Application of Titanium Alloy as Sandblasting Media for Dental Implants

A technology for dental implants and implants, applied in the field of titanium alloys, can solve the problems of contamination of microstructures by impurity elements, application of sandblasting media for titanium alloy dental implants, unevenness, etc., to avoid pollution, protect smoothness, The effect of high production efficiency

Active Publication Date: 2017-09-12
成都华西一为生物植体科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN 103668390 A reports the use of corundum or TiO 2 The sandblasting method in which particles are sprayed on the surface of titanium implants at high speed has problems such as contamination by impurity elements and uneven microstructure
[0007] At present, the titanium alloys used in implants mainly include Ti-13Zr-13Nb, Ti-6Al-7Nb, Ti-15Mo, Ti-6Al-4V, Ti-12Mo-6Zr-2Fe, Ti-35Nb-7Zr-5Ta, Ti -16Nb-10Hf etc. (Chinese patent CN 103668390A), there is no report on the application of titanium alloy as a sandblasting medium for dental implants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of Titanium Alloy as Sandblasting Media for Dental Implants
  • Application of Titanium Alloy as Sandblasting Media for Dental Implants
  • Application of Titanium Alloy as Sandblasting Media for Dental Implants

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Embodiment 1 Application of titanium alloy of the present invention as a sandblasting medium for dental implants

[0065] 1. Preparation before sandblasting

[0066] (1) Sand composition and size

[0067] Composition: 6Al4V titanium alloy -- TC4 (that is, Ti-6Al-4V)

[0068] Size: 60 mesh

[0069] (2) Implant cleaning

[0070] Submerge the implant in an aqueous solution of detergent. The aqueous solution of detergent is prepared by adding water to ordinary household detergent at a ratio of 1:30, and then placed in an ultrasonic oscillator for 20 minutes to remove any damage caused by the previous mechanical processing on the surface of the implant. Oil and other dirt, rinse with purified water and dry.

[0071] (3) Choose a sandblasting machine that can be used for metal sandblasting

[0072] The sandblasting machine structure schematic diagram that the present invention selects is as figure 2 As shown, it includes an operation room 2 with a sandblasting head, a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a new use of titanium alloy, i.e. application as a dental implant sandblasting medium. The invention also discloses a dental implant sandblasting roughening method. The method comprises the steps of: a. selecting titanium alloy as the blasting medium; b. cleaning an implant; and c. blasting sand by a sandblasting machine. According to the invention, the titanium alloy Ti-6Al-4V is adopted as the sandblasting medium, and at the same time the specific sandblasting machine, sandblasting head and clamp are employed to reach the purposes of roughening the implant surface, enhancing the bonding strength between the implant and bone tissue, and accelerating osseointegration. Also, the risk of pollution by undesirable chemical components can be avoided, and elements incompatible with implant chemical components cannot be left on the implant surface subjected to sandblasting treatment.

Description

technical field [0001] The invention relates to the application of a titanium alloy as a sandblasting medium for dental implants. Background technique [0002] When the implant is placed in the jawbone, osseointegration with the surrounding tissue is the criterion for successful implantation. However, its main components are completely different from bone tissue. As a biologically inert material, it cannot induce new bone growth after implantation, and it is integrated with bone tissue. Weaker and takes longer to heal. [0003] With the in-depth research on implant materials, scholars have found that the rough surface has better osteoinductivity, the implant is more firmly integrated with the surrounding bone tissue, and the long-term effect of implant is better than that of the smooth surface implant. At present, surface modification is mainly to improve the wear resistance, corrosion resistance and biological properties (including biocompatibility and bioactivity) of impl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24C1/00B24C11/00B24C3/02B24C9/00
CPCB24C1/00B24C3/02B24C9/00B24C11/00
Inventor 杨小东周镇华陈志宁吴大怡
Owner 成都华西一为生物植体科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com