A kind of preparation method of sulfuric acid acidified mesoporous SIO2 colloidal sphere catalyst for synthesizing biodiesel
A technology for synthesizing organisms and colloidal spheres, which is applied in the direction of physical/chemical process catalysts, chemical instruments and methods, and biofuels. It can solve problems such as saponification reactions, and achieve low environmental pollution, few by-products, and high catalytic efficiency. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] 1# sulfuric acid acidified mesoporous SiO 2 The concrete preparation steps of colloidal ball catalyst are as follows:
[0031] (1) Preparation of cetyltrimethylammonium phosphomolybdate
[0032] Measure 100mL of absolute ethanol into a beaker, add 0.4g of cetyltrimethylammonium bromide (CTAB), stir until CTAB is completely dissolved, measure 50mL of absolute ethanol into another beaker, add 0.75g For phosphomolybdic acid, stir with a glass rod until the phosphomolybdic acid is completely dissolved. Under stirring, use a dropper to drop the phosphomolybdic acid solution into the CTAB solution. After the addition is completed, continue stirring for 0.5h to make it fully react , after filtering and drying, the product quaternary ammonium phosphomolybdate was obtained, denoted as M-6;
[0033] (2) Mesoporous SiO 2 Preparation method of colloidal balls:
[0034] Weigh 80mg of M-6, put it into a round bottom flask, add 15mL of absolute ethanol, disperse in ultrasonic wave...
Embodiment 2
[0038] 2# sulfuric acid acidified mesoporous SiO 2 The concrete preparation steps of colloidal ball catalyst are as follows:
[0039] (1) The preparation method of M-6:
[0040] With the preparation method of M-6 among the embodiment 1.
[0041] (2) Mesoporous SiO 2 Preparation method of colloidal balls:
[0042] Weigh 70mg of M-6, put it into a round bottom flask, add 15mL of absolute ethanol, disperse in ultrasonic wave for 30min, until the solid is completely dispersed, add 60mL of distilled water dropwise, and keep stirring at 28°C. After stirring for 6 hours, add 0.14mL of ammonia water and 0.15mLTEOS, continue to stir at constant temperature for 16 hours, filter, dry, and then put the product into a muffle furnace for roasting at a heating rate of 1°C / min, at a constant temperature of 450°C for 4.5h to obtain mesoporous SiO 2 colloidal balls.
[0043] (3) Acidified mesoporous SiO 2 Preparation of colloidal spheres
[0044] With the preparation method of step (3) i...
Embodiment 3
[0046] 3# sulfuric acid acidified mesoporous SiO 2 The concrete preparation steps of colloidal ball catalyst are as follows:
[0047] (1) The preparation method of M-6:
[0048] With the preparation method of M-6 among the embodiment 1.
[0049] (2) Mesoporous SiO 2 Preparation method of colloidal balls:
[0050] Weigh 180mg of M-6, put it into a round bottom flask, add 15mL of absolute ethanol, disperse in ultrasonic wave for 30min, until the solid is completely dispersed, add 60mL of distilled water dropwise, and keep stirring at 28°C. After stirring for 6 hours, add 0.14mL of ammonia water and 0.15mLTEOS, continue to stir at constant temperature for 16 hours, filter, dry, and then put the product into a muffle furnace for roasting at a heating rate of 1°C / min, at a constant temperature of 450°C for 4.5h to obtain mesoporous SiO 2 colloidal balls.
[0051] (3) Acidified mesoporous SiO 2 Preparation of colloidal spheres
[0052] With the preparation method of step (3) ...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
pore size | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com