A technology of wet strength agent and emulsion type, which is applied in the field of emulsion type wet strength agent and its preparation, which can solve the problems of short storage time, easy deterioration, and inability to store for a long time, and achieve the effect of improved folding resistance and long storage time

Active Publication Date: 2015-11-25
SUZHOU HENGKANG NEW MATERIALS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wet strength agent can be used for different papers to improve the wet strength and dry strength of paper, so as to make the paper better in folding resistance and burst resistance. Wet strength agent is a light yellow, transparent viscous liquid. Such a solution The storage time is relatively short, generally about half a year. The preparation process contains harmful substances such as formaldehyde, and it is easy to deteriorate, so it cannot be stored for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] An emulsion type wet strength agent, comprising the following raw materials in parts by weight: 50 parts of dimethyl diallyl ammonium chloride, 40 parts of polyamide polyamine epichlorohydrin resin, 30 parts of dicyandiamide, stearic acid 60 parts of polyoxyethylene ester, 55 parts of myristate stearic acid, 65 parts of sodium hyaluronate, 20 parts of sodium formate, 35 parts of polyoxyethylene ether, 55 parts of aluminum oxide, 60 parts of azobisisobutyronitrile , 70 parts of formic acid, 50 parts of sodium carbonate, 30 parts of sodium sulfamate aqueous solution, and 10 parts of catalyst.

[0014] Wherein, the catalyst is dicarboxy half ester, and the mass fraction of sodium sulfamate aqueous solution is 20%.

[0015] The preparation method of the above-mentioned wet strength agent comprises the following steps: mixing dimethyl diallyl ammonium chloride, polyamide polyamine epichlorohydrin resin, dicyandiamide, polyoxyethylene stearate, myristate Mix stearic acid and...

Embodiment 2

[0017] An emulsion type wet strength agent, comprising the following raw materials in parts by weight: 60 parts of dimethyl diallyl ammonium chloride, 50 parts of polyamide polyamine epichlorohydrin resin, 40 parts of dicyandiamide, stearic acid 70 parts of polyoxyethylene ester, 60 parts of myristate stearic acid, 70 parts of sodium hyaluronate, 30 parts of sodium formate, 40 parts of polyoxyethylene ether, 70 parts of aluminum oxide, 65 parts of azobisisobutyronitrile , 80 parts of formic acid, 60 parts of sodium carbonate, 40 parts of sodium sulfamate aqueous solution, and 20 parts of catalyst.

[0018] Wherein, the catalyst is dimethylolpropionic acid, and the mass fraction of sodium sulfamate aqueous solution is 40%.

[0019] The preparation method of the above-mentioned wet strength agent comprises the following steps: mixing dimethyl diallyl ammonium chloride, polyamide polyamine epichlorohydrin resin, dicyandiamide, polyoxyethylene stearate, myristate Mix stearic acid...

Embodiment 3

[0021] An emulsion type wet strength agent, comprising the following raw materials in parts by weight: 55 parts of dimethyl diallyl ammonium chloride, 45 parts of polyamide polyamine epichlorohydrin resin, 35 parts of dicyandiamide, stearic acid 65 parts of polyoxyethylene ester, 58 parts of myristate stearic acid, 68 parts of sodium hyaluronate, 25 parts of sodium formate, 38 parts of polyoxyethylene ether, 60 parts of aluminum oxide, 63 parts of azobisisobutyronitrile , 75 parts of formic acid, 55 parts of sodium carbonate, 35 parts of sodium sulfamate aqueous solution, and 15 parts of catalyst.

[0022] Wherein, the catalyst is dimethylolpropionic acid, and the mass fraction of sodium sulfamate aqueous solution is 30%.

[0023] The preparation method of the above-mentioned wet strength agent comprises the following steps: mixing dimethyl diallyl ammonium chloride, polyamide polyamine epichlorohydrin resin, dicyandiamide, polyoxyethylene stearate, myristate Mix stearic acid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an emulsion-type wet strength agent and a preparation method thereof. The emulsion-type wet strength agent is prepared from dimethyl diallyl ammonium chloride, polyamide polyamine epichlorohydrin resin, dicyandiamide, polyethylene glycol monostearate, stearyl myristate, sodium hyaluronate, sodium formate, polyoxyethylene ether, alumina, azodiisobutyronitrile, formic acid, sodium carbonate, a sodium sulfamate aqueous solution and a catalyst. The preparation method comprises the following steps of mixing dimethyl diallyl ammonium chloride, polyamide polyamine epichlorohydrin resin, dicyandiamide, polyethylene glycol monostearate, stearyl myristate and sodium hyaluronate to obtain a uniform mixture, adding sodium formate, polyoxyethylene ether, alumina and azodiisobutyronitrile into the mixture, heating the mixture to a temperature of 40-60 DEG C for a reaction for 1-2h, adding formic acid, sodium carbonate, the sodium sulfamate aqueous solution and the catalyst into the reaction product, carrying out mixing to obtain a uniform mixture and carrying out standing. The emulsion-type wet strength agent is green and environmentally friendly and greatly improves wet strength, tensile strength and folding strength of a paper coated with the emulsion-type wet strength agent.

Description

technical field [0001] The invention relates to the field of papermaking treatment agents, in particular to an emulsion type wet strength agent and a preparation method thereof. Background technique [0002] Wet strength agent can be used for different papers to improve the wet strength and dry strength of paper, so that the folding resistance and burst resistance of paper are better. Wet strength agent is a slightly yellow, transparent viscous liquid. Such a solution The storage time is relatively short, generally about half a year. The preparation process contains harmful substances such as formaldehyde, and it is easy to deteriorate, so it cannot be stored for a long time. Contents of the invention [0003] The purpose of the present invention is to provide an emulsion type wet strength agent and a preparation method thereof, which has a long storage time and is environmentally friendly. [0004] The present invention adopts the following technical solutions to solve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21H21/20C08F283/04C08F251/00
Inventor 邓强
Owner SUZHOU HENGKANG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products