A kind of highly safe metal lithium negative electrode and preparation method thereof

A high-safety, metal lithium technology, applied in battery electrodes, electrical components, circuits, etc., can solve problems such as failure to meet practical standards, deterioration of electrochemical performance, capacity loss, etc., to improve battery rate charge and discharge capacity and use Longevity, prevention of lithium dendrites, and performance improvement effects

Active Publication Date: 2018-02-02
李震祺 +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to suppress the formation of lithium dendrites in the lithium metal negative electrode during the charge-discharge cycle, researchers have done a lot of research, mainly focusing on the surface modification of the negative electrode lithium, and most of them use electrolyte additives to modify the surface properties of the lithium negative electrode. ; but this single modification effect can not meet the practical standard, and it is easy to cause capacity loss, internal resistance increase, electrochemical performance deterioration and other disadvantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of highly safe metal lithium negative electrode and preparation method thereof
  • A kind of highly safe metal lithium negative electrode and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Such as figure 1 with figure 2 As shown, a high-safety metal lithium negative electrode includes a lithium powder porous electrode 2 and a silicon-based protective layer 1, and also includes a negative electrode tab; the lithium powder porous electrode 2 includes a lithium powder material layer 21 and a copper foil 22, The lithium powder porous electrode 2 is formed by mixing the lithium powder and the binder PVDF in a tetrahydrofuran solvent, coating it on the copper foil 22, and forming it through sheeting; the silicon-based protective layer 1 is formed by vacuum coating The silicon-based material is vapor-deposited on the lithium powder material layer 21 by evaporation, and the thickness of the silicon-based protective layer 1 is 0.02˜0.2 μm.

[0040] Such as figure 2 As shown, since the lithium powder porous electrode 2 is a powder porous electrode, when the silicon-based protective layer 1 adopts the vacuum coating method to vapor-deposit silicon-based material...

Embodiment 2

[0045] On the basis of Example 1, the structure of the high-safety metal lithium negative electrode in this example is the same as that in Example 1, only the preparation method is different. In this example, the following steps are used to prepare:

[0046] Stir the mixture of molten lithium metal and 250°C hot silicone oil at 30,000rpm at high speed to form a dispersion system, cool to room temperature to obtain lithium metal powder, wash three times with cyclohexane and dry at room temperature to obtain lithium metal powder with a particle size of 18∼30µm; The mass ratio of metal lithium powder and binder PVDF is 80:20. Weigh the prepared metal lithium powder and binder PVDF respectively, and inject tetrahydrofuran 2.0 times the mass of metal lithium powder and binder PVDF solid powder into vacuum Stirring machine, stirring for 4h to mix the slurry, coating on the pre-treated copper foil, drying, tableting to prepare the lithium powder porous electrode 2; put the silicon-bas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a high-safety metal lithium negative electrode and a preparation method thereof, the high-safety metal lithium negative electrode includes a lithium powder porous electrode and a silicon-based protective layer, and the silicon-based protective layer is vapor-deposited on the lithium On the powder porous electrode, the thickness of the silicon-based protective layer is 0.02∼0.2µm. By adopting the technical scheme of the present invention, a layer of silicon-based protective film with lithium storage function is vapor-deposited on the metal lithium powder electrode, which greatly improves the safety of the metal lithium negative electrode, has a higher current density, and has a smaller internal resistance. It improves the cycle efficiency and provides development space for the application of metal lithium anodes in the field of high-energy batteries.

Description

technical field [0001] The invention belongs to the technical field of lithium batteries, relates to a high-safety metallic lithium negative electrode and a preparation method thereof, in particular to a high-safety and high-performance metallic lithium negative electrode and a preparation method thereof. Background technique [0002] Lithium-ion batteries have the advantages of large energy storage, no pollution, and light weight, and have been widely used in portable electronic devices, power tools and other fields. However, there are still some development bottlenecks in large-scale battery applications such as electric vehicles and energy storage: use safety, cycle life, energy density, etc. [0003] Lithium-ion batteries use graphite as the negative electrode, and the theoretical capacity of graphite-based negative electrodes is 375mAh / g, which cannot meet the needs of high-energy lithium-ion batteries. Compared with graphite-based negative electrodes, metallic lithium...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/134H01M2/16H01M2/14H01M4/1395
CPCH01M4/134H01M4/1395H01M50/403H01M50/431Y02E60/10
Inventor 李震祺刘立君宋翠环
Owner 李震祺