Finishing technology for yellowing prevention of silk fabric

An anti-yellowing and silk technology, applied in the field of silk, to achieve good shielding effect, excellent water dispersibility, and beneficial to resource regeneration

Inactive Publication Date: 2014-12-24
广州迪柯尼服饰股份有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A moderate amount of ultraviolet radiation is necessary for the growth of human body and plants, but excessive exposure to ultraviolet radiation can cause many problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Dissolve 10g of waste silk in 100ml of lithium bromide solution, treat at 60°C for 2 hours to obtain a silk fibroin solution with a concentration of 10%, mix the ethylene glycol diglycidyl ether aqueous solution with the silk fibroin solution evenly, and prepare a An aqueous solution of silk fibroin and 5% ethylene glycol diglycidyl ether, immersing the silk fabric in the solution until the silk fabric is evenly soaked by the solution, then take it out and dry it at 30°C.

[0025] Mix 20ml tetrabutyl titanate, 40ml glacial acetic acid, and 40ml water evenly, adjust the pH value to 2, stir until it is in a sol-gel state, and then mix it evenly with the silk fibroin solution to obtain 2% silk fibroin. Silk fibroin nano sol finishing agent, immerse silk fabrics in silk fibroin nano sol finishing agent, after two dipping and two rolling, the scrapping rate is 90%, pre-baking at 80°C for 5 minutes, heat treatment at 150°C for 3 minutes, taking out and soaping and drying, and ...

Embodiment 2

[0028] Dissolve 2g of waste silk in 100ml of lithium bromide solution, and treat at 60°C for 2 hours to obtain a silk fibroin solution with a concentration of 2%. Sodium and 1% aqueous solution of ethylene glycol diglycidyl ether, immerse the silk fabric in the solution until the silk fabric is evenly soaked by the solution, take it out and dry it at 30°C.

[0029] Mix 20ml tetrabutyl titanate, 60ml glacial acetic acid, and 20ml water evenly, adjust the pH value to 4, stir until it is in a sol-gel state, and then mix it evenly with the silk fibroin solution to obtain a silk fibroin with a content of 0.2%. Silk fibroin nano sol finishing agent, immerse the silk fabric in the silk fibroin nano sol finishing agent, after dipping and rolling twice, the scrapping rate is 80%, pre-baking at 80°C for 3 minutes, heat treatment at 120°C for 5 minutes, taking it out, soaping and drying, and the silk fabric is obtained. Yellowed silk fabric.

[0030] Wet the anti-yellowing finished silk...

Embodiment 3

[0032] Dissolve 5g of waste silk in 100ml lithium bromide solution, treat at 60°C for 3 hours to obtain a silk fibroin solution with a concentration of 5%, mix the ethylene glycol diglycidyl ether aqueous solution with the silk fibroin solution evenly, and obtain a silk fibroin solution containing 0.5% Sodium and 2% aqueous solution of ethylene glycol diglycidyl ether, immerse the silk fabric in the solution until the silk fabric is evenly soaked by the solution, take it out and dry it at 30°C.

[0033] Mix 20ml tetrabutyl titanate, 40ml glacial acetic acid, and 40ml water evenly, adjust the pH value to 4, stir until it is in a sol-gel state, and then mix it evenly with the silk fibroin solution to obtain a silk fibroin with a content of 0.5%. Silk fibroin nano-sol finishing agent, immerse silk fabrics in silk fibroin nano-sol finishing agent, after dipping and rolling twice, the excess rate is 85%, pre-baking at 80°C for 4 minutes, heat-treating at 130°C for 4 minutes, taking ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a finishing technology for the yellowing prevention silk fabric, and belongs to the technical field of silk. The finishing technology comprises the following steps: dissolving waste silk by using a lithium bromide solution to prepare a silk fibroin solution; immersing silk fabric into the silk fibroin solution containing ethylene glycol diglycidyl ether, taking out the silk fabric, naturally curing, and then immersing the silk fabric into a titanium dioxide sol solution; performing heat treatment after twice immersing and twice rolling; washing and drying to obtain the silk fabric subjected to yellowing-prevention finishing. The finishing method is simple and convenient to operate, can protect silky luster of the silk fabric, and has outstanding advantages in anti-aging and yellowing prevention; the waste silk is used as a raw material, so that the finishing method is environment-friendly and conducive to resource regeneration; the silk fabric prepared by the finishing method is comfortable, safe, environment-friendly, healthy and fashionable.

Description

Technical field: [0001] The invention relates to the technical field of silk, in particular to an anti-yellowing finishing process of silk fabrics. Background technique: [0002] Sunlight contains a large amount of ultraviolet rays, most of which will be absorbed by the ozone layer in the air, and only about 10% of the ultraviolet rays will be projected onto the ground. A moderate amount of ultraviolet radiation is necessary for the growth of human body and plants, but excessive exposure to ultraviolet radiation can cause many problems. [0003] Silk is a kind of natural protein fiber, which mainly contains silk fibroin, sericin and a small amount of other substances. Under the action of light, heat, biology and other factors, silk fiber will turn yellow. Its mechanical properties, surface morphology, aggregate structure, molecular The quality and so on have all changed, and the light has a greater effect on the yellowing process of silk fabrics. [0004] Usually, refined ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/11D06M15/15D06M11/46C07K14/435D06M101/10
Inventor 周继东
Owner 广州迪柯尼服饰股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap