High-temperature-resistant sealing material and preparation method thereof

A sealing material and high temperature resistant technology, which is applied in the field of high temperature resistant sealing material and its preparation, can solve the problems of sealing material volume expansion, affecting the sealing effect, hidden safety hazards, etc., to achieve improved friction resistance, high work efficiency, and increased service life Effect

Inactive Publication Date: 2015-07-29
SUZHOU TONGMING MACHINERY
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the service life of the existing sealing materials is greatly reduced when the ambient temperature is high, but when the temperature is high, the volume of the sealing material will expand, seriously affecting its sealing effect, and bringing huge safety hazards to production, so it is urgently needed. High temperature resistant sealing material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] This embodiment provides a high-temperature resistant sealing material. The components of the wear-resistant sealing material in parts by weight are: acrylic rubber: 70 parts, styrene butadiene rubber: 22 parts, carbon black: 11 parts, glycerol Triglyceride: 5 parts, high styrene resin: 15 parts, active agent magnesium oxide: 2 parts, flame retardant tetrachlorophthalic anhydride: 5 parts, sulfur powder: 1 part, triethyl citrate: 2 parts, antioxidant 4010NA: 3 parts, ceramic powder: 1 part, dioctyl oxalate: 3 parts, zinc oxide: 2 parts, ethyl chrysanthemum acid: 4 parts, accelerator TMTD: 0.2 parts, palm wax: 1 copy;

[0027] The components of the ceramic powder are calculated in parts by weight: kaolinite: 12 parts, quartz: 1 part, clay: 20 parts, diamond powder: 3 parts, and titanium dioxide: 1 part;

[0028] The ceramic powder is prepared by mixing kaolinite, quartz, clay, diamond powder and titanium dioxide into a ball mill for pulverization, passing through a 100-mesh ...

Embodiment 2

[0035] This embodiment provides a high-temperature resistant sealing material. The components of the wear-resistant sealing material in parts by weight are: acrylic rubber: 72 parts, styrene butadiene rubber: 25 parts, carbon black: 13 parts, glycerol Triglyceride: 7 parts, high styrene resin: 18 parts, active agent magnesium oxide: 4 parts, flame retardant tetrachlorophthalic anhydride: 8 parts, sulfur powder: 3 parts, triethyl citrate: 4 parts, antioxidant 4010NA: 5 parts, ceramic powder: 3 parts, dioctyl oxalate: 6 parts, zinc oxide: 6 parts, ethyl chrysanthemum acid: 8 parts, accelerator TMTD: 0.8 parts, palm wax: 2 copies;

[0036] The components of the ceramic powder are calculated in parts by weight: kaolinite: 15 parts, quartz: 3 parts, clay: 22 parts, diamond powder: 5 parts, and titanium dioxide: 3 parts;

[0037] The ceramic powder is prepared by mixing kaolinite, quartz, clay, diamond powder and titanium dioxide into a ball mill for pulverization, passing a 100-mesh si...

Embodiment 3

[0044] This embodiment provides a high-temperature resistant sealing material. The components of the wear-resistant sealing material in parts by weight are: acrylic rubber: 71 parts, styrene-butadiene rubber: 24 parts, carbon black: 12 parts, glycerol Triglyceride: 6 parts, high styrene resin: 17 parts, active agent magnesium oxide: 3 parts, flame retardant tetrachlorophthalic anhydride: 8 parts, sulfur powder: 3 parts, triethyl citrate: 3 parts, antioxidant 4010NA: 4 parts, ceramic powder: 3 parts, dioctyl oxalate: 6 parts, zinc oxide: 6 parts, ethyl chrysanthemum acid: 5 parts, accelerator TMTD: 0.6 parts, palm wax: 2 copies;

[0045] The components of ceramic powder are calculated in parts by weight: kaolinite: 14 parts, quartz: 2 parts, clay: 21 parts, diamond powder: 4 parts, and titanium dioxide: 2 parts;

[0046] The ceramic powder is prepared by mixing kaolinite, quartz, clay, diamond powder and titanium dioxide into a ball mill for pulverization, passing through a 100-mes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-temperature-resistant sealing material and a preparation method thereof. The wear-resistant sealing material comprises the following components in parts by weight: 70-72 parts of acrylate rubber, 22-25 parts of butadiene styrene rubber, 11-13 parts of carbon black, 5-7 parts of glycerol trioleate, 15-18 parts of high styrene resin, 2-4 parts of an active agent magnesium oxide, 5-8 parts of a fire retardant tetrachlorophthalic anhydride, 1-3 parts of sulphur powder, 2-4 parts of triethyl citrate, 3-5 parts of an anti-aging agent 4010NA, 1-3 parts of ceramic powder, 3-6 parts of dioctyl adipate, 2-6 parts of zinc oxide, 4-8 parts of ethyl chrysanthemate, 0.2-0.8 part of an accelerant TMTD and 1-2 parts of palm wax.

Description

technical field [0001] The invention belongs to the field of sealing materials, and relates to a high-temperature-resistant sealing material and a preparation method thereof. Background technique [0002] Sealing materials refer to materials that can withstand joint displacement to achieve airtightness and watertightness and are embedded in building joints. Early sealing materials are mainly fabrics, mineral fibers or felts. With the development of industrial technology, in order to meet the increasingly complex and diverse requirements of hydraulic and pneumatic seals, sealing materials have also developed rapidly, with more and more types and continuous improvement of physical and chemical properties; [0003] However, the service life of the existing sealing materials is greatly reduced when the ambient temperature is high, but when the temperature is high, the volume of the sealing material will expand, seriously affecting its sealing effect, and bringing huge safety haz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/04C08L9/06C08L91/06C08K13/06C08K9/00C08K3/34C08K3/36C08K3/22C08K3/04C08K5/1539
Inventor 吴明黄莉
Owner SUZHOU TONGMING MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap