Acrylic acid structural adhesive with good weatherability and stability
A stable, acrylic technology, applied in the direction of adhesives, non-polymer organic compound adhesives, etc., can solve the problems of long operating time, acrylic structural adhesive is difficult to meet the requirements of use, etc., achieve long operating time, good high and low temperature resistance , good reliability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1
[0024] Accurately weigh the following raw materials, 20g methyl methacrylate, 25g hydroxyethyl methacrylate, 25g hydroxypropyl methacrylate, 14g ABS, 14g SBS, and put them into the reactor, stir and mix at 40°C for 4h, and cool to room temperature. Add 0.2g of N,N-dihydroxyethyl-p-toluidine, 0.15g of γ-aminopropyltriethoxysilane, 0.15g of γ-(2,3-glycidoxy)propyltrimethoxysilane, Hydroxyanisole 0.03g, EDTA-Na0.02g, paraffin wax 0.05g, gas phase SiO 2 1.4g, vacuum stirring and mixing for 2h, the product component A is obtained; BPO50g, polyol benzoate 15g, epoxy resin 828 30g, PE powder 5g, put into the reactor, mix and stir at room temperature for 4h, vacuum deaeration, that is Obtain product B component.
Example Embodiment
[0025] Example 2
[0026] Accurately weigh the following raw materials, 5g trimethylolpropane methyl triacrylate, 25g hydroxyethyl methacrylate, 30g tetrahydrofuran methacrylate, 20g chloroprene rubber, 15g nitrile rubber, and put it into the reactor, 50g Stir and mix for 4 hours at ℃, cool to room temperature, add 1g N,N-dihydroxyethyl p-toluidine, 3g γ-(methacryloxy)propyltrimethoxysilane, 0.3g p-hydroxyanisole, EDTA- Na0.1g, paraffin wax 0.1g, gas phase SiO 2 0.5g, vacuum stirring and mixing for 2h, the product component A is obtained; 20g BPO, 40g polyol benzoate, 20g epoxy resin 828, 20g PE powder, put into the reactor, mix and stir at room temperature for 4h, vacuum deaeration, that is Obtain product B component.
Example Embodiment
[0027] Example 3
[0028] Accurately weigh the following raw materials, 20g hydroxypropyl methacrylate, 10g hydroxyethyl methacrylate, 20g tetrahydrofuran methacrylate, 20g ABS, 25g nitrile rubber, put them into the reactor, stir and mix at 45°C for 4h, and cool At room temperature, add 2g of N,N-dihydroxyethyl p-toluidine, 1g of γ-(methacryloxy)propyltrimethoxysilane, 0.5g of p-hydroxyanisole, 0.5g of EDTA-Na, and 0.2 of paraffin wax. g, gas phase SiO 2 0.8g, vacuum stirring and mixing for 2h, the product component A is obtained; 30g BPO, 45g polyol benzoate, 10g epoxy resin 828, 15g PE powder, put into the reactor, mix and stir at room temperature for 4h, vacuum deaeration, that is Obtain product B component.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap