A heat-resistant and oil-resistant hot-melt adhesive for notebook glue binding

A notebook and hot melt adhesive technology, applied in the directions of adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problem of notebook paper falling, and achieve fine coating, strong oil resistance and strong bonding ability. Effect

Inactive Publication Date: 2016-02-10
吕明肇
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In our daily life, we sometimes encounter this kind of situation: the notebook falls when the paper is turned over

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A heat-resistant and oil-resistant hot-melt adhesive for notebook binders, which is prepared by mixing material A and material B at a ratio of 1:2.2:

[0014] Described A material is made by the raw material of following weight (kg): terpene resin 30, titanium dioxide 10, diatomite 6, zinc oxide 2, bamboo charcoal powder 5, tannic acid 0.2, epoxy resin 50, ethylene glycol Amine 0.5, white carbon black 2, white mineral oil 0.5, paraffin 0.4, calcium formate 0.4, nylon 66 resin 1, chlorinated paraffin 2, humic acid 0.2;

[0015] Described B material is made by the raw material of following weight (kg): barium sulfate 2, rosin 3, C5 petroleum resin 30, nano calcium carbonate 1, zeolite powder 4, cobalt isooctanoate 0.2, silicon dioxide powder 1, chlorine Aluminum 2, chopped glass fiber 1, acrylamide 0.2, polyvinyl acetate emulsion 2.

[0016] The preparation method of the hot-melt adhesive for heat-resistant and oil-resistant notebook binders comprises the following steps...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a temperature-resistant and oil-resistant hot melt adhesive for perfect binding of a notebook. The hot melt adhesive is prepared by uniformly mixing materials A and B in a proportion of 1 to (2-2.2). The material A is prepared from the following raw materials in parts by weight: 20-30 parts of terpene resin, 5-10 parts of titanium dioxide, 4-8 parts of diatomite, 1-2 parts of zinc oxide, 3-5 parts of bamboo charcoal powder, 0.1-0.2 part of tannic acid, 30-50 parts of epoxy resin, 0.3-0.5 part of ethanediamine, 1-2 parts of white carbon black, 0.3-0.5 part of white mineral oil, 0.2-0.4 part of paraffin, 0.2-0.4 part of calcium formate, 1-3 parts of nylon 66 resin, 1-2 parts of chlorinated paraffin and 0.1-0.2 part of humic acid.

Description

technical field [0001] The invention belongs to the field of adhesives, in particular to a heat-resistant and oil-resistant hot-melt adhesive for notebook binders. Background technique [0002] The glue used for perfect binding of books, periodicals and notebooks is mainly divided into back glue and side glue. The back glue is mainly milky white, and the side glue is mainly white transparent or light yellow transparent. The hot-melt adhesive used as side glue requires good fluidity, low viscosity, long opening time and curing time, and high bonding strength. In our daily life, we sometimes encounter this situation: the notebook falls when the paper is turned over. The correct use of hot melt adhesive is the quality assurance of perfect binding products. Contents of the invention [0003] The object of the present invention is to provide a heat-resistant and oil-resistant hot-melt adhesive for notebook binders. [0004] In order to achieve the above object, the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/04C09J11/06C09J11/08
Inventor 吕明肇
Owner 吕明肇
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com