Anti-mould fire-resistant rubber

A fire-resistant rubber and anti-fungal agent technology, applied in the field of rubber, can solve problems such as damage and people's loss, achieve good fire-resistant performance, reduce losses, and improve the effect of anti-mold

Inactive Publication Date: 2015-09-30
TIANJIN GUTE METAL PROD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] If the existing rubber burns in case of a big fire, in case of heavy rain or rainy season, it will become moldy and cause damage, which will bring huge losses to people. For this reason, we have designed a kind of mold-proof and fire-resistant rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The following will be described in detail in conjunction with the embodiments of the present invention.

[0008] A mildew-resistant fire-resistant rubber, which is composed of the following materials in parts by mass: 12.9-70.5 parts by mass of chloroprene rubber, 6-15 parts of EPDM rubber, 8-20 parts of epoxidized natural rubber, 4-12 parts of nano-zinc oxide, and stearin Sodium Oxide 1-4, Magnesium Hydroxide 1-5, Antifungal Agent 2-5, Aluminum Phosphate 2-6, Sodium Silicate 2-5, Mica Powder 0.4-1.8, Silicon Carbide 0.2-1.2, Antiaging Agent 1-5 , calcium carbonate 0.1-1, hydroxyl silicone oil 0.2-0.7, hydrogen silicone oil 0.1-0.6, white carbon black 0.1-0.3, dimethyl silicone oil 0.2-0.5, dibutyl phthalate 0.1-0.5, 2-mercaptan Imidazoline 1-3, plasticizer 0.1-0.5.

[0009] The antifungal agent is a series of quaternary ammonium salt derivatives.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides anti-mould fire-resistant rubber. The anti-mould fire-resistant rubber comprises, by mass, 12.9-70.5 parts of neoprene, 6-15 parts of ethylene-propylene-diene monomer, 8-20 parts of epoxidized natural rubber, 4-12 parts of nano-zinc oxide, 1-4 parts of sodium stearate, 1-5 parts of magnesium hydrate, 2-5 parts of mildew preventive, 2-6 parts of aluminium phosphate, 2-5 parts of sodium silicate, 0.4-1.8 parts of mica powder, 0.2-1.2 parts of silicon carbide, 1-5 parts of anti-aging agent, 0.1-1 part of calcium carbonate, 0.2-0.7 part of hydroxyl silicone oil, 0.1-0.6 part of hydro-silicone oil, 0.1-0.3 part of white carbon black, 0.2-0.5 part of simethicone, 0.1-0.5 part of dibutyl phthalate, 1-3 parts of 2-mercaptoimidazoline and 0.1-0.5 part of plasticizer. The mildew preventive is a quaternary ammonium salt derivative. The anti-mould fire-resistant rubber has good fire resistance, the anti-mould effect of the anti-mould fire-resistance rubber is greatly improved, and the loss of people can be reduced.

Description

technical field [0001] The invention relates to the field of rubber, in particular to a mold-proof and fire-resistant rubber. Background technique [0002] Existing rubber burns up in case of big fire, and in case of heavy rain or rainy season, it will become moldy and cause damage, which will bring huge losses to people. For this reason, we have designed a kind of mold-proof and fire-resistant rubber. Contents of the invention [0003] The invention provides a mildew-proof and fire-resistant rubber in order to make the rubber possess the functions of mildew resistance and fire resistance. [0004] In order to achieve the above object, the present invention provides a mildew-proof and fire-resistant rubber, which is composed of the following materials in parts by mass: neoprene 12.9-70.5, EPDM 6-15, epoxidized natural rubber 8-20, nano Zinc oxide 4-12, sodium stearate 1-4, magnesium hydroxide 1-5, antifungal agent 2-5, aluminum phosphate 2-6, sodium silicate 2-5, mica pow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L23/16C08L15/00C08L83/06C08L83/05C08L83/04C08K13/02C08K5/12C08K3/22C08K5/098C08K3/32C08K3/34C08K3/26
Inventor 田振明
Owner TIANJIN GUTE METAL PROD