A silk-like fabric technology, applied in the field of silk-like fabrics, can solve problems such as insufficient skin-friendly properties, and achieve the effects of good skin-friendly properties, light weight, and low temperature

Active Publication Date: 2016-04-27
浙江泉能纺织股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the actual operation process, it is found that although the prepared fabric feels soft, it is not skin-friendly enough, and there is still a certain gap between silk and silk fabrics in terms of wearing comfort.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Material selection: the warp yarn is pure BB.FDY diamond yarn drawn yarn, and the weft yarn is blended yarn of soybean protein fiber and milk protein fiber;

[0027] (2) Warp processing: BB.FDY diamond wire drafting yarn → TW-N warping machine → KSH300 sizing machine → KB20 paralleling machine → TD type splitting machine → threading → A;

[0028] (3) Weft yarn treatment: soybean protein fiber and milk protein fiber blended yarn → winding → B;

[0029] (4) A and B are woven into cloth with a ZA205i air-jet loom;

[0030] (5) Organize.

[0031] The warping speed described in step (2) is set to 300m / min, and the single yarn tension reaches 23.5cN;

[0032] The sizing described in step (2): the vehicle speed is set at 200m / min; the sizing rate is controlled at about 8%, and the size formula is according to the mass percentage: ZS805F acrylic acid 8%, PVA205MB1%, chitosan 2%, collagen protein 1%, Antistatic agent 0.2%, the rest is water;

[0033] The soybean protein ...

Embodiment 2

[0039] (1) Material selection: the warp yarn is pure BB.FDY diamond yarn drawn yarn, and the weft yarn is blended yarn of soybean protein fiber and milk protein fiber;

[0040] (2) Warp processing: BB.FDY diamond wire drafting yarn → TW-N warping machine → KSH300 sizing machine → KB20 paralleling machine → TD type splitting machine → threading → A;

[0041] (3) Weft yarn treatment: soybean protein fiber and milk protein fiber blended yarn → winding → B;

[0042] (4) A and B are woven into cloth with a ZA205i air-jet loom;

[0043] (5) Organize.

[0044] The warping speed described in step (2) is set to 300m / min, and the single yarn tension reaches 23.5cN;

[0045] The sizing described in step (2): the vehicle speed is set at 200m / min; the sizing rate is controlled at about 8%, and the size formula is according to the mass percentage: ZS805F acrylic acid 8%, PVA205MB1%, chitosan 2%, collagen protein 1%, Antistatic agent 0.2%, the rest is water;

[0046] The soybean protein ...

Embodiment 3

[0052] (1) Material selection: the warp yarn is pure BB.FDY diamond yarn drawn yarn, and the weft yarn is blended yarn of soybean protein fiber and milk protein fiber;

[0053] (2) Warp processing: BB.FDY diamond wire drafting yarn → TW-N warping machine → KSH300 sizing machine → KB20 paralleling machine → TD type splitting machine → threading → A;

[0054] (3) Weft yarn treatment: soybean protein fiber and milk protein fiber blended yarn → winding → B;

[0055] (4) A and B are woven into cloth with a ZA205i air-jet loom;

[0056] (5) Organize.

[0057] The warping speed described in step (2) is set to 300m / min, and the single yarn tension reaches 23.5cN;

[0058] The sizing described in step (2): the vehicle speed is set at 200m / min; the sizing rate is controlled at about 8%, and the size formula is according to the mass percentage: ZS805F acrylic acid 8%, PVA205MB1%, chitosan 2%, collagen protein 1%, Antistatic agent 0.2%, the rest is water;

[0059] The soybean protein fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a silk-like fabric. The steps include: (1) material selection: the warp yarn is BB.FDY diamond silk drawn silk pure spun yarn, and the weft yarn is a blended yarn of soybean protein fiber and milk protein fiber; (2) Warp processing: BB.FDY diamond wire drafting yarn → TW-N warping machine → KSH300 sizing machine → KB20 paralleling machine → TD type splitting machine → threading → A; (3) Weft yarn Processing: soybean protein fiber and milk protein fiber blended yarn→winding→B; (4) A and B are woven into cloth with ZA205i air-jet loom; (5) Finishing.

Description

technical field [0001] The invention relates to a silk-like fabric and a preparation method thereof, in particular to a silk-like fabric whose texture is very close to real silk. Background technique [0002] The market demand for imitation silk is great, and there are many imitation silk fabrics on the market, but there is still a certain gap between the feel and appearance of real silk fabrics. [0003] In order to achieve the best effect of imitation silk fabrics, the selection of raw materials is very critical. Judging from the cross-sectional shape of silk raw materials, silk is in the form of two inverted triangular fibroin, wrapped with sericin, so its luster is elegant and luxurious. Silk is a protein fiber. Silk fibroin has excellent skin-friendly properties after scouring and dyeing, and it feels soft and comfortable. [0004] Bleached soybean protein composite fiber has good physical and chemical properties, its single fiber fineness can be as low as 0.9dtex, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D47/30D02G3/04D06M16/00D06M101/04D06M101/10D03D15/233D03D15/283D03D15/47D03D15/50
Inventor 王爱泉
Owner 浙江泉能纺织股份有限公司