Organic-inorganic composite nanometer heat-insulating fire-retardant coating and preparation method thereof

An inorganic composite and nano-insulation technology, applied in the field of chemical building materials, can solve the problems of poor foamability, poor flame retardant and heat insulation performance, etc., and achieve the effects of low thermal conductivity, preventing rapid fire occurrence, and increasing anti-shedding properties.

Active Publication Date: 2014-12-03
山西省建筑科学研究院集团有限公司
View PDF8 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since epoxy resin molecules contain a large number of benzene ring rigid groups, as a film-forming substance of intumescent fireproof coatings, when heated and expanded, the foamability is poor, and the flame retardant and heat insulation performance is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]Weigh 10 parts of acrylate emulsion or styrene-acrylic emulsion according to the mass fraction at room temperature in a cylinder with dispersing emulsification, then add 10 parts of water-based epoxy emulsion and 0.05 part of defoamer respectively, and set the speed of the disperser mixer to 500r / min stirring for 8-10min; then add 10 parts of pentaerythritol, 25 parts of melamine, 15 parts of ammonium polyphosphate, 10 parts of nano aluminum hydroxide, 4 parts of nano magnesium hydroxide, 10 parts of nano titanium dioxide, 5 parts of Ceramic hollow microspheres, 1 part of glass hollow microspheres, 0.2 part of hydrophobic agent, 0.1 part of leveling agent, set the speed of the stirrer at 1500r / min~2000r / min and stir again for 15~50min to obtain the organic-inorganic composite nano-separator Thermal insulation fireproof coating.

Embodiment 2

[0037] Weigh 15 parts of acrylate emulsion or styrene-acrylic emulsion according to the mass fraction at room temperature in a cylinder with dispersing emulsification, then add 6 parts of water-based epoxy emulsion and 0.05 part of defoamer respectively, and set the speed of the disperser mixer to 500r / min stirring for 8-10min; Ceramic hollow microspheres, 5 parts of glass hollow microspheres, 0.2 parts of hydrophobic agent, 0.1 part of leveling agent, set the speed of the stirrer at 1500r / min~2000r / min and stir again for 15~50min to obtain the organic-inorganic composite nano-separator Thermal insulation fireproof coating.

Embodiment 3

[0039] Weigh 20 parts of acrylate emulsion or styrene-acrylic emulsion according to the mass fraction at room temperature in a cylinder with dispersing emulsification, then add 8 parts of water-based epoxy emulsion and 0.06 part of defoamer respectively, and set the speed of the disperser mixer to 500r / min and stirring for 8-10min; Ceramic hollow microspheres, 4 parts of glass hollow microspheres, 0.3 parts of hydrophobic agent, 0.2 parts of leveling agent, set the speed of the stirrer at 1500r / min~2000r / min and stir again for 15~50min to obtain the organic-inorganic composite nano-separator Thermal insulation fireproof coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an organic-inorganic composite nanometer heat-insulating fire-retardant coating and a preparation method thereof. The organic-inorganic composite nanometer heat-insulating fire-retardant coating is prepared by mixing organic film-forming substance acrylic ester emulsions or styrene-acrylate emulsions, epoxide resin, organic intumescent fire-retardant system pentaerythritol, melamine and ammonium polyphosphate with inorganic fire retardant nanometer aluminum hydroxide, nanometer magnesium hydroxide, filler nanometer titanium dioxide, ceramic hollow microspheres, glass hollow microspheres and a part of auxiliary agents. The organic-inorganic composite nanometer heat-insulating fire-retardant coating disclosed by the invention not only has excellent facing property and fire-retardant property, but also achieves reflection effect on solar radiation and certain heat-insulating and heat-preserving property on a substrate, also has good adhesivity, mechanical property and hydrophobic effect, can be formed through spray coating or brush coating before being solidified, and is a novel water-based multifunctional fire-retardant material. The organic-inorganic composite nanometer heat-insulating fire-retardant coating disclosed by the invention can not only be used as a general building wall body fire-retardant coating, but also be suitable for the fire prevention of building and ornament materials, heat-insulating materials, steel structure supports, beam columns, metal roofs and the like.

Description

technical field [0001] The invention belongs to the field of chemical building materials, and in particular relates to a composite nano heat-insulating fireproof coating and a preparation method thereof. technical background [0002] Building fire prevention is an important field of fire science and technology. Our country attaches great importance to fire prevention. Many buildings require the use of fireproof coatings during construction design. Fire retardant coatings are applied on the surface of combustible substrates to decorate and protect the substrates. They can prevent the spread and spread of fire, prolong the ignition time of the substrates or the thermal insulation performance to delay the destruction time of the substrates, and provide protection for life and property safety. Favorable protection. At present, there are many kinds of fire retardant coatings, which are widely used in many fields. Fire retardant coatings have different classification methods acc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D163/00C09D5/18C09D5/33C09D7/12
Inventor 王芳芳李宪军郭涵瑜李绩王晓敏裴峻军
Owner 山西省建筑科学研究院集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap