Preparation method of flame-retardance and light-resistance phosphorylation fatliquor

A phosphorylated fatliquoring agent and light resistance technology, which is applied in chemical treatment of small hide/big hide/leather/fur, small hide/big hide/leather/fur treatment, leather impregnation, etc. Agglomeration and other problems, achieve low price, improve heat release too fast, and control production costs

Inactive Publication Date: 2014-11-19
ANYANG INST OF TECH
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Because the phosphorylation reagent commonly used in the preparation of phosphorylated fatliquor: phosphorus pentoxide has high activity and fast reaction rate, but it is difficult to join the system and has the defects of agglomeration, so it is necessary to disperse phosphorus pentoxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] (1) Preparation of phosphorus pentoxide dispersion: mix 20g of phosphorus pentoxide, Sodium lignosulfonate Add 60g and 12g of chlorinated paraffin-70 into a 250ml three-necked flask, mix and stir at 70°C for 2 hours to obtain 90g of phosphorus pentoxide dispersion;

[0026] (2) Add 50g of castor oil, 0.25g of concentrated sulfuric acid and 0.15g of silver molybdate to a 500ml three-necked flask with a stirrer, heat up to 70°C, condense and reflux for 3 hours to obtain product A; (1) 90g of the prepared phosphorus pentoxide dispersion was stirred evenly, then heated to 70°C, and kept for 3 hours to obtain the product B;

[0027] (3) Add 10g of cinnamoylcaffeic acid to product B, stir evenly, heat up to 60°C, keep warm for 1 hour, then add 11g of N-(phosphonomethyl)glycine isopropylamine salt and 5.5g of cuprous chloride, and heat up to 70°C, stirred and reacted for 2 hours to obtain product D;

[0028] (4) Add 15ml of sodium hydroxide solution with a mass concentratio...

example 2

[0030] (1) Preparation of phosphorus pentoxide dispersion: Add 20g of phosphorus pentoxide, 60g of alkylphenol polyoxyethylene ether formaldehyde condensate sulfate and 12g of chlorinated paraffin-70 into a 250ml three-necked bottle, and mix at 70°C Stirring and reacting for 2 hours, 91 g of phosphorus pentoxide dispersion liquid was obtained;

[0031] (2) Add 50g of castor oil, 0.25g of concentrated sulfuric acid and 0.15g of silver molybdate into a 500ml three-neck flask with a stirrer, raise the temperature to 85°C, condense and reflux for 4 hours to obtain product A; (1) 91g of the prepared phosphorus pentoxide dispersion was stirred evenly, then heated to 90°C, and kept for 3 hours to obtain the product B;

[0032] (3) Add 15g of 2-methyl-2-butenyl-ferulic acid to product B, stir evenly, heat up to 80°C, keep warm for 3 hours, then add 11g of molybdic acid and 5.5g of cuprous chloride, and heat up to 70°C, stirred and reacted for 3 hours to obtain product D;

[0033] (4...

example 3

[0035] (1) Preparation of phosphorus pentoxide dispersion: Add 20g of phosphorus pentoxide, 60g of sodium dibutylnaphthalenesulfonate and 12g of chlorinated paraffin-70 into a 250ml three-necked flask, mix and stir at 70°C for 2h to obtain Phosphorus pentoxide dispersion 92g;

[0036] (2) Add 50g of castor oil, 0.25g of concentrated sulfuric acid and 0.15g of silver molybdate to a 500ml three-necked flask with a stirrer, raise the temperature to 78°C, condense and reflux for 3.5h to obtain product A; 92g of the phosphorus pentoxide dispersion prepared in the above (1) was stirred evenly, then the temperature was raised to 80°C, and the temperature was kept for 3.5 hours to obtain the product B;

[0037] (3) Add 12.5g of 2-methyl-2-butenyl-p-coumaric acid to product B, stir evenly, heat up to 70°C, keep warm for 3 hours, then add 11g of trisodium dodecamolybdenum phosphate and chlorine Cuprous chloride 5.5g, heated up to 70°C, stirred for 2.5h to obtain product D;

[0038] (4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of flame-retardance and light-resistance phosphorylation fatliquor. Concentrated sulfuric acid and silver molybdate are added in castor oil, the temperature is increased to 70-85 DEG C, and the condensation backflow insulation reaction is performed for 3-4 hours to obtain a product A; phosphorus pentoxide dispersion liquid is added in the product A for evenly mixing, and the temperature is increased to 70-90 DEG C and kept for 3-4 hours to obtain a product B; a light resistant material is added in the product B for evenly mixing, the temperature is increased to 60-80 DEG C and kept for 1-3 hours, a flame retardant material and cuprous chloride are added in the product B, the temperature is increased to 70 DEG C, and the mixing reaction is performed for 2-3 hours to obtain a product D; and sodium hydroxide solution is dripped in the product D to become neutral to obtain brown liquid, and the brown liquid is the flame-retardance and light-resistance phosphorylation fatliquor. The prepared fatliquor not only retains the sensory performance and mechanical strength of traditional fatliquor, but also has excellent flame retardance and light resistance.

Description

technical field [0001] The invention relates to a preparation method of a phosphorylated fatliquoring agent, in particular to a preparation method of a flame-retardant and light-resistant phosphorylated fatliquoring agent. Background technique [0002] With the improvement of people's living standards, furniture leather and automotive leather are also increasing. At the same time, fires caused by leather and synthetic leather are also increasing. Therefore, the flame retardant problem of leather has become a research hotspot in the industry. [0003] In the process of leather processing, fatliquoring is an essential process, which has a great influence on the sensory and mechanical properties of leather products. However, the fatliquor used for fatliquoring is easy to burn. Therefore, it is necessary to adjust the fatliquor Modification is carried out to reduce its flammability and improve its flame resistance, so as to meet the market demand for flame-retardant leather pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C14C9/02
Inventor 段宝荣
Owner ANYANG INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com