Paper prepared through carboxymethylcellulose modified sodium silicate pulp and preparation method thereof

A kind of technology of carboxymethyl cellulose and sodium silicate, applied in the field of paper made by filling and papermaking

Inactive Publication Date: 2014-12-24
济南科纳信息科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009]The current paper pulp internal sizing agents mainly include rosin glue, reinforced rosin glue, dispersed rosin glue, petroleum resin glue, paraffin glue, etc. Among them, rosin sizing agent And petroleum resin sizing agents are mainly used in acidic papermaking, and the effect on filler modification is poor, so it is difficult to meet the requirements of industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper prepared through carboxymethylcellulose modified sodium silicate pulp and preparation method thereof
  • Paper prepared through carboxymethylcellulose modified sodium silicate pulp and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of paper made of carboxymethyl cellulose modified sodium silicate, prepared according to the following steps:

[0031] (1) First make aluminum sulfate into an aqueous solution with a mass concentration of 5%, impregnate the filter paper for 1 min, and place the filter paper at 100 o C under drying number;

[0032] (2) Put carboxymethyl cellulose with a concentration of 8% in ethanol, add sodium silicate in the ratio of sodium silicate: carboxymethyl cellulose = 1:1, and disperse in carboxymethyl cellulose-ethanol solution, Obtain the carboxymethyl cellulose-ethanol solution containing sodium silicate, pull and dip the filter paper impregnated with aluminum sulfate described in step (1) in the ethanol solution of carboxymethyl cellulose-sodium silicate several times ; After that, air-dry for 24 hours to get it.

Embodiment 2

[0034] A kind of paper made of carboxymethyl cellulose modified sodium silicate, prepared according to the following steps:

[0035] (1) First make aluminum sulfate into an aqueous solution with a mass concentration of 20%, impregnate the filter paper for 3 minutes, and place the filter paper at 105 o Drying number at C; (2) Put carboxymethyl cellulose with a concentration of 12% in ethanol, add sodium silicate to carboxymethyl cellulose in the ratio of sodium silicate: carboxymethyl cellulose = 1:4 In the plain-ethanol solution, ultrasonically oscillate for 8 min to obtain a carboxymethyl cellulose-ethanol solution containing sodium silicate, and use a paint scraper to coat the prepared carboxymethyl cellulose-ethanol solution on the surface of the filter paper. The amount of cloth should be controlled to 8g / m 2 ; Afterwards, the impregnated filter paper was dried at 105° C. for 15 minutes in a constant-temperature blast drying oven to obtain a final product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides paper prepared through carboxymethylcellulose modified sodium silicate pulp. The paper is prepared through the following steps: firstly, preparing water solution of aluminum sulfate with the mass concentration percent of 5-20%, dipping filter paper for 1-3 min, then drying and numbering the filter paper at 100-105 DEG C, secondly, adding sodium silicate into carboxymethylcellulose ethyl alcohol with carboxymethylcellulose concentration of 8-12% according to the ratio of sodium silicate to carboxymethylcellulose being 1:1 to 1:4, so as to ensure that the sodium silicate is dispersed in carboxymethylcellulose-ethyl alcohol solution, obtaining carboxymethylcellulose-ethyl alcohol solution containing sodium silicate, lifting and dipping the filter paper dipped by aluminum sulfate and obtained in step one into the carboxymethylcellulose-sodium silicate ethyl alcohol solution for multiple times, and then performing air drying on the filter paper for 24-48 h, so as to obtain the paper.

Description

[0001] technical field [0002] The invention relates to paper made with filling, in particular to paper made with carboxymethyl cellulose modified sodium silicate and a preparation method thereof. Background technique [0003] Carboxymethyl cellulose is a carboxymethyl group substitution product of cellulose. According to its molecular weight or degree of substitution, it can be a completely soluble or insoluble polymer. The latter can be used as a weak acid cation exchanger to separate neutral or basic proteins. Carboxymethyl cellulose can form high-viscosity colloids and solutions, have the characteristics of adhesion, thickening, flow, emulsification and dispersion, shaping, water retention, protective colloid, film forming, acid resistance, salt resistance, suspension, etc., and is physiologically harmless Therefore, it is widely used in the production of food, medicine, daily chemical, petroleum, paper making, textile, construction and other fields. [0004] Carboxym...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H17/69D21H21/16D21H21/14
Inventor 李上
Owner 济南科纳信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap