Zirconia-doped rare earth-modified acrylic resin type powder coating

An acrylic resin, rare earth modification technology, applied in powder coatings, coatings and other directions, can solve the problems of high price, complex synthesis process, no promotion, etc., and achieve the effects of high production efficiency, safe and convenient transportation, and high utilization rate

Inactive Publication Date: 2015-09-30
蚌埠市阳光粉沫涂料有限责任公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because of its high price and complex synthesis process, it has not been popularized in my country.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconia-doped rare earth-modified acrylic resin type powder coating
  • Zirconia-doped rare earth-modified acrylic resin type powder coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A zirconia-doped rare-earth modified acrylic resin powder coating, made of the following raw materials in parts by mass:

[0023] 90 parts of glycidyl methacrylate, 15 parts of zirconia, 2 parts of yttrium oxide, 2 parts of cerium oxide, 2 parts of lanthanum oxide, 10 parts of diatomaceous earth, 8 parts of asbestos powder, 5 parts of lauric acid, 4 parts of white carbon black 3 parts, 3 parts of sodium zeolite, 3 parts of superfine transparent iron oxide yellow, 2 parts of dibutyl phthalate, 2 parts of polyester modified organosiloxane, 1 part of sodium metaborate, 100 parts of ethanol;

[0024] Its preparation method is as follows:

[0025] (1) Dissolve glycidyl methacrylate in ethanol, then add zirconia and rare earth, mix evenly, first ultrasonically treat at ultrasonic frequency 22kHz, power 100W for 15min, then microwave at microwave frequency 2450MHz, power 300W for 10min , obtain material I;

[0026] (2) Add diatomaceous earth, asbestos powder, white carbon bl...

Embodiment 2

[0030] A zirconia-doped rare-earth modified acrylic resin powder coating, made of the following raw materials in parts by mass:

[0031] 95 parts of glycidyl methacrylate, 18 parts of zirconia, 2 parts of yttrium oxide, 2 parts of cerium oxide, 2 parts of lanthanum oxide, 11 parts of diatomaceous earth, 9 parts of asbestos powder, 6 parts of lauric acid, 5 parts of white carbon black 4 parts of sodium zeolite, 3 parts of superfine transparent iron oxide yellow, 2 parts of dibutyl phthalate, 2 parts of polyester modified organosiloxane, 1 part of sodium metaborate, 110 parts of ethanol.

[0032] The preparation method of the present embodiment powder coating is the same as embodiment 1.

Embodiment 3

[0034] A zirconia-doped rare-earth modified acrylic resin powder coating, made of the following raw materials in parts by mass:

[0035] 100 parts of glycidyl methacrylate, 20 parts of zirconia, 2 parts of yttrium oxide, 2 parts of cerium oxide, 2 parts of lanthanum oxide, 12 parts of diatomaceous earth, 10 parts of asbestos powder, 8 parts of lauric acid, 5 parts of white carbon black 4 parts of sodium zeolite, 3 parts of superfine transparent iron oxide yellow, 2 parts of dibutyl phthalate, 2 parts of polyester modified organosiloxane, 1 part of sodium metaborate, 120 parts of ethanol.

[0036] The preparation method of the present embodiment powder coating is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a zirconia-doped rare earth-modified acrylic resin type powder coating, and relates to the technical field of powder coating production. The powder coating is prepared from the following raw materials in parts by mass: 90-100 parts of glycidyl methacrylate, 15-20 parts of zirconia, 5-8 parts of rare earth, 10-12 parts of diatomite, 8-10 parts of asbestos powder, 5-8 parts of dodecanedioic acid, 4-6 parts of white carbon black, 3-5 parts of natrolite, 3-4 parts of ultra-fine transparent yellow iron oxide, 2-3 parts of dibutyl phthalate, 2-3 parts of polyester-modified organosiloxane, 1-2 parts of sodium metaborate and 100-120 parts of ethanol. The coating provided by the invention is non-toxic and free of solvents and volatile toxic substances, and complies with environmental requirements; the raw material utilization rate reaches 99%; a dense coating is formed after spraying, and high adhesion, good impact resistance, and excellent weather resistance and corrosion resistance are realized.

Description

Technical field: [0001] The invention relates to the technical field of powder coating production, in particular to a zirconia-doped rare earth modified acrylic resin type powder coating. Background technique: [0002] Powder coating is a new type of solvent-free 100% solid powder coating, which has the characteristics of no solvent, no pollution, recyclable, environmental protection, energy and resource saving, reduced labor intensity and high mechanical strength of the coating film. It is mainly divided into thermoplastic powder There are two types of coatings and thermosetting powder coatings. Thermosetting powder coating refers to the use of thermosetting resin as a film-forming substance, adding a curing agent for crosslinking reaction and heating to form an insoluble and infusible hard coating. At higher temperatures, the coating does not soften like thermoplastic coatings, but only decomposes. Since the resin used in thermosetting powder coatings is a prepolymer wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/14C09D7/12C09D5/03C08F220/32
Inventor 司从辉司大勇陈安全司从翔
Owner 蚌埠市阳光粉沫涂料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com