Vacuum plating UV composite coating for TPU materials

A technology of vacuum electroplating and composite coating, which is applied in coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve the problems of UV coatings being difficult to adapt and high hardness, and achieve reduced formulation costs, good compatibility, Appearance decorative effect rich and colorful effect

Inactive Publication Date: 2015-11-25
DONGGUAN YINGMING CHEM ENG
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, one of the prominent features of UV coatings is high hardness, which makes ordinary UV coatings unable to withstand large deformations. When it is necessary to obtain similar decorative effects on soft materials such as TPU, ordinary UV coatings are difficult. adapt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A kind of TPU material is used vacuum electroplating UV composite coating, comprises primer and topcoat, and described primer comprises following component by weight percentage:

[0054] Modified epoxy acrylate 12500g;

[0055] Two functional aliphatic urethane acrylate 2300g;

[0056] Cellulose acetate butyrate 350g;

[0057] 1-hydroxycyclohexyl phenyl ketone 620g;

[0058] 2,4,6-Trimethylbenzoyl-diphenylphosphine oxide 170g;

[0059] Polydimethylsiloxane 60g;

[0060] Ethyl ester 16500g;

[0061] Butyl ester 14000g;

[0062] Propylene glycol methyl ether 3500g;

[0063] Described finish paint comprises following component by weight percentage:

[0064] Modified epoxy acrylate 11600g;

[0065] Two functional aliphatic urethane acrylate 2100g;

[0066] Cellulose acetate butyrate 300g;

[0067] 2-Hydroxyethyl methacrylate phosphate 240g;

[0068] 1-hydroxycyclohexyl phenyl ketone 520g;

[0069]2,4,6-Trimethylbenzoyl-diphenylphosphine oxide 170g;

[0070] Ben...

Embodiment 2

[0092] A kind of TPU material is used vacuum electroplating UV composite coating, comprises primer and topcoat, and described primer comprises following component by weight percentage:

[0093] Modified epoxy acrylate 21680g;

[0094] Two functional aliphatic urethane acrylate 4352g;

[0095] Cellulose acetate butyrate 640g;

[0096] 1-hydroxycyclohexyl phenyl ketone 1480g;

[0097] 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 268g;

[0098] Polydimethylsiloxane 136g;

[0099] Ethyl ester 25760g;

[0100] Butyl ester 20784g;

[0101] Propylene glycol methyl ether 4880g;

[0102] Described finish paint comprises following component by weight percentage:

[0103] Modified epoxy acrylate 21600g;

[0104] Two functional aliphatic urethane acrylate 4080g;

[0105] Cellulose acetate butyrate 640g;

[0106] 2-Hydroxyethyl methacrylate phosphate 440g;

[0107] 1-hydroxycyclohexyl phenyl ketone 1120g;

[0108] 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 288g;

[0109]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A vacuum plating UV composite coating for TPU materials comprises primer paint and finish paint. The primer paint comprises modified epoxy acrylate, two-functionality aliphatic polyurethane acrylate, cellulose acetate butyrate, 1-hydroxycyclohexyl phenyl ketone, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, polydimethylsiloxane, ethyl ester, butyl ester and propylene glycol monomethyl ether by weight percentage; the finish paint comprises modified epoxy acrylate, two-functionality aliphatic polyurethane acrylate, cellulose acetate butyrate, 2-hydroxy ethyl methacrylate phosphate, 1-hydroxycyclohexyl phenyl ketone, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, 2,2-dimethoxy-2-phenylacetophenone, polydimethylsiloxane, ethyl ester and butyl ester. According to the vacuum plating UV composite coating for the TPU materials, excellent flex resistance property is achieved, after folding is conducted, the phenomena of cracking and coloring of a paint film and a coating do not occur, and the good recuperability is achieved.

Description

technical field [0001] The invention relates to a UV coating, in particular to a UV composite coating used for vacuum electroplating on a TPU material. Background technique [0002] UV curing coating is an energy-saving and environment-friendly coating. It has no or low VOC emission, energy saving, fast curing rate, high production efficiency, suitable for assembly line production, low curing temperature, suitable for coating heat-sensitive substrates, good friction resistance, solvent resistance and stain resistance And other excellent performance, can also be tailored according to the requirements of users to meet the diverse individual needs of the market. Light-curing vacuum coating is a new type of UV coating developed on the basis of light-curing plastic coatings. It combines two technologies of UV coating and vacuum coating to obtain a new surface decoration effect. The treated plastic surface is completely shimmering with metallic luster, showing noble metal quali...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D175/14C09D183/04C09D7/12
Inventor 康指余刘甲明冯玉涛阳中云李煜亮付阳云刘亚平米绍毅史平昆
Owner DONGGUAN YINGMING CHEM ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com