Glass ceramic bowl with good strength and preparation process thereof

A ceramic bowl, high-strength technology, applied in the field of tableware, can solve the problems of glass products being fragile, fragments are easy to scratch the human body, etc., and achieve the effects of not being easy to break, not sharp fragments, and no residue of toxic substances

Active Publication Date: 2014-11-19
米兰度骨瓷(上海)有限公司
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Glass products are easy to break, and the fragments are easy to scratch the human

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A glass-ceramic bowl with good strength is composed of the following components in parts by weight: 50 parts of silicon dioxide, 18 parts of nano-silicon carbide, 10 parts of aluminum oxide, 5 parts of glass fiber, 0.8 part of chloroplatinic acid, tourmaline 1 part of fine powder, 3 parts of boron nitride, 1 part of sodium silicate, 3 parts of carbon fiber, 0.2 part of selenium powder, 2 parts of firing aid, 0.5 part of graphene microflakes and 0.8 part of boron fiber;

[0026] Graphene microflakes are grown in a three-dimensional honeycomb manner. After generation, wet nano-grinding is used to grind in a single direction to prepare graphene microflakes with nanometer thickness and micron area. All four valence electrons form covalent bonds and are bound, unable to form a directional mobile electron flow, so they cannot conduct electricity.

[0027] A method for preparing a glass-ceramic bowl with good strength, comprising the following process steps,

[0028] 1) Dispe...

Embodiment 2

[0034] A glass-ceramic bowl with good strength is composed of the following components in parts by weight: 55 parts of silicon dioxide, 20 parts of nano-silicon carbide, 15 parts of aluminum oxide, 8 parts of glass fiber, 1 part of platinum compound, and fine powder of tourmaline 1 part, 4 parts of boron nitride, 2 parts of sodium silicate, 4 parts of carbon fiber, 0.5 part of selenium powder, 3 parts of firing aid, 1 part of graphene microchip and 1 part of boron fiber;

[0035] The platinum compound is selected from chloroplatinic acid;

[0036] The graphene microflakes are produced by growing crystals in a three-dimensional honeycomb manner. After generation, wet nanogrinding is used to grind in a single direction to prepare graphene microflakes with a nanometer thickness and a micronized area, in which each carbon The four valence electrons of the atom are all bound by covalent bonds, and cannot form a directional mobile electron flow, so they cannot conduct electricity. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a glass ceramic bowl with good strength, and relates to the technical field of tableware. The glass ceramic bowl comprises the following components in parts by weight: 50-55 parts of silicon dioxide, 15-20 parts of nanometer silicon carbide, 10-15 parts of aluminium trioxide, 3-8 parts of glass fibers, 0.5-1 part of platinum compounds, 0.5-1 part of tourmaline micropowder, 2-4 parts of boron nitride, 0.2-2 parts of sodium silicate, 2-4 parts of carbon fibers, 0.1-0.5 part of selenium powder, 0.1-1 part of graphene mini-sheets and 0.5-1 part of boron fibers. The glass ceramic bowl disclosed by the invention is smooth in surface, good in strength and low in possibility of breaking due to dropping through special preparation on raw materials. Compared with the traditional process, the glass ceramic bowl disclosed by the invention has the advantages of short required time, low energy consumption, good product texture and no toxic substance residue.

Description

technical field [0001] The invention relates to the technical field of tableware, in particular to a glass ceramic bowl with good strength and a preparation process. Background technique [0002] Glass is divided into non-oxide glass and oxide glass according to the composition, oxide glass is divided into silicate glass, borate glass, phosphate glass and so on. Silicate glass refers to the basic composition of Si0 2 Glass is a colorless and transparent material with the largest output, the widest range of uses, and the lowest price. Quartz glass is the best among silicate glasses. The raw materials used to manufacture quartz glass are crystal, high-purity quartz sand, or white quartz sand, and its composition is high-purity Si0 2 , the melting temperature is required to be above 1713°C. [0003] Quartz glass has a series of special physical and chemical properties: 1. It has excellent high temperature resistance, and its melting point is similar to that of platinum; 2. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C10/14
Inventor 彭友才
Owner 米兰度骨瓷(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap