nitrate is 2.5:1;

[0073] Heat the mixture to 50°C, add dicyclohexane-18-crown-6 and sodium metaphosphate to the mixture while stirring, heat to 75°C, and keep stirring for 6 minutes; dicyclohexane-18-crown The molar ratio of -6 to silver nitrate is 1.5:1; the molar ratio of sodium metaphosphate to silver nitrate is 0.8:1, and the pH value is controlled to be 8.5 to obtain nano silver.

[0074] Preparation of nano silver aqueous solution:

[0075] Using deionized water as solvent, nano silver as solute dissolved in deionized water, acrylic resin as complexing agent and stabilizer dissolved in deionized water, then adding dispersant and reducing agent to form a solution;

[0076] The dispersant is triethanolamine, and the mass content in the solution is 2%; the fir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of nano materials, and particularly relates to a nano silver decoration laminated board. The nano silver decoration laminated board is formed by bonding a decoration single board and a base material by a bonding agent layer; the decoration single board and the base material are formed by impregnating by a nanometer aqueous solution; the bonding agent layer contains a nanometer silver substance; the decoration single board and the base material are engineering wood; the nanometer silver aqueous solution is formed by taking deionized water as a solvent, dissolving nanometer silver as solute into the deionized water, taking acrylic resin as a complexing agent and dissolving a stabilizing agent into the deionized water, and meanwhile adding a dispersion agent and a first reducing agent; the concentration of nanometer silver in the bonding agent is 75-150ppm; the mass content of flour in the solution is 18-45%; environment-friendly glue comprises 40-80 parts solid with 40-55%bacrylic resin emulsion, 20-40 parts of acrylic resin powder, 5-20 parts of solid with 40-60%EVA emulsion as well as 7-13 parts of chlorinated polypropylene or polyolefin substrate adhesion promoter. The nano silver decoration laminated board provided by the invention is good in stability and dispersion, and can fully resist mildew.

Description

technical field [0001] The invention relates to the field of nanometer materials, in particular to a nanometer silver decorative veneer. Background technique [0002] Metal nanomaterials are an important branch of nanomaterials, represented by precious metals gold, silver, and copper, among which nano-silver has received the most attention because of its broad application prospects. Nano-silver can be used in many ways: adding a small amount of nano-silver to chemical fiber can improve some properties of chemical fiber products and make it have a strong bactericidal ability; doping an appropriate amount of nano-silver in the silicon oxide film can make The glass coated with this film has certain photoluminescence. Therefore, nano-silver has broad application prospects in the fields of antibacterial materials, high-efficiency catalysts, lubricants, light-absorbing materials, coatings, sensors, conductive pastes, high-performance electrode materials, etc., and has become a fu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44C5/04B22F9/24
Inventor 刘元强沈金祥詹先旭杨勇
Owner DEHUA TB NEW DECORATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com