Rubber sealing materials

A sealing material and rubber sealing technology, applied in the field of materials, can solve the problems of large load, loss and trouble, and vicious accidents of the sealing ring, and achieve the effects of strong wear resistance, long service life and high mechanical strength

Inactive Publication Date: 2015-08-05
LIUZHOU LINGTONG TECH CO LTD
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the quality of the seal is poor, it will cause loss and trouble if it is light, and it will cause serious accidents if it is serious
Especially in an environment with high working pressure, the seal ring bears a large load, and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The formula of rubber sealing material of the present invention is as follows:

[0012] Acrylic rubber 42kg, hydrogenated nitrile rubber 18kg, stearic acid 4kg, methyl hydrogen silicone oil 1kg, glass fiber 0.6kg, oleic acid diethanolamine borate 2.5kg, diacetyl peroxide 5kg, aluminum oxide 2.5kg, light Quality calcium carbonate 1.4kg, dry oil alkyd resin 0.7kg, white carbon black 7kg, antioxidant 1.5kg, sulfur 2.5kg.

[0013] The preparation method of rubber sealing material of the present invention is as follows:

[0014] The acrylic rubber and hydrogenated nitrile rubber in the formula are thinned separately and then mixed into the open mill, and then the rest of the components are added into the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber. The rubber is vulcanized for one stage, the vulcanization temperature is controlled at 160°C, the vulcanization time is 35 minutes, and the vulcanization pressure is 10MPa; after ...

Embodiment 2

[0016] The formula of rubber sealing material of the present invention is as follows:

[0017] Acrylic rubber 40kg, hydrogenated nitrile rubber 15kg, stearic acid 3kg, methyl hydrogen silicone oil 1.2kg, glass fiber 0.8kg, oleic acid diethanolamine borate 2kg, diacetyl peroxide 4kg, aluminum oxide 2kg, lightweight Calcium carbonate 1.6kg, drying oil alkyd resin 0.9kg, white carbon black 6kg, antioxidant 0.5kg, sulfur 3kg.

[0018] The preparation method of rubber sealing material of the present invention is as follows:

[0019] The acrylic rubber and hydrogenated nitrile rubber in the formula are thinned separately and then mixed into the open mill, and then the rest of the components are added into the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber. The rubber is vulcanized for one stage, the vulcanization temperature is controlled at 150°C, the vulcanization time is 40 minutes, and the vulcanization pressure is 8MPa; the rubber...

Embodiment 3

[0021] The formula of rubber sealing material of the present invention is as follows:

[0022] Acrylate rubber 45kg, hydrogenated nitrile rubber 20kg, stearic acid 5kg, methyl hydrogen silicone oil 0.8kg, glass fiber 0.5kg, oleic acid diethanolamine borate 3kg, diacetyl peroxide 6kg, aluminum oxide 3kg, lightweight Calcium carbonate 1.2kg, dry oil alkyd resin 0.6kg, white carbon black 8kg, antioxidant 2kg, sulfur 2kg.

[0023] The preparation method of rubber sealing material of the present invention is as follows:

[0024] The acrylic rubber and hydrogenated nitrile rubber in the formula are thinned separately and then mixed into the open mill, and then the rest of the components are added into the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber. The rubber is vulcanized for one stage, the vulcanization temperature is controlled at 170°C, the vulcanization time is 30 minutes, and the vulcanization pressure is 11MPa; the rubber is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides rubber sealing materials. The rubber sealing materials are formed by the following components of, by mass, 40 to 45 parts of acrylate rubber, 15 to 20 parts of hydrogenated nitrile-butadiene rubber 15-20, 3 to 5 parts of stearic acid, 0.8 to 1.2 parts of methyl hydrogen silicone oil, 0.5 to 0.8 part of glass fibers, 2 to 3 parts of oleic acid diethanolamine borate ester, 4 to 6 parts of diacetyl peroxide, 2 to 3 parts of aluminum oxide, 1.2 to 1.6 parts of light calcium carbonate, 0.6 to 0.9 part of drying oil alkyd resin, 6 to 8 parts of white carbon black, 0.5 to 2 parts of anti-aging agent and 2 to 3 parts of sulfur. According to the rubber sealing materials, the mechanical strength is high, the friction coefficient which is 0.19 to 0.21 is low, the abrasion resistance is high, and the 140 to 170 days of service life under the high temperature and the high pressure working conditions is long, wherein the rubber sealing materials can work at 200 DEG C and the 420 MPa pressure can be borne.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a rubber sealing material. Background technique [0002] Sealing products are important basic components of all kinds of machinery, and almost all industrial sectors cannot do without it. The quality of the sealing element is directly related to the service life and operational reliability of the machine. If the quality of the seals is poor, it will cause loss and trouble if it is light, and it will cause serious accidents if it is serious. Especially in an environment with high working pressure, the seal ring bears a large load, and the seals are often damaged during the operation of the equipment. Some seals can only be used for 1-2 months, or even a shorter time , it needs to be replaced, which brings troubles to the continuous production of the enterprise. Therefore, there is an urgent need for a sealing material that can be used for a long period of time in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L33/04C08L15/00C08L83/05C08L67/08C08K13/04C08K5/09C08K7/14C08K5/55C08K5/14C08K3/22C08K3/26C08K3/36
Inventor 张文玲
Owner LIUZHOU LINGTONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap