A technology for cleaning degreaser and corrosion inhibitor, applied in the field of electroplating, can solve the problems of affecting product quality, poor cleaning effect, and many residues, so as to reduce the probability of rework, improve quality and service life, and save labor.

Inactive Publication Date: 2015-04-29
ZHENJIANG RUIDE ENERGY SAVING TECH
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] When the workpiece is electroplated and copper-plated, it is often due to various or artificial or process reasons that the copper plating will adhere to a large amount of oil, dust and other substances on the surface of the workpiece, and at the same time, the surface of the workpiece will also be oxidized to varying degrees, resulting in oxidation. Therefore, it is necessary to clean the workpiece after copper plating. When using traditional cleaning and degreasing agents, not only the cleaning effect is not good, but there are many residues.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A cleaning and degreasing agent for electroplating is characterized in that it consists of the following raw material components in parts by weight:

[0037] Anionic active agent 5 parts

[0038] Non-ionic active agent 5 parts

[0039] Alkylphenol polyoxyethyl ether 8 parts

[0040] Sodium carbonate 20 parts

[0041] Sodium metasilicate 17 parts

[0042] Metal rust inhibitor 18 parts

[0043] Clean corrosion inhibitor 2 parts.

[0044] Wherein, the anionic active agent is sodium dodecylsulfonate and sodium lauryl sulfate mixed in a ratio of 1.3:1.5, and the nonionic active agent is alkylphenol polyoxyethylene ether and fatty alcohol polyoxyethylene ether It is formed by mixing in a ratio of 1: 1.6, the purity of the sodium carbonate is 98%, the purity of the trisodium phosphate is 98%, the cleaning corrosion inhibitor is thiourea, and the metal rust inhibitor is trisodium phosphate.

Embodiment 2

[0046] A cleaning and degreasing agent for electroplating is characterized in that it consists of the following raw material components in parts by weight:

[0047] 6 parts of anionic active agent

[0048] 4 parts of non-ionic active agent

[0049] Alkylphenol polyoxyethyl ether 9 parts

[0050] Sodium carbonate 19 parts

[0051] Sodium metasilicate 18 parts

[0052] Metal rust inhibitor 17 parts

[0053] Clean corrosion inhibitor 3 parts.

[0054] Wherein, the anionic active agent is sodium dodecylsulfonate and sodium lauryl sulfate mixed in a ratio of 1.2:1.5, and the nonionic active agent is alkylphenol polyoxyethylene ether and fatty alcohol polyoxyethylene ether Mixed according to the ratio of 1.1:1.6, the purity of the sodium carbonate is 98%, the purity of the trisodium phosphate is 98%, the cleaning corrosion inhibitor is thiourea, and the metal rust inhibitor is trisodium phosphate.

Embodiment 3

[0056] A cleaning and degreasing agent for electroplating is characterized in that it consists of the following raw material components in parts by weight:

[0057] 7 parts of anionic active agent

[0058] 4 parts of non-ionic active agent

[0059] Alkylphenol polyoxyethyl ether 10 parts

[0060] Sodium carbonate 18 parts

[0061] Sodium metasilicate 19 parts

[0062] Metal rust inhibitor 16 parts

[0063] Clean corrosion inhibitor 4 parts.

[0064] Wherein, the anionic active agent is sodium dodecylsulfonate and sodium lauryl sulfate mixed in a ratio of 1.3:1.7, and the nonionic active agent is alkylphenol polyoxyethylene ether and fatty alcohol polyoxyethylene ether Mixed according to the ratio of 1.1:1.7, the purity of the sodium carbonate is 98%, the purity of the trisodium phosphate is 98%, the cleaning corrosion inhibitor is thiourea, and the metal rust inhibitor is trisodium phosphate.

[0065] A cleaning and degreasing agent for electroplating. It is not only eas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cleaning degreaser for electroplating. The cleaning degreaser is characterized by consisting of the following raw material components in parts by weight: 5-8 parts of an anionic surfactant, 3-5 parts of a non-ionic surfactant, 8-10 parts of alkyl phenol polyoxyethylene ether, 15-20 parts of sodium carbonate, 17-23 parts of sodium metasilicate, 15-18 parts of a metal anti-rusting agent and 2-5 parts of a cleaning corrosion inhibitor. The cleaning degreaser disclosed by the invention, which is prepared from the raw materials, is not only convenient to use but also can be used for rapidly removing grease, polishing paste, fingerprint and like stains on the surface of a workpiece; and meanwhile, the cleaning degreaser can be used for removing an oxide layer on the surface of a copper layer and is quite excellent in cleaning effect; labor is saved and rework rate is reduced, and meanwhile, the quality and the service life of the product are improved.

Description

technical field [0001] The invention relates to the field of electroplating, in particular to a cleaning and degreasing agent for electroplating. Background technique [0002] When the workpiece is electroplated and copper-plated, it is often due to various or artificial or process reasons that the copper plating will adhere to a large amount of oil, dust and other substances on the surface of the workpiece, and at the same time, the surface of the workpiece will also be oxidized to varying degrees, resulting in oxidation. Therefore, it is necessary to clean the workpiece after copper plating. When using traditional cleaning and degreasing agents, not only the cleaning effect is not good, but there are many residues. Contents of the invention [0003] In view of the above problems, the invention provides a cleaning and degreasing agent for electroplating. [0004] For solving above technical problem, technical scheme provided by the invention is: [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D5/48C23G1/26
CPCC25D5/48C23G1/26
Inventor 尹伟
Owner ZHENJIANG RUIDE ENERGY SAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap