A kind of p-n series expansion reaction flame retardant and preparation method thereof

An expansion reaction, P-N technology, applied in the chemical field, can solve problems such as large amount of addition, smoke, and environmental pollution

Inactive Publication Date: 2016-08-24
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the application method of flame retardants, they can be divided into additive flame retardants and reactive flame retardants. According to the composition, additive flame retardants mainly include inorganic flame retardants, halogenated flame retardants (organic chlorides and organic Bromide), phosphorus-based flame retardants (red phosphorus, phosphoric acid ester and halogenated phosphate ester, etc.) Such as: halogenated flame retardants produce harmful gases in high temperature environment, pollute the environment, generate smoke, add a large amount, affect mechanical properties, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of p-n series expansion reaction flame retardant and preparation method thereof
  • A kind of p-n series expansion reaction flame retardant and preparation method thereof
  • A kind of p-n series expansion reaction flame retardant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1 Preparation of P-N series intumescent reactive flame retardant

[0025] (a) Add 0.13mol of acrylic acid to a 250ml three-neck flask equipped with a constant pressure low liquid funnel, stirrer and reflux device, stir magnetically at a rate of 200rpm and raise the temperature to 90°C. At this time, add 0.1mol of benzene Phosphorous dichloride, the dropping rate is controlled at 1.0ml / min, and the dropping time is 2h; after the dropping is completed, the temperature is raised to 110°C and refluxed, and the reaction is continuously stirred at 200rpm for 4h. After the reaction is completed, the solution becomes a colorless transparent liquid. It is 2-carboxyethylphenylphosphorous acid;

[0026] (b) Cool the 2-carboxyethylphenylphosphorous acid obtained in step a to 1°C in a low-temperature reaction constant temperature bath, add 0.26mol triethylamine acid-binding agent, raise the temperature to 5°C, and take 0.2mol p-aminobenzene Dissolve formic acid in glacial a...

Embodiment 2

[0040] Add 0.13 mol of acrylic acid to a 250 ml three-necked flask equipped with a constant-pressure low-liquid funnel, a stirrer and a reflux device, stir magnetically at a rate of 200 rpm and heat up to 90 ° C. The dropping rate was controlled at 1.0ml / min, and the dropping time was 2h; after the dropping was completed, the temperature was raised to 110°C for reflux, and the stirring reaction was continued at a rate of 200rpm for 4h. - Carboxyethylphenylphosphorous acid;

[0041] Place the above product in a low-temperature reaction constant temperature bath and cool it to about 1°C, add 0.26mol triethylamine acid-binding agent, heat up to 5°C, dissolve 0.19mol p-aminobenzoic acid in glacial acetic acid, add it to 2-carboxyethyl In the mixed solution of phenylphosphinic acid and triethylamine, stir the reaction at a rate of 200rpm for 2h, then raise the temperature to 80°C, and continue to stir the reaction at a rate of 200rpm for 4h; After suction filtration and drying, a ...

Embodiment 3

[0043] Add 0.13 mol of acrylic acid to a 250 ml three-necked flask equipped with a constant-pressure low-liquid funnel, a stirrer and a reflux device, stir magnetically at a rate of 200 rpm and heat up to 90 ° C. The dropping rate was controlled at 1.0ml / min, and the dropping time was 2h; after the dropping was completed, the temperature was raised to 110°C for reflux, and the stirring reaction was continued at a rate of 200rpm for 4h. - Carboxyethylphenylphosphorous acid.

[0044] Put the above product in a low-temperature reaction constant temperature bath and cool it to about 1°C, add 0.26mol triethylamine acid-binding agent, heat up to 5°C, dissolve 0.21mol p-aminobenzoic acid in glacial acetic acid, add it to 2-carboxyethyl In the mixed solution of phenylphosphinic acid and triethylamine, stir the reaction at a rate of 200rpm for 2h, then raise the temperature to 80°C, and continue to stir the reaction at a rate of 200rpm for 4h; After suction filtration and drying, a wh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a P-N series expansion reaction type flame retardant p-(carboxyphenyl-amino)-(carboxyphenyl-amidoethyl)phenylphosphine oxide and its preparation method: (a) p-aminobenzoic acid solution In glacial acetic acid; (b) Add triethylamine and the mixed solution obtained in step a to the 2-carboxyethylphenylphosphinic acid solution, stir and react at high speed for 2 hours, heat up to 80°C, react for 4 hours, then cool and hydrolyze , suction filtration, water washing and drying, the white powder obtained is the P-N series expansion reaction flame retardant; the present invention overcomes the disadvantages of general flame retardants such as producing harmful gas, polluting the environment, emitting smoke, and affecting mechanical properties, etc. The terminal group bonds the effective flame retardant ingredients to the main chain of PA66, which plays the role of essential flame retardancy, and has the advantages of harmlessness, smoke suppression, high efficiency, and environmental protection.

Description

technical field [0001] The invention belongs to the field of chemistry, in particular to a P-N series expansion reaction flame retardant and a preparation method thereof. Background technique [0002] With the advancement of science and technology, polymer materials such as synthetic fibers, rubber, and plastics are increasingly used in various fields, especially engineering plastics play a more important role in the national economy and people's lives. However, engineering plastics belong to Flammable or combustible polymer materials are prone to fire and other accidents. In order to solve the problems of engineering plastics such as heat resistance and smoke suppression, the most effective method is to introduce flame retardants to convert flammable or combustible polymer materials into flame-retardant or Non-combustible materials, reduce the burning rate, delay the spread of flames, and control the occurrence of fires. According to the application method of flame retarda...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G69/42C07F9/36
Inventor 崔益华吕文晏袁锦瑶张伟曹玺张绪杰
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com