Diatom ooze coating and preparation method thereof

A diatom mud coating and raw material technology, which is applied in the direction of fireproof coatings, antifouling/underwater coatings, coatings, etc., can solve the problem of poor adhesion of diatom mud coatings, inability to reduce formaldehyde content, insufficient coating adhesion, etc. problems, to achieve the effect of improving adhesion, facilitating blood oxygen delivery, and excellent air permeability

Inactive Publication Date: 2015-09-02
TONGCHENG HUIQI IND & TRADE
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing coatings use potassium silicate solution as a film-forming substance. Potassium silicate provides excellent adhesion performance, but due to the existence of alkali metal ions, the adhesion of the coating is not enough. At the same time, due to the existe...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of diatom mud coating, it is made by the following components according to parts by weight:

[0023] 15 parts of water, 0.6 parts of lignin or lignin derivatives, 10 parts of tourmaline, 0.1 parts of silver oxide, 10 parts of titanium dioxide, 3 parts of precipitated barium sulfate, 5 parts of kaolin, 5 parts of sepiolite powder, 30 parts of nano diatomite 0.5 parts of palladium, 5 parts of nano-titanium dioxide, 0.4 parts of leveling agent, 1.5 parts of thickener, 0.6 parts of antifungal agent, 1 part of nano-activated carbon, 0.5 parts of deodorant emulsion, 8 parts of redispersible rubber powder, and 1 part of pigment share.

[0024] The lignin is one of sulfuric acid lignin, hydrochloric acid lignin, ground wood lignin, alkali lignin, enzymatic lignin, steam explosion lignin and ethanol lignin; the lignin derivative is sulfonated lignin One of natural lignin, epoxy-modified lignin, amination-modified lignin, hydroxymethylated lignin, and graft-modified ligni...

Embodiment 2

[0036] The difference between this embodiment and embodiment 1 is only that

[0037] 20 parts of water, 1.2 parts of lignin or lignin derivatives, 13 parts of tourmaline, 0.2 parts of silver oxide, 13 parts of titanium dioxide, 4.5 parts of precipitated barium sulfate, 10 parts of kaolin, 8 parts of sepiolite powder, 37 parts of nano diatomite 1 part of palladium, 6 parts of nano-titanium dioxide, 0.5 parts of leveling agent, 2.5 parts of thickener, 0.9 parts of anti-fungal agent, 3 parts of nano-activated carbon, 1.5 parts of deodorant emulsion, 11 parts of redispersible rubber powder, 2 parts of pigment share.

Embodiment 3

[0039] The difference between this embodiment and embodiment 1 is only that

[0040] 25 parts of water, 2.6 parts of lignin or lignin derivatives, 15 parts of tourmaline, 0.3 parts of silver oxide, 15 parts of titanium dioxide, 6 parts of precipitated barium sulfate, 15 parts of kaolin, 10 parts of sepiolite powder, 45 parts of nano diatomite, palladium 1.5 parts, 10 parts of nano-titanium dioxide, 0.6 parts of leveling agent, 4 parts of thickener, 1.2 parts of antifungal agent, 5 parts of nano-activated carbon, 2 parts of deodorant emulsion, 13 parts of redispersible rubber powder, 2.5 parts of pigment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a diatom ooze coating which is made of raw materials comprising, by weight, 15-25 parts of water, 0.6-2.6 parts of lignin or lignin derivatives, 10-15 parts of tourmalines, 0.1-0.3 part of silver oxide, 10-15 parts of titanium dioxide, 3-6 parts of precipitated barium sulphate, 5-15 parts of kaoline, 5-10 parts of sea-foam stone powder, 30-45 parts of nano diatomite, 0.5-1.5 parts of palladium, 5-10 parts of nanometer titania, 0.4-0.6 part of leveling agents, 1.5-4 parts of thickening agents, 0.6-1.2 parts of mildew preventives, 1-5 parts of active carbon nanoparticles, 0.5-3 parts of net-flavor emulsions, 8-15 parts of dispersible adhesive powder and 0-3 parts of pigment. The diatom ooze coating is excellent in breathability and moisture absorption, gas ion negatively charged can be released, human body synthesis and vitamin storage can be promoted, and human immune ability is improved; functions of sterilization, mold prevention, deodorization, air purification and fire prevention are achieved; the preparation method is simple, easy to operate and convenient for large-scale production.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a diatom mud coating and a preparation method thereof. Background technique [0002] Coating is a material that can be coated on the surface of an object by different construction techniques to form a solid film with strong adhesion, certain strength and continuity. The film formed in this way is commonly called coating film, also known as paint film or coating, which is composed of three basic substances: film-forming substances, secondary film-forming substances and auxiliary film-forming substances. Existing coatings use potassium silicate solution as a film-forming substance. Potassium silicate provides excellent adhesion performance, but due to the existence of alkali metal ions, the adhesion of the coating is not enough. At the same time, due to the existence of alkali metal ions, the The water resistance of the coating is low; the current coatings still have the problems of not be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D7/12C09D5/14C09D5/18
CPCC09D7/65C08K3/04C08K3/34C08K2201/011C08K2201/014C09D5/14C09D5/18C09D7/61
Inventor 王宇
Owner TONGCHENG HUIQI IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap